Fracture Analysis of 3Cr2W8V Steel Pressure-casting Die
![](/skin/Gold/line_sep1.gif)
摘 要
3Cr2W8V钢压铸模具在压铸了几件铝件后发生断裂失效,采用化学成分分析、宏观检验、金相检验和断口分析等方法,对3Cr2W8V钢压铸模具的断裂原因进行了分析。结果表明: 模具材料在断裂处的显微组织不均匀,存在大颗粒状碳化物或集中分布的未溶碳化物是造成模具断裂的直接原因。
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
Abstract
The fracture reason of 3Cr2W8V steel pressure-casting die had been analyzed by mean of chemical compositions analysis,macro examination,metallographic examination and fracture analysis. The results show that there were many big-size carbides or liquation carbides in the steel near the fracture,which resulted in the fracture of the 3Cr2W8V steel pressure-casting die.
中图分类号 TG76
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/2/20
修改稿日期
网络出版日期
![](/skin/blank.gif)
作者单位点击查看
![](/skin/blank.gif)
备注黄福祥(1964-),男,教授,博士。
引用该论文: HUANG Fu-xiang,YANG Hui,TANG Li-wen,CHENG Li. Fracture Analysis of 3Cr2W8V Steel Pressure-casting Die[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(8): 517~518
黄福祥,杨惠,唐丽文,程里. 3Cr2W8V钢压铸模具断裂分析[J]. 理化检验-物理分册, 2009, 45(8): 517~518
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
![请选择您对本文的评价](/skin/Gold/evaluation/ev_01.gif)
![您认为本文一无是处!](/skin/Gold/evaluation/ev_02.gif)
![您认为本文较差,没啥用!](/skin/Gold/evaluation/ev_03.gif)
![您认为本文一般,没太大参考价值](/skin/Gold/evaluation/ev_04.gif)
![您认为本文尚可,值得参考](/skin/Gold/evaluation/ev_05.gif)
![您认为本文很好,值得推荐](/skin/Gold/evaluation/ev_06.gif)
参考文献
【1】吴连生. 失效分析技术[M]. 成都:四川科学技术出版社,1985.
【2】陈南平,顾守仁,沈万慈. 脆断失效分析[M]. 北京:机械工业出版社,1993,140-141.
【3】查利R布鲁克斯,阿肖克·考霍莱. 工程材料的失效分析[M]. 谢斐娟,孙家骏,译.北京:机械工业出版社,2003,105-138.
【2】陈南平,顾守仁,沈万慈. 脆断失效分析[M]. 北京:机械工业出版社,1993,140-141.
【3】查利R布鲁克斯,阿肖克·考霍莱. 工程材料的失效分析[M]. 谢斐娟,孙家骏,译.北京:机械工业出版社,2003,105-138.
相关信息