直缝埋弧焊钢管背弯不合格原因分析
Reason Analysis on Unqualified Root Bend of SAWL Pipe
摘 要
采用化学成分分析、力学性能测试、金相检验以及断口分析等方法对某批直缝埋弧焊钢管背弯不合格的原因进行了分析。结果表明: 埋弧焊钢管背弯热区裂纹的形成是由于钢板在轧制过程中钢板边部次表层存在钙铝硅酸盐夹杂物, 在焊接过程中, 该处在热应力作用下萌生裂纹并扩展, 形成断续出现的应力裂纹。
钢管
热区裂纹
夹杂物
应力裂纹
SAWL
steel pipe
heat affected zone crack
inclusions
stress cracks
Abstract
The unqualified reason in root bend test for SAWL pipe was analyzed by means of chemical composition analysis, mechanical property testing, metallographic examination and fracture analysis. The results showed that heat affected zone crack in SAWL pipe formed because of the inclusions of calcium aluminum silicate in plate edge subsurface during the rolling process for steel plate. In the welding process, the cracks initiated from inclusions and grew under thermal stress, at last the intermittent stress cracks occurred.
中图分类号 TE973
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/10/11
修改稿日期
网络出版日期
作者单位点击查看
备注王东超(1981-), 男, 工程师, 硕士。
引用该论文: WANG Dong-chao. Reason Analysis on Unqualified Root Bend of SAWL Pipe[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(7): 507～511
王东超. 直缝埋弧焊钢管背弯不合格原因分析[J]. 理化检验－物理分册, 2014, 50(7): 507～511
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郑磊, 傅俊岩.高等级管线钢的发展现状[J].钢铁, 2006, 41(10):1-10.
【2】张斌, 钱成文, 王玉梅, 等.国内外高钢级管线钢的发展及应用[J].石油工程建设, 2012, 38(1):1-4.
【3】张伟卫, 熊庆人, 吉玲康, 等.国内管线钢生产应用现状及发展前景[J].焊管, 2011, 34(1):5-8.
【4】万友捐, 罗元生, 杨小敏.转动支架焊接接头断裂分析[J].理化检验-物理分册, 2012, 48(1):55-58.
【5】张涛, 卫志刚, 田力男, 等.火电机组给水前置泵轴断裂原因分析[J].理化检验-物理分册, 2013, 49(12):848-851.
【2】张斌, 钱成文, 王玉梅, 等.国内外高钢级管线钢的发展及应用[J].石油工程建设, 2012, 38(1):1-4.
【3】张伟卫, 熊庆人, 吉玲康, 等.国内管线钢生产应用现状及发展前景[J].焊管, 2011, 34(1):5-8.
【4】万友捐, 罗元生, 杨小敏.转动支架焊接接头断裂分析[J].理化检验-物理分册, 2012, 48(1):55-58.
【5】张涛, 卫志刚, 田力男, 等.火电机组给水前置泵轴断裂原因分析[J].理化检验-物理分册, 2013, 49(12):848-851.
相关信息