Fracture cause of check rod
![](/skin/Gold/line_sep1.gif)
摘 要
某检查杆在服役期间发生断裂。采用宏观观察、化学成分分析、力学性能测试、金相检验、扫描电镜及能谱分析等方法,对检查杆断裂的原因进行分析。结果表明:检查杆中存在原始裂纹,在使用过程中该处属于薄弱环节,容易造成应力集中;受到循环载荷后,检查杆发生疲劳断裂。
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
![](flash/relate.gif)
Abstract
The check rod was broken during service. The reason for the fracture of the check rod was analyzed by means of macro observation, chemical composition analysis, mechanical property test, metallographic examination, scanning electron microscope and energy spectrum analysis. The results show that there was a original crack in the check rod, which was a weak link in the use process and was easy to cause stress concentration. Fatigue fracture of the check rod occurred after cyclic loading.
中图分类号 TB31 DOI 10.11973/lhjy-wl202301014
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/4/9
修改稿日期
网络出版日期
![](/skin/blank.gif)
作者单位点击查看
![](/skin/blank.gif)
备注付洋洋(1989-),男,工程师,主要从事金相检测及失效分析工作,nlfd_lg@163.com
引用该论文: FU Yangyang. Fracture cause of check rod[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(1): 51~53
付洋洋. 检查杆断裂原因[J]. 理化检验-物理分册, 2023, 59(1): 51~53
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
![请选择您对本文的评价](/skin/Gold/evaluation/ev_01.gif)
![您认为本文一无是处!](/skin/Gold/evaluation/ev_02.gif)
![您认为本文较差,没啥用!](/skin/Gold/evaluation/ev_03.gif)
![您认为本文一般,没太大参考价值](/skin/Gold/evaluation/ev_04.gif)
![您认为本文尚可,值得参考](/skin/Gold/evaluation/ev_05.gif)
![您认为本文很好,值得推荐](/skin/Gold/evaluation/ev_06.gif)
参考文献
【1】杨王玥,齐俊杰,孙祖庆,等.低碳钢形变强化相变的特征[J].金属学报,2004,40(2):135-140.
【2】刘雪松,李书齐,王苹,等.6N01-T5铝合金焊接接头疲劳断裂分析[J].焊接学报,2009,30(10):25-28.
【3】郭东,翟振东,刘东坡.存在裂纹的压力容器疲劳断裂分析[J].建筑科学与工程学报,2007,24(3):87-90.
【2】刘雪松,李书齐,王苹,等.6N01-T5铝合金焊接接头疲劳断裂分析[J].焊接学报,2009,30(10):25-28.
【3】郭东,翟振东,刘东坡.存在裂纹的压力容器疲劳断裂分析[J].建筑科学与工程学报,2007,24(3):87-90.
相关信息