Influences of Concentration,Temperature and Strain Rate on Stress Corrosion Cracking of 316L Stainless Steel in Alkali Solution at High Temperature
![](/skin/Gold/line_sep1.gif)
摘 要
通过不同应变速率的拉伸试验,研究了316L不锈钢在不同温度和浓度的NaOH溶液中的应力腐蚀开裂行为,分析了以上三个因素对该钢应力腐蚀开裂的影响.结果表明:当应变速率为10-5 s-1时,316L不锈钢不会发生明显的应力腐蚀开裂,而当应变速率降低到10-6 s-1时,在高温低浓度的NaOH溶液中该钢会发生明显的应力腐蚀开裂;当应变速率为10-6 s-1时,NaOH溶液温度对316L不锈钢应力腐蚀开裂的影响程度要高于浓度的.
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
Abstract
Stress corrosion cracking (SCC) behavior of 316L stainless steel in NaOH solutions with different concentrations was investigated by using tension test at different strain rates and temperatures.And the effects of above three factors on stress corrosion cracking were analyzed.The results show that at the strain rate of 10-5 s-1,SCC of 316L stainless steel was not obvious,while the strain rate decreased to 10-6 s-1,SCC of 316L stainless steel in alkali solution at high temperature was remarkable.Effect of temperature of NaOH solution on SCC of 316L steel was more remarkable than solution concentration at 10-6 s-1.
中图分类号 TG172
所属栏目 试验研究
基金项目
收稿日期 2008/5/13
修改稿日期 2008/10/29
网络出版日期
![](/skin/blank.gif)
作者单位点击查看
![](/skin/blank.gif)
备注姜勇(1974-),男,山东威海人,博士研究生.
引用该论文: JIANG Yong,GONG Jian-ming,ZHOU Rong-rong. Influences of Concentration,Temperature and Strain Rate on Stress Corrosion Cracking of 316L Stainless Steel in Alkali Solution at High Temperature[J]. Materials for mechancial engineering, 2009, 33(5): 26~28
姜勇,巩建鸣,周荣荣. 高温碱液浓度与温度及应变速率对316L不锈钢应力腐蚀开裂的影响[J]. 机械工程材料, 2009, 33(5): 26~28
![](skin/blank.gif)
被引情况:
![](/skin/Gold/line_sep1.gif)
【1】姜勇,严明盛,陈佳栋,郜杰,巩建鸣, "PTA装置干燥机换热管的失效原因",腐蚀与防护 37, 80-82(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
![请选择您对本文的评价](/skin/Gold/evaluation/ev_01.gif)
![您认为本文一无是处!](/skin/Gold/evaluation/ev_02.gif)
![您认为本文较差,没啥用!](/skin/Gold/evaluation/ev_03.gif)
![您认为本文一般,没太大参考价值](/skin/Gold/evaluation/ev_04.gif)
![您认为本文尚可,值得参考](/skin/Gold/evaluation/ev_05.gif)
![您认为本文很好,值得推荐](/skin/Gold/evaluation/ev_06.gif)
参考文献
【1】ZHOU Rong-rong,GONG Jian-ming,LI Feng,et al.Evaluation of stress corrosion cracking of type 304L stainless steel in low concentration sodium hydroxide solution with high temperature[J].Key Engineering Materials,2007,353/358:3031-3034.
【2】小若正伦.金属的腐蚀破坏与防蚀技术[M].北京:化学工业出版社,1988:445-447.
【3】余存烨.不锈钢设备环境敏感断裂分析[J].石油化工腐蚀与防护,2004,21(1):33-36.
【4】乔立杰.应力腐蚀机理[M].北京:科学技术出版社,1993:15-17.
【5】李宇春,龚洵杰,周科朝.材料腐蚀与防护技术[M].北京:中国电力出版社,2004:29.
【2】小若正伦.金属的腐蚀破坏与防蚀技术[M].北京:化学工业出版社,1988:445-447.
【3】余存烨.不锈钢设备环境敏感断裂分析[J].石油化工腐蚀与防护,2004,21(1):33-36.
【4】乔立杰.应力腐蚀机理[M].北京:科学技术出版社,1993:15-17.
【5】李宇春,龚洵杰,周科朝.材料腐蚀与防护技术[M].北京:中国电力出版社,2004:29.
相关信息