顶盖螺栓断裂原因分析
Analysis on Fracture Reason of Roof Bolts
摘 要
利用化学成分分析、硬度测试、室温拉伸试验及金相检验等方法对顶盖螺栓断裂的原因进行了分析。结果表明: 螺栓断裂的原因是螺栓的热处理不合格, 造成螺栓的组织不良、性能下降, 在安装预紧时发生螺栓过载脆性断裂。
脆性断裂
热处理
过载
roof bolts
brittle fracture
heat treatment
overload
Abstract
The fracture reason of roof bolts was analyzed by means of chemical composition analysis, hardness testing, tensile testing at ambient temperature, metallographic examination and so on. The results showed that the unqualified heat treatment for bolts was resulted in poor microstructure and reduced mechanical properties. At last the overload brittle fracture was founded in bolts during installation.
中图分类号 TK730.8
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/8/20
修改稿日期
网络出版日期
作者单位点击查看
备注石顺梅(1982—), 女, 工程师。
引用该论文: SHI Shun-mei,BIAN Mei-hua. Analysis on Fracture Reason of Roof Bolts[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(5): 363～364
石顺梅,边美华. 顶盖螺栓断裂原因分析[J]. 理化检验－物理分册, 2014, 50(5): 363～364
被引情况:
【1】俞圆,怀华培,戴立强,凌国平, "尼龙丝切口形貌与旋转剃须刀锋利度关系",理化检验－物理分册 51, 874-879(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】中国机械工程学会热处理学会.热处理手册 第2卷 典型零件热处理[M].4版.北京: 机械工业出版社,2008.
【2】中国机械工程学会热处理学会.热处理手册 第1卷 工艺基础[M].4版.北京: 机械工业出版社,2008.
【3】张立业.钢中魏氏组织的形成因素综述[J].科技致富向导,2012(35): 93.
【4】宁玫, 李志群,孙梅红,等.魏氏组织形成机理及对钢管性能影响的分析研究[J].天津冶金, 2008(5): 118-124.
【5】中国机械工程学会热处理学会.热处理手册 第4卷 热处理质量控制和检验[M].4版.北京: 机械工业出版社,2008.
【2】中国机械工程学会热处理学会.热处理手册 第1卷 工艺基础[M].4版.北京: 机械工业出版社,2008.
【3】张立业.钢中魏氏组织的形成因素综述[J].科技致富向导,2012(35): 93.
【4】宁玫, 李志群,孙梅红,等.魏氏组织形成机理及对钢管性能影响的分析研究[J].天津冶金, 2008(5): 118-124.
【5】中国机械工程学会热处理学会.热处理手册 第4卷 热处理质量控制和检验[M].4版.北京: 机械工业出版社,2008.
相关信息