Corrosion Resistance and Antimicrobial Properties of Copperized Stainless Steel
![](/skin/Gold/line_sep1.gif)
摘 要
利用75%Cu+7%Na3AlF3+18%Al2O3膏剂,在900 ℃对18-8型奥氏体不锈钢进行8h渗铜后缓冷制备渗铜抗菌不锈钢.采用电子探针和X射线衍射仪分析其渗层组织;涂抹印迹法测定其抗菌性能;采用浸泡法和盐雾试验检验其耐蚀性能.结果表明渗铜不锈钢24 h后对大肠杆菌的杀灭率可达99.99%,抗蚀性较原始试样有略微下降,但下降程度很小,仍具有较好的耐蚀性.
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
Abstract
An anti-microbial copperized stainless steel had been obtained by copperizing with a paste of 75%Cu+7%Na3AlF3+18%Al2O3 at 900 ℃ for 8 hrs.The microstructure,corrosion resistanc and anti-microbial property of the copperized steel were investigated by means of XRD,SEM,tests of immersion salt-spray and smearing culture.The copperized stainless steel possessed excellent anti-microbial propery and could kill 99.99% Escherichia coli.The corrosion resistance of copperized stainless steel fell down a little both in the organic or inorganic solvents.
中图分类号 TG174.44
所属栏目 试验研究
基金项目
收稿日期 2007/5/25
修改稿日期 2007/6/20
网络出版日期
![](/skin/blank.gif)
作者单位点击查看
引用该论文: LI Jin-gang,WANG Zhen-fu,SHI Hai-fang,LI Zhi-chao. Corrosion Resistance and Antimicrobial Properties of Copperized Stainless Steel[J]. Corrosion & Protection, 2008, 29(5): 253~256
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
![请选择您对本文的评价](/skin/Gold/evaluation/ev_01.gif)
![您认为本文一无是处!](/skin/Gold/evaluation/ev_02.gif)
![您认为本文较差,没啥用!](/skin/Gold/evaluation/ev_03.gif)
![您认为本文一般,没太大参考价值](/skin/Gold/evaluation/ev_04.gif)
![您认为本文尚可,值得参考](/skin/Gold/evaluation/ev_05.gif)
![您认为本文很好,值得推荐](/skin/Gold/evaluation/ev_06.gif)
参考文献
【1】王世森,许伯藩,倪红卫,等.渗铜法制备抗菌不锈钢渗层工艺的研究[J].金属热处理,2003,28(2):49-51.
【2】李宁,文玉华,张伟,等.高铜马氏体不锈钢的抗菌性能[J].特殊刚,2003,24(4):29-31.
【3】杨志勇,李文辉,林师表.抗菌不锈钢的开发[J].金属功能材料,2000,7(4).
【4】张伟,李宁,胥永刚,等.3Cr13Cu3马氏体不锈钢抗菌性能[J].特殊钢,2004,25(2):27-28.
【5】陈四红,吕曼祺, 张敬党,等.含Cu抗菌不锈钢的微观组织及其抗菌性能[J].金属学报,2004,40(3):314-318.
【6】汪铭.不锈钢表面抗菌薄膜的制备[D].浙江大学硕士论文,2003.
【7】李宁,文玉华,张伟,等.高铜马氏体不锈钢的抗菌性能[J].特殊钢,2003,24(4):29-30.
【8】王小丽,赵荣达,张伟强,等.含铜1Cr13型低碳马氏体抗菌不锈钢的组织和性能[J].特殊钢,2006,27(5):38-39.
【9】谷志刚,王荣吉,徐久全.18-8 型不锈钢固体法氮碳共渗的研究[J].热加工工艺,1997(1):31-33.
【2】李宁,文玉华,张伟,等.高铜马氏体不锈钢的抗菌性能[J].特殊刚,2003,24(4):29-31.
【3】杨志勇,李文辉,林师表.抗菌不锈钢的开发[J].金属功能材料,2000,7(4).
【4】张伟,李宁,胥永刚,等.3Cr13Cu3马氏体不锈钢抗菌性能[J].特殊钢,2004,25(2):27-28.
【5】陈四红,吕曼祺, 张敬党,等.含Cu抗菌不锈钢的微观组织及其抗菌性能[J].金属学报,2004,40(3):314-318.
【6】汪铭.不锈钢表面抗菌薄膜的制备[D].浙江大学硕士论文,2003.
【7】李宁,文玉华,张伟,等.高铜马氏体不锈钢的抗菌性能[J].特殊钢,2003,24(4):29-30.
【8】王小丽,赵荣达,张伟强,等.含铜1Cr13型低碳马氏体抗菌不锈钢的组织和性能[J].特殊钢,2006,27(5):38-39.
【9】谷志刚,王荣吉,徐久全.18-8 型不锈钢固体法氮碳共渗的研究[J].热加工工艺,1997(1):31-33.
相关信息