Continuous Cooling Phase Transformation Law of 440 MPa High-Strength IF Steel
![](/skin/Gold/line_sep1.gif)
摘 要
利用膨胀仪和热模拟试验机测定了440 MPa级高强度IF钢的静态和动态CCT曲线, 并对其相变规律进行了分析。结果表明: 在静态和动态转变的开始阶段均出现了铁素体组织, 随冷速的提高出现了贝氏体铁素体组织, 使转变产物晶粒细化; 与静态转变相比, 动态转变提高了奥氏体向铁素体转变的开始温度, 促进了铁素体相变, 使转变产物晶粒细化。
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
Abstract
The static and dynamic continuous cooling transformation (CCT) curves of 440 MPa high-strength IF steel were tested by dilatometer and thermal simulation tester, and the phase transformation law of the steel was analyzed. The results show that ferrite appeared at the start stage of static and dynamic transformation, and bainite ferrite appeared with the increase of cooling rates and the grains of phase transformation product were refined. Comparing with static transformation, dynamic transformation increased the starting temperature of austentite transforming to ferrite, promoted ferrite phase transformation and refined the grains of phase transformation products.
中图分类号 TG335.11
所属栏目 物理模拟与数值模拟
基金项目 北京市科委重大项目(D07010300700701); 国家“十一五”科技支撑计划项目(2006BAE03A06)
收稿日期 2011/3/22
修改稿日期 2011/10/1
网络出版日期
![](/skin/blank.gif)
作者单位点击查看
![](/skin/blank.gif)
备注王纯(1985-), 女, 天津人, 硕士研究生。
引用该论文: WANG Chun,ZHAO Ai-min,SU Lan. Continuous Cooling Phase Transformation Law of 440 MPa High-Strength IF Steel[J]. Materials for mechancial engineering, 2012, 36(2): 88~90
王纯,赵爱民,苏岚. 440 MPa级高强IF钢的连续冷却相变规律[J]. 机械工程材料, 2012, 36(2): 88~90
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
![请选择您对本文的评价](/skin/Gold/evaluation/ev_01.gif)
![您认为本文一无是处!](/skin/Gold/evaluation/ev_02.gif)
![您认为本文较差,没啥用!](/skin/Gold/evaluation/ev_03.gif)
![您认为本文一般,没太大参考价值](/skin/Gold/evaluation/ev_04.gif)
![您认为本文尚可,值得参考](/skin/Gold/evaluation/ev_05.gif)
![您认为本文很好,值得推荐](/skin/Gold/evaluation/ev_06.gif)
参考文献
【1】康永林.现代汽车板的质量控制与成形性[M].北京: 冶金工业出版社, 1999.
【2】王作成, 王先进, 韦柯.高强度无间隙原子钢板的热模拟实验研究[J].塑性工程学报, 1999(6):36-39.
【3】李曼云, 孙本荣.钢的控制轧制和控制冷却技术手册[M].北京: 冶金工业出版社, 1993.
【4】贺信莱.高性能低碳贝氏体钢[M].北京: 冶金工业出版社, 2008.
【5】刘宗昌, 王海燕, 计云萍, 等.钢中贝氏体相变理论研究的新进展[J].内蒙古科技大学学报, 2008, 27(2):99-108.
【2】王作成, 王先进, 韦柯.高强度无间隙原子钢板的热模拟实验研究[J].塑性工程学报, 1999(6):36-39.
【3】李曼云, 孙本荣.钢的控制轧制和控制冷却技术手册[M].北京: 冶金工业出版社, 1993.
【4】贺信莱.高性能低碳贝氏体钢[M].北京: 冶金工业出版社, 2008.
【5】刘宗昌, 王海燕, 计云萍, 等.钢中贝氏体相变理论研究的新进展[J].内蒙古科技大学学报, 2008, 27(2):99-108.
相关信息