Surface Hardness Test of Campieces by Eddy Current Based on VB
摘 要
利用VB编写检测程序,设计分别与待测凸轮片凸圆和基圆耦合良好的涡流探头,选择3件经过高频感应淬火处理的不同硬度的球墨铸铁凸轮片进行硬度测试。结果表明: 该涡流检测仪能够精确检测球墨铸铁凸轮片的硬度, 与洛氏硬度计检测结果的对比表明其检测精度可达到±1.5 HRC;金相分析结果表明显微组织的不同是导致该3个凸轮片感应淬火层表面硬度高低不同的根本原因。
Abstract
By programming the eddy current test based on VB and designing two eddy current probes which couple well respectively with the gibbous circle and base circle of the campieces, the hardness of three high-frequency induction quenched nodular cast iron campieces with different surface hardness were tested. The results show that the test precession of the eddy current tester could be ±1.5 HRC according to the test results of Rockwell hardness tester. The metallographic examination results indicate that the difference of microstructure led to the difference of quenched case surface hardness of the three campieces.
中图分类号 TG115.28
所属栏目 试验技术与方法
基金项目
收稿日期 2012/10/23
修改稿日期
网络出版日期
作者单位点击查看
备注侯怀书(1972-),男,讲师,博士。
引用该论文: HOU Huai-shu,WU Bin,ZHANG Suo-huai. Surface Hardness Test of Campieces by Eddy Current Based on VB[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(12): 793~796
侯怀书,吴斌,张锁怀. 基于VB的凸轮片表面硬度涡流检测[J]. 理化检验-物理分册, 2012, 48(12): 793~796
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】龙建勇. 合金钢凸轮轴的加工工艺[J]. 现代零部件,2011(4):74-78.
【2】裴畅贵,白培康. 凸轮轴制造工艺及国内外发展趋势[J]. 新技术新工艺,2009(3):35-39.
【3】林俊明. 电磁(涡流)检测技术在中国[J]. 无损检测,2008,30(5):261-266.
【4】任吉林. 电磁无损检测[M]. 北京:航空工业出版社,1988.
【5】刘天佑. 金属学与热处理[M]. 北京:冶金工业出版社,2009.
【2】裴畅贵,白培康. 凸轮轴制造工艺及国内外发展趋势[J]. 新技术新工艺,2009(3):35-39.
【3】林俊明. 电磁(涡流)检测技术在中国[J]. 无损检测,2008,30(5):261-266.
【4】任吉林. 电磁无损检测[M]. 北京:航空工业出版社,1988.
【5】刘天佑. 金属学与热处理[M]. 北京:冶金工业出版社,2009.
相关信息