12Cr1MoV钢管在长时服役后组织及拉伸性能的退化
          
Deterioration of Microstructure and Tensile Properties of 12Cr1MoV Steel Pipe after Long-Term Service

摘    要
研究了12Cr1MoV钢主蒸汽管道在长时(26 a)服役后的显微组织以及室温与高温拉伸性能,并与未服役钢管的进行了对比。结果表明:长时服役后钢管的组织退化表现为珠光体明显球化、层状Fe3C相明显碎化、铁素体中析出M7C3型碳化物以及晶粒明显长大;与未服役钢管相比,长时服役后钢管的室温屈服强度明显降低,但室温抗拉强度变化不大,高温屈服强度和抗拉强度则均明显降低;长时服役后钢管的室温拉伸断口存在典型的纤维区和撕裂区,为韧性断裂,高温拉伸时发生准解理断裂。
标    签 长时服役   显微组织   主蒸汽管道   拉伸性能   long-term service   microstructure   main steam piping   tensile property  
 
Abstract
Microstructure and tensile properties at room temperature and elevated temperature of main steam piping of 12Cr1MoV steel after long-term (26 a) service were studied, and compared with those of the unused steel pipe. The results show that the structural degradation of the long-term served steel pipe was characterized by obvious spheroidization of pearlite, obvious fragmentation of layered Fe3C phase, precipitation of M7C3 carbides in ferrite and significant growth of grains; Compared with those of the unused steel pipe, the yield strength at room temperature of the long-term served steel pipe decreased significantly, the tensile strength at room temperature changed little, and the yield strength and tensile strength at elevated temperature decreased greatly. The tensile fracture at room temperature of the long-term served steel pipe had typical fiber zone and tear zone, indicating a ductile fracture mode; while during tensile at elevated temperature, quasi-cleavage fracture occured.

中图分类号 TB35   DOI 10.11973/jxgccl201907006

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及应用

基金项目 国家自然科学基金青年基金资助项目(51805546);山东省自然科学基金博士基金资助项目(ZR2019BEE050);中央高校基本科研业务费专项资金资助项目(18CX02149A);青岛市博士后基金资助项目(BY20170211);中国石油大学(华东)引进人才科研启动项目(YJ20170018)

收稿日期 2018/5/4

修改稿日期 2019/5/5

网络出版日期

作者单位点击查看

备注杨滨(1988-),男,山东邹城人,讲师,博士

引用该论文: YANG Bin,SUN Wenqi,JIANG Wenchun,ZHAO Yanling. Deterioration of Microstructure and Tensile Properties of 12Cr1MoV Steel Pipe after Long-Term Service[J]. Materials for mechancial engineering, 2019, 43(7): 24~27
杨滨,孙文起,蒋文春,赵延灵. 12Cr1MoV钢管在长时服役后组织及拉伸性能的退化[J]. 机械工程材料, 2019, 43(7): 24~27


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】黄维浩, 张瑞, 唐松青, 等. 运行15万h后F12钢主蒸汽管道剩余寿命的预测与试验验证[J]. 机械工程材料, 2014, 38(1):90-95.
 
【2】周顺深. 火电厂高温部件剩余寿命评估[M]. 北京:中国电力出版社, 2006:17-21.
 
【3】PANDEY C, MAHAPATRA M M, KUMAR P, et al. Microstructure-based assessment of creep rupture behaviour of cast-forged P91 steel[J]. Materials Science and Engineering:A, 2017, 695:291-301.
 
【4】LIMA W F, RIGUEIRA G, FURTADO H C, et al. Microstructure evolution and creep properties of 2.25Cr-1Mo ferrite-pearlite and ferrite-bainite steels after exposure to elevated temperatures[J]. Materials Research, 2017, 20(2):418-422.
 
【5】PRAT O, GARCIA J, ROJAS D, et al. Investigations on coarsening of MX and M23C6 precipitates in 12% Cr creep resistant steels assisted by computational thermodynamics[J]. Materials Science and Engineering:A, 2010, 527(21/22):5976-5983.
 
【6】KASSNER M E, HAYES T A. Creep cavitation in metals[J]. International Journal of Plasticity, 2003, 19(10):1715-1748.
 
【7】CHAUDHURI S. Some aspects of metallurgical assessment of boiler tubes:Basic principles and case studies[J]. Materials Science and Engineering:A, 2006, 432(1/2):90-99.
 
【8】BOND L J, DOCTOR S R, GRIFFIN J W, et al. Damage assessment technologies for prognostics and proactive management of materials degradation[J]. Nuclear Technology, 2011, 173(1):46-55.
 
【9】朱家明. 基于图像分析软件的晶粒尺寸分布统计[J]. 压电与声光, 2013, 35(4):585-587.
 
【10】姜勇, 巩建鸣, 叶有俊, 等. 基于碳化物相分析法的12Cr1MoV过热器管寿命无损评价[J]. 材料热处理学报, 2011, 32(8):15-18.
 
【11】张而耕, 童遂放, 王琼琦, 等. 12Cr1MoV珠光体耐热钢长期服役中碳化物的变化及对性能的影响[J]. 机械工程材料, 2009, 33(9):28-32.
 
相关信息
   标题 相关频次
 6061铝合金热轧厚板的形变硬化特性
 4
 6061铝合金在多向锻造过程中显微组织与拉伸性能的演变
 4
 MnO含量对SJ612焊剂焊接18-8不锈钢接头组织和性能的影响
 4
 NaCl-KCl基排杂熔剂对A356铝合金熔体的净化及净化后的组织和性能
 4
 不同固化压力下制备碳纤维增强铝层板的拉伸性能
 4
 不同显微组织套管钻井用钢的拉伸性能与疲劳裂纹扩展性能
 4
 不同应变速率下D1车轮钢的拉伸性能与断口形貌
 4
 不同状态Mg-9Li-3Al-2.0Gd合金的显微组织及性能
 4
 充型压力对石膏型反重力铸造ZM5镁合金组织和拉伸性能的影响
 4
 大变形轧制制备超细晶镍基合金的显微组织与拉伸性能
 4
 复合添加稀土钕和铒的AZ91D镁合金显微组织与拉伸性能
 4
 钙对Mg-6Al变形镁合金显微组织和拉伸性能的影响
 4
 固溶时效工艺参数对TA19钛合金显微组织与拉伸性能的影响
 4
 国产X80管线钢管焊接接头的力学性能
 4
 国产和进口P92耐热钢显微组织、拉伸和蠕变性能的对比
 4
 焊接材料及热输入对Q460钢厚板焊接接头拉伸性能的影响
 4
 核电设备用SA533B钢板的组织和性能
 4
 激光立体成形TC4合金的显微组织和拉伸性能
 4
 激光选区熔化Hastelloy-X合金的显微组织与拉伸性能
 4
 颗粒粒径对喷射沉积制备SiC颗粒增强铝硅合金复合材料显微组织及拉伸性能的影响
 4
 累积叠轧工艺对AA3003铝合金显微组织和性能的影响
 4
 冷金属过渡电弧增材制造H13钢块体的显微组织与力学性能
 4
 冷金属过渡加脉冲电弧增材制造4043铝合金薄壁件的组织与拉伸性能
 4
 模压变形5052铝合金的显微组织与室温拉伸性能
 4
 钕变质处理对Mg-8Al合金显微组织和拉伸性能的影响
 4
 热处理对Gr.38钛合金管组织和性能的影响
 4
 热处理工艺对Ti55531钛合金显微组织与拉伸性能的影响
 4
 热等静压对ZL111-T6铝合金叶轮组织和性能的影响
 4
 试样直径对TC4钛合金拉伸性能的影响
 4
 铈对2195铝锂合金显微组织和拉伸性能的影响
 4