Wear Resistance of Martensite Stainless Steel 11Cr17 after Sulphonitrocarburizing
![](/skin/Gold/line_sep1.gif)
摘 要
应用MM-200型磨损试验机对浸硫氮化后11Cr17马氏体不锈钢进行了耐磨性能试验, 用三维超景深显微镜测量计算磨痕面积并观察表面磨痕形貌; 通过渗层的显微组织、硬度梯度、EDS谱及XRD谱分析其耐磨性能提高的机理。结果表明: 11Cr17钢浸硫氮化后能获得优异的耐磨性能, 在干摩擦条件下比M2高速钢的优异, 主要是由于表面高硬度的化合物层及FeS的固体润滑作用, 油润滑下两者性能相当; 11Cr17钢浸硫氮化后的抗咬合性能出色, 能有效延缓发生严重磨损的时间。
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
Abstract
Wear resistance of sulphonitrocarburized martensite stainless steel 11Cr17 was tested on MM-200 wear tester. Wear area was measured and wear morphology was observed by microscopy with three dimensional ultra depth of field. The mechanism of increasing wear resistance of sulphonitrocarburized 11Cr17 steel was analyzed by microstructure, hardness gradient, EDS spectrum and XRD pattern. The results show that the 11Cr17 steel after sulphonitrocarburizing had more excellent wear resistance than high speed steel M2 under dry friction condition, because the former had a compound layer with high hardness and solid-lubricated FeS. The wear resistance of 11Cr17 steel after sulphonitrocarburizing and high speed steel M2 under oil lubrication conditions was not differen obviously.The anti-seizure property of sulphonitrocarburized 11Cr17 steel was also excellent, which could effectively delay the time of bad wear.
中图分类号 TG156.8
所属栏目
基金项目
收稿日期 2010/9/8
修改稿日期 2011/7/11
网络出版日期
![](/skin/blank.gif)
作者单位点击查看
![](/skin/blank.gif)
备注王博(1985-), 男, 湖北天门人, 硕士研究生。
引用该论文: WANG Bo,ZHANG Heng-hua. Wear Resistance of Martensite Stainless Steel 11Cr17 after Sulphonitrocarburizing[J]. Materials for mechancial engineering, 2011, 35(10): 12~15
王博,张恒华. 11Cr17马氏体不锈钢浸硫氮化后的耐磨性能[J]. 机械工程材料, 2011, 35(10): 12~15
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
![请选择您对本文的评价](/skin/Gold/evaluation/ev_01.gif)
![您认为本文一无是处!](/skin/Gold/evaluation/ev_02.gif)
![您认为本文较差,没啥用!](/skin/Gold/evaluation/ev_03.gif)
![您认为本文一般,没太大参考价值](/skin/Gold/evaluation/ev_04.gif)
![您认为本文尚可,值得参考](/skin/Gold/evaluation/ev_05.gif)
![您认为本文很好,值得推荐](/skin/Gold/evaluation/ev_06.gif)
参考文献
【1】江静华,蒋建清.室温盐液渗流[J].金属热处理,2002,27(12):33-35.
【2】佟晓辉,陈蕴博,胡以正.Cr12MoV钢硫氮碳共渗层摩擦磨损特性研究[J].机械科学与技术,1993(增刊):21-23.
【3】张双科,吴晓春.Cr12MoV钢等离子S-N-C共渗摩擦磨损特性研究[J].金属热处理,2003,28(4):24-28.
【4】朱达文.论SURSULF处理[J].航空精密制造技术,1992(3):41-43.
【5】SRINIVASAN P B. Sliding wear behavior of salt bath nitrocarburized medium carbon steel[J].Journal of Materials Engineering and Performance,2002,11:509-515.
【6】WILLBUR P J. High current density,low energy, ion implantation of AISI-M2 tool steel for tribological applications[J]. Surface and Coatings Technology,1996,83:250-256.
【7】FU Rui-dong. Solid solution nitriding technology of 15Cr-7.5 Mn-2.6Mo duplex stainless steel[J]. Transactions of Materials and Heat Treatment,2004,25(5):417-421.
【8】戴兵,王博,张恒华.具有表面类金刚石膜高速钢的耐磨性能[J].机械工程材料,2010,34(4):51-54.
【9】张红,宋玉悟.硫氮共渗后磨损粘着特性的研究[J].材料科学与工艺,1997,5(1):65-67.
【10】RAMPRASAD M. Some studies on scuffing performance of surface treated AISI 4340 steels[J]. Journal of Tribology,2003,125(1):181-186.
【11】袁相春,胡以正.非重载齿轮硫氮碳共渗层组织与抗胶合、承载特性[J].热加工工艺,1991(6):14-16.
【12】戴中兴.45、45CrNi钢硫氮碳共渗层组织特性的研究[J].湘潭大学学报: 自然科学版,1992,15(2):102-108.
【2】佟晓辉,陈蕴博,胡以正.Cr12MoV钢硫氮碳共渗层摩擦磨损特性研究[J].机械科学与技术,1993(增刊):21-23.
【3】张双科,吴晓春.Cr12MoV钢等离子S-N-C共渗摩擦磨损特性研究[J].金属热处理,2003,28(4):24-28.
【4】朱达文.论SURSULF处理[J].航空精密制造技术,1992(3):41-43.
【5】SRINIVASAN P B. Sliding wear behavior of salt bath nitrocarburized medium carbon steel[J].Journal of Materials Engineering and Performance,2002,11:509-515.
【6】WILLBUR P J. High current density,low energy, ion implantation of AISI-M2 tool steel for tribological applications[J]. Surface and Coatings Technology,1996,83:250-256.
【7】FU Rui-dong. Solid solution nitriding technology of 15Cr-7.5 Mn-2.6Mo duplex stainless steel[J]. Transactions of Materials and Heat Treatment,2004,25(5):417-421.
【8】戴兵,王博,张恒华.具有表面类金刚石膜高速钢的耐磨性能[J].机械工程材料,2010,34(4):51-54.
【9】张红,宋玉悟.硫氮共渗后磨损粘着特性的研究[J].材料科学与工艺,1997,5(1):65-67.
【10】RAMPRASAD M. Some studies on scuffing performance of surface treated AISI 4340 steels[J]. Journal of Tribology,2003,125(1):181-186.
【11】袁相春,胡以正.非重载齿轮硫氮碳共渗层组织与抗胶合、承载特性[J].热加工工艺,1991(6):14-16.
【12】戴中兴.45、45CrNi钢硫氮碳共渗层组织特性的研究[J].湘潭大学学报: 自然科学版,1992,15(2):102-108.
相关信息