低合金钢中低含量元素的定量测试及不确定度评估
Quantitative measurement and uncertainty evaluation of low content elements in low alloy steels
摘 要
采用校准曲线法对低合金钢中常见的微量元素Mn和Si进行电子探针微区定量测试和不确定度计算。结果表明:取包含因子k=2时,试样中Mn元素的质量分数为0. 12%,扩展不确定度为0. 004 8%;Si元素的质量分数为1. 36%,扩展不确定度为0. 042%。
低含量元素
电子探针显微分析
校准曲线法
不确定度
low alloy steel
low content element
electron probe microanalysis
calibration curve method
uncertainty evaluation
Abstract
The calibration curve method was used to carry out quantitative measurement and uncertainty evaluation of Mn and Si, the common trace elements in low alloy steels, in micro area by electron probe microanalysis. The results show that when the inclusion factor k=2, the mass fraction of Mn in the sample was 0. 12%, and the expanded uncertainty was 0. 004 8%. The mass fraction of Si element was 1. 36%, and the expanded uncertainty was 0. 042%.
中图分类号 TB31 TH841 O213.2 DOI 10.11973/lhjy-wl202211007
所属栏目 试验技术与方法
基金项目
收稿日期 2022/3/7
修改稿日期
网络出版日期
作者单位点击查看
备注赵同新(1983-),男,本科,工程师,主要从事电子探针微束分析及其在材料测试领域应用的研究工作,sshztx@shimadzu.com.cn
引用该论文: ZHAO Tongxin,CUI Huijie,SUN Youbao,HUANG Taohong. Quantitative measurement and uncertainty evaluation of low content elements in low alloy steels[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(11): 25～27
赵同新,崔会杰,孙友宝,黄涛宏. 低合金钢中低含量元素的定量测试及不确定度评估[J]. 理化检验－物理分册, 2022, 58(11): 25～27
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵同新,吉见聪,加藤治彦,等.电子探针在金属材料分析与研究中的应用[J].理化检验(物理分册),2018,54(7):504-507.
【2】于凤云,李绍威,李春艳,等.含钛高熵合金中氮元素的电子探针微区分析技术[J].理化检验(物理分册),2020,56(9):28-30.
【2】于凤云,李绍威,李春艳,等.含钛高熵合金中氮元素的电子探针微区分析技术[J].理化检验(物理分册),2020,56(9):28-30.
相关信息