7050和7075铝合金板材的淬火残余应力
          
Quenching Residual Stresses of 7050 and 7075 Aluminum Alloy Plates

摘    要
铝合金板材的残余应力主要产生于淬火过程中,而残余应力是导致航空航天用铝合金板材机加工变形的主要原因。采用X射线衍射法、超声波法和盲孔法分别对7050铝合金板材水浸淬火试样的残余应力进行了测试,并对3种方法的测试结果进行了对比和分析;采用超声波法对7075铝合金板材喷淋淬火试样的残余应力进行了测试。结果表明:超声波法测得的7050铝合金板材水浸淬火试样的残余应力分布规律与X射线衍射法和盲孔法测得的具有较好的一致性,板材近表层处的残余应力随着测试深度的增加而减小;7075铝合金板材喷淋淬火试样的残余应力随着辊速和喷水量的增大而增大。
标    签 铝合金板材   残余应力   淬火   X射线衍射法   超声波法   盲孔法   aluminum alloy plate   residual stress   quenching   X-ray diffraction method   ultrasonic wave method   blind-hole method  
 
Abstract
Residual stress of aluminium alloy plates was mainly produced in quenching process, and residual stress was the main cause of deformation of aerospace aluminium alloy plates during machining. The residual stress of 7050 aluminium alloy plates sample after water quenching were tested by X-ray diffraction method, ultrasonic method and blind-hole method respectively, and the results of the three methods were compared and analyzed. The residual stress of 7075 aluminum alloy plates sample after spray quenching was tested by ultrasonic method. The results show that the residual stress distribution of 7050 aluminium alloy plates after water quenching tested by ultrasonic method was in good agreement with that tested by X-ray diffraction method and blind-hole method. The residual stress near the surface of the plate decreased with the increase of test depth. The residual stress of 7075 aluminum alloy plates sample after spray quenching increased with the increase of roll speed and water spray volume.

中图分类号 TG146.2+1   DOI 10.11973/lhjy-wl201901003

 
  中国光学期刊网论文下载说明


所属栏目 试验与研究

基金项目 国家重点研发计划(2016YFB0300900);中国铝业公司科技发展基金项目(2015KJZD02)

收稿日期 2018/3/20

修改稿日期

网络出版日期

作者单位点击查看

备注杨中玉(1987-),男,工程师,主要从事铝合金材料研究和残余应力的测试表征工作,y906050963@163.com

引用该论文: YANG Zhongyu,NIU Guanmei,CAO Hailong,WANG Junqiang,FAN Shitong,LIU Cheng. Quenching Residual Stresses of 7050 and 7075 Aluminum Alloy Plates[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(1): 9~14
杨中玉,牛关梅,曹海龙,王军强,范世通,刘成. 7050和7075铝合金板材的淬火残余应力[J]. 理化检验-物理分册, 2019, 55(1): 9~14


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】米谷茂. 残余应力的产生和对策[M]. 北京:机械工业出版社,1983.
 
【2】秦国华,林锋,左敦稳. 基于材料非均匀性铝厚板预拉伸残余应力的预测方法[J]. 中国有色金属学报,2015,25(3):626-633.
 
【3】唐志涛,刘战强,艾兴,等. 基于裂纹柔度法的铝合金预拉伸板内部残余应力测试[J]. 中国有色金属学报,2007,17(9):1404-1409.
 
【4】ROSSINI N S,DASSISTI M,BENYOUNIS K Y,et al. Methods of measuring residual stresses in components[J]. Materials & Design,2012,35:572-588.
 
【5】WITHERS P J,TURSKI M,EDWARDS L,et al. Recent advances in residual stress measurement[J]. International Journal of Pressure Vessels and Piping,2008,85(3):118-127.
 
【6】HUANG X F,LI Z W,XIE H. Recent progress in residual stress measurement techniques[J]. Acta Mechanica Solida Sinica,2013,26(6):570-583.
 
【7】巴发海,李凯. 金属材料残余应力的测定方法[J]. 理化检验(物理分册),2017,53(11):771-777.
 
【8】JAVADI Y,PIRZAMAN H S,RAEISI M H,et al. Ultrasonic inspection of a welded stainless steel pipe to evaluate residual stresses through thickness[J]. Materials & Design,2013,49:591-601.
 
【9】XU C,SONG W,PAN Q,et al. Nondestructive testing residual stress using ultrasonic critical refracted longitudinal wave[J]. Physics Procedia,2015,70:594-598.
 
【10】JAVADI Y,NAJAFABADI M A. Comparison between contact and immersion ultrasonic method to evaluate welding residual stresses of dissimilar joints[J]. Materials & Design,2013,47(9):473-482.
 
【11】郑林,张津,何长光,等. 短波长X射线衍射无损测定铝板内部残余应力[J]. 精密成形工程,2011,3(2):25-30.
 
【12】ZAPATA J,TORO M,LÍPEZ D. Residual stresses in friction stir dissimilar welding of aluminum alloys[J]. Journal of Materials Processing Technology,2016,229:121-127.
 
【13】宋文涛,徐春广. 超声法的残余应力场无损检测与表征[J]. 机械设计与制造,2015(10):9-12.
 
【14】BRAY D E,TANG W. Subsurface stress evaluation in steel plates and bars using the LCR ultrasonic wave[J]. Nuclear Engineering and Design,2001,207(2):231-240.
 
【15】马昌训,吴运新,郭俊康. X射线衍射法测量铝合金残余应力及误差分析[J]. 热加工工艺,2010,39(24):5-8.
 
【16】王晓宇,任丽萍,徐星泓,等. X射线衍射法测定圆棒表面残余应力的影响因素[J]. 理化检验(物理分册),2017,53(7):470-473.
 
【17】虞付进. 基于临界折射纵波的残余应力检测研究[D]. 杭州:浙江工业大学,2007.
 
【18】GIRI A,PANDEY C,MAHAPATRA M M,et al. On the estimation of error in measuring the residual stress by strain gauge rosette[J]. Measurement,2015,65:41-49.
 
相关信息
   标题 相关频次
 两种残余应力测定方法的研究和比较
 5
 测定钢板残余应力的改进盲孔法
 4
 大功率柴油机气缸盖的残余应力
 4
 电阻焊直缝焊接套管残余应力分布的测定
 4
 压路机压轮焊接变形和残余应力的有限元模拟
 4
 再制造工件表面的残余应力分布
 4
 X80钢大口径螺旋焊管的残余应力
 3
 X射线衍射法测残余应力的“突变”现象与定峰技巧探讨
 3
 材料内应力的检测方法
 3
 高钢级大口径焊管残余应力的测试方法
 3
 基于分段冷压法7050大型铝合金锻件残余应力的消减
 3
 基于临界折射纵波的超声波应力测量方法
 3
 切环法和盲孔法测试大口径厚壁X80钢级埋弧焊管的残余应力
 3
 热时效对消除钢结构焊接残余应力的工艺评估
 3
 陶瓷/金属封接残余应力的计算和测试
 3
 用X射线衍射法测定振动时效后水电站钢岔管中的残余应力
 3
 10B21钢防滑链抗拉载荷不合格原因分析
 2
 16MnD5钢板焊接件热影响区开裂原因分析
 2
 16MnR钢板焊接对接接头残余应力磁记忆检测研究
 2
 16Mn钢弯管的开裂原因
 2
 17Cr2Ni2Mo钢的表面复合喷丸强化
 2
 18Cr2Ni4WA钢氮化和喷丸强化处理的残余应力及性能
 2
 1Cr18Ni9Ti不锈钢导管开裂原因分析
 2
 2A14铝合金去应力热时效的作用
 2
 300M钢热损伤的巴克豪森检测
 2
 304不锈钢薄壁焊管表面残余拉应力的测定及消除
 2
 304不锈钢焊缝附近的点蚀损伤发展规律
 2
 304不锈钢焊管应力腐蚀开裂原因
 2
 30CrMnSiNi2A钢轮轴表面镀硬铬区域开裂的原因及控制措施
 2
 316L不锈钢板式换热器泄漏原因
 2