Corrosion Behavior of 316NG Stainless Steel in High Pure Water Environment
摘 要
通过腐蚀失重试验,获得了316NG不锈钢在高纯水环境中的腐蚀失重曲线及均匀腐蚀速率;采用XPS、XRD、SEM等手段对腐蚀产物的组成元素、物相、形貌进行了分析。结果表明:316NG不锈钢在高纯水环境中的平均腐蚀速率为0.05 mm/a,远小于304NG不锈钢和321不锈钢的;腐蚀产物膜主要以耐蚀性强的磁铁矿Fe3O4、尖晶石类氧化物FeCr2O4和NiFe2O4、镍和铬氧化物及氢氧化物等形式存在,且(铬+镍)与铁的原子比高于基体的,说明316NG不锈钢具有良好的耐腐蚀性能。
Abstract
The corrosion behavior of 316NG stainless steel in high pure water environment was studied. The kinetic curve and corrosion rate of 316NG stainless steel were obtained by corrosion weight-loss test. The elements, phases and microscopic morphology of corrosion products were analyzed by the method of XPS, XRD and SEM. The results show that the corrosion rate of 316NG stainless steel in high pure water environment was 0.05 mm/a, which was lower than that of 304NG and 321 stainless steels. The corrosion products consisted of magnetite Fe3O4 with good corrosion resistance, spinel oxide FeCr2O4 and NiFe2O4, Ni oxide and hydroxide, Cr oxide and hydroxide. The atomic ratio of Ni+Cr to Fe in corrosion products was higher than that in base metal. The results show that 316NG stainless steel had good corrosion resistance.
中图分类号 TG172 DOI 10.11973/fsyfh-201608005
所属栏目 试验研究
基金项目
收稿日期 2015/5/4
修改稿日期
网络出版日期
作者单位点击查看
联系人作者王理(wl918@263.com)
备注王 理(1969-),研究员,本科,从事结构材料研究
引用该论文: HE Kun,WANG Li. Corrosion Behavior of 316NG Stainless Steel in High Pure Water Environment[J]. Corrosion & Protection, 2016, 37(8): 631
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】彭德全,胡石林,张平柱,等. 304L和304NG在模拟压水堆一回路条件下长期均匀腐蚀性能的研究[J]. 中国腐蚀与防护学报,2013,33(4):288-292.
【2】姜峨,文燕,刘然超,等. 304NG不锈钢均匀腐蚀性能研究[J]. 核动力工程,2005,26(4):290-292.
【3】杨文斗. 反应堆材料学[M]. 北京:原子能出版社,2000.
【4】彭青娇,张志明,王俭秋,等. 溶解氢对316L不锈钢在模拟压水堆一回路水中氧化行为的影响[J]. 中国腐蚀与防护学报,2012,33(4):217-222.
【5】段振刚,张乐福,姜苏青,等. 压水堆一回路加锌对800合金氧化膜成分影响的XPS分析[J]. 腐蚀与防护,2014,35(3):224-227.
【2】姜峨,文燕,刘然超,等. 304NG不锈钢均匀腐蚀性能研究[J]. 核动力工程,2005,26(4):290-292.
【3】杨文斗. 反应堆材料学[M]. 北京:原子能出版社,2000.
【4】彭青娇,张志明,王俭秋,等. 溶解氢对316L不锈钢在模拟压水堆一回路水中氧化行为的影响[J]. 中国腐蚀与防护学报,2012,33(4):217-222.
【5】段振刚,张乐福,姜苏青,等. 压水堆一回路加锌对800合金氧化膜成分影响的XPS分析[J]. 腐蚀与防护,2014,35(3):224-227.
相关信息