醋酸回收罐进口管泄漏原因
Causes of Inlet Pipe Leakage in Acetic Acid Recovery Tank
摘 要
通过宏微观腐蚀形貌观察，管材和腐蚀产物化学成分分析等方法对精对苯二甲酸（PTA）氧化回收单元醋酸回收罐进口管的泄漏原因进行了分析。结果表明：醋酸回收罐进口管发生了严重的点蚀穿孔；点蚀穿孔主要是由溴离子引起的，另外，由于工艺不稳定导致管线超温服役，加速了管线在含溴离子醋酸中点蚀的发生，最终导致穿孔。
316L不锈钢
溴离子
腐蚀
acetic acid
316L stainless steel
bromide ion
corrosion
Abstract
The causes of inlet pipe leakage of acetic acid recovery tank were analyzed by means of macro and micro corrosion morphology observation, chemical composition analysis of pipe and corrosion product. The results show that pitting corrosion and perforation because of the existance of bromide ion were found in inlet pipe of acetic acid recovery tank. The pipe was overheated in service because of unstable process, which accelerated pitting corrosion of the pipe in acetic acid solution containing Br- and finally resulted in perforation.
中图分类号 TG142.71 DOI 10.11973/fsyfh-201706016
所属栏目 失效分析
基金项目
收稿日期 2015/11/20
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: CHEN Jiadong,JIANG Yong,ZHOU Yang,WEN Xiaoxiang,GONG Jianming. Causes of Inlet Pipe Leakage in Acetic Acid Recovery Tank[J]. Corrosion & Protection, 2017, 38(6): 483
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨振国,龚嶷,孟新昊. PTA装置干燥机316L不锈钢列管的腐蚀失效分析[C]//2009年全国失效分析学术会议论文集.[出版地不详]:[出版者不详],2009:6-16.
【2】李金桂,赵闰彦. 腐蚀和腐蚀控制手册[M]. 北京:国防工业出版社,1988:50.
【3】魏宝明. 金属腐蚀理论及应用[M]. 北京:化学工业出版社,1984:40.
【4】姜换强,余存烨. PTA装置不锈钢废气管失效对策[J]. 石油化工腐蚀与防护,2002,19(1):31-34.
【5】梁斌,巩建鸣,涂善东. AISI 316L和SAF 2205不锈钢在含溴醋酸溶液中腐蚀行为的研究[J]. 机械工程材料,2006,30(1):56-59.
【6】SZKLARSKA-SMIALOWSKA Z. Pitting corrosion of metals[M]. Texas:NACE,1986.
【7】SZKLARSKA-SMIALOWSKA Z,MANKOWSKI J. Effect of temperature on the kinetics of development of pits in stainless steel in 0.5 N NaCl + 0.1 N H2SO4 solution[J]. Corrosion,1972,12(12):925-934.
【8】SEKINE I,MASUKO A,SENOO K. Corrosion behavior of AISI 316 stainless steel in formic and acetic acid solutions[J]. Corrosion,1987,43(9):553-560.
【9】程学群,李晓刚,杜翠薇,等. 不锈钢和镍基合金在高温高压醋酸溶液中的腐蚀行为[J]. 中国腐蚀与防护学报,2006,26(2):70-74.
【10】程姗姗. 化纤PTA装置不锈钢材料腐蚀行为研究[D]. 西安:西安石油大学,2012:74.
【11】BOGAERTS W,VAN HAUTE A,BRABERS M J. Localized corrosion[M]. Houston:NACE,1981:89.
【12】余存烨. 高温醋酸塔器选材分析讨论[J]. 石油化工腐蚀与防护,1999,16(1):28-30.
【2】李金桂,赵闰彦. 腐蚀和腐蚀控制手册[M]. 北京:国防工业出版社,1988:50.
【3】魏宝明. 金属腐蚀理论及应用[M]. 北京:化学工业出版社,1984:40.
【4】姜换强,余存烨. PTA装置不锈钢废气管失效对策[J]. 石油化工腐蚀与防护,2002,19(1):31-34.
【5】梁斌,巩建鸣,涂善东. AISI 316L和SAF 2205不锈钢在含溴醋酸溶液中腐蚀行为的研究[J]. 机械工程材料,2006,30(1):56-59.
【6】SZKLARSKA-SMIALOWSKA Z. Pitting corrosion of metals[M]. Texas:NACE,1986.
【7】SZKLARSKA-SMIALOWSKA Z,MANKOWSKI J. Effect of temperature on the kinetics of development of pits in stainless steel in 0.5 N NaCl + 0.1 N H2SO4 solution[J]. Corrosion,1972,12(12):925-934.
【8】SEKINE I,MASUKO A,SENOO K. Corrosion behavior of AISI 316 stainless steel in formic and acetic acid solutions[J]. Corrosion,1987,43(9):553-560.
【9】程学群,李晓刚,杜翠薇,等. 不锈钢和镍基合金在高温高压醋酸溶液中的腐蚀行为[J]. 中国腐蚀与防护学报,2006,26(2):70-74.
【10】程姗姗. 化纤PTA装置不锈钢材料腐蚀行为研究[D]. 西安:西安石油大学,2012:74.
【11】BOGAERTS W,VAN HAUTE A,BRABERS M J. Localized corrosion[M]. Houston:NACE,1981:89.
【12】余存烨. 高温醋酸塔器选材分析讨论[J]. 石油化工腐蚀与防护,1999,16(1):28-30.
相关信息