12Cr1MoV钢在碱金属硫氯盐中的腐蚀行为
          
Corrosion Behavior of 12Cr1MoV Steel in Alkali Metal Sulfur-chloride Salt

摘    要
将12Cr1MoV钢在不同温度(500,550,600℃)、不同组成的KCl-K2SO4熔盐中进行腐蚀试验,研究了温度和熔盐组成对试验钢腐蚀动力学、腐蚀形貌和腐蚀产物的影响。结果表明:随温度的升高或熔盐中K2SO4含量的增加,试验钢的腐蚀加剧;在600℃ KCl-25% K2SO4(质量分数,下同)熔盐中腐蚀后,试验钢表面存在大量的孔洞,腐蚀产物呈颗粒状,而在600℃ KCl-75% K2SO4熔盐中腐蚀后,表面孔洞较少,腐蚀产物呈片状;在600℃ KCl-25% K2SO4熔盐中腐蚀后,试验钢呈现非均匀腐蚀形貌,在550℃和500℃下呈现均匀腐蚀形貌,腐蚀内层主要由铁、铬氧化物组成,铬元素含量随温度升高而减少;在550℃ KCl-75% K2SO4熔盐中腐蚀形成的腐蚀内层厚度为83.8 μm,比在550℃ KCl-25% K2SO4熔盐中形成的厚了近1倍,且腐蚀内层更致密、孔洞更小。
标    签 生物质   锅炉   12Cr1MoV钢   碱金属熔盐   腐蚀   biomass   boiler   12Cr1MoV steel   alkali metal molten salt   corrosion  
 
Abstract
Corrosion tests in KCl-K2SO4 molten salts with different composition at different temperatures (500, 550, 600℃) were conducted on 12Cr1MoV steel. The effects of temperature and molten salt composition on corrosion kinetics, corrosion morphology and corrosion products of the tested steel were studied. The results show that with the rise of temperature or with the increase of K2SO4 content in molten salts, the corrosion of the tested steel increased. After corrosion in KCl-25wt%K2SO4 molten salt at 600℃, a large number of holes existed on surface of the tested steel and the corrosion products were granular; after corrosion in KCl-75wt%K2SO4 molten salt at 600℃, few holes existed on surface of the tested steel and the corrosion products were flake. The tested steel presented uneven corrosion morphology after corrosion in KCl-25wt%K2SO4 molten salt at 600℃ while showed uniform corrosion morphology at 550℃ and 500℃. The inner corrosion layer was composed of oxides of Fe and Cr, and the Cr content decreased with the temperature rising. The thickness of inner corrosion layer formed during corrosion in KCl-75wt%K2SO4 molten salt at 550℃ was 83.8 μm, nearly twice that formed in KCl-25wt%K2SO4 molten salt at 550℃, and the inner corrosion layer was relatively dense and the holes were relatively small.

中图分类号 TG178   DOI 10.11973/jxgccl201811001

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 国家自然科学基金资助项目(51275058)

收稿日期 2017/8/3

修改稿日期 2018/7/13

网络出版日期

作者单位点击查看

备注王刚(1992-),男,江苏连云港人,硕士研究生

引用该论文: WANG Gang,HE Jianjun,LI Wei,LIU Chen,LIU Zhenyao. Corrosion Behavior of 12Cr1MoV Steel in Alkali Metal Sulfur-chloride Salt[J]. Materials for mechancial engineering, 2018, 42(11): 1~5
王刚,何建军,李微,刘晨,刘震瑶. 12Cr1MoV钢在碱金属硫氯盐中的腐蚀行为[J]. 机械工程材料, 2018, 42(11): 1~5


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】武岳, 王永征, 栗秀娟, 等. 生物质混煤燃烧锅炉过热器受热面金属氯腐蚀特性[J]. 动力工程学报, 2014, 34(9):690-695.
 
【2】AHO M, PAAKKINEN K, TAIPALE R. Quality of deposits during grate combustion of corn stover and wood chip blends[J]. Fuel, 2013, 104:476-487.
 
【3】MONTGOMERY M,LARSEN O H. Field test corrosion experiments in Denmark with biomass fuels(Ⅱ):Co-firing of straw and coal[J]. Materials and Corrosion, 2002, 53(3):185-194.
 
【4】HANSEN P F B,ANDERSEN K H,WIECK-HANSEN K,et al. Co-firing straw and coal in a 150 MW utility boiler:In situ measurements[J]. Fuel Processing Technology,1998,54(1):207-225.
 
【5】李琰, 鲁金涛, 杨珍, 等. 锅炉奥氏体不锈钢在模拟煤灰和高硫烟气环境中腐蚀行为的研究[J]. 动力工程学报, 2017, 37(2):156-162.
 
【6】NIELSEN H P, BAXTER L L, SCLIPPAB G, et al. Deposition of potassium salts on heat transfer surfaces in straw-fired boilers:A pilot-scale study[J]. Fuel, 2000, 79(2):131-139.
 
【7】METSÄJOKI J, HUTTUNEN-SAARIVIRTA E, LEPISTÖ T. Elevated-temperature corrosion of uncoated and aluminized 9%-12% Cr boiler steels beneath KCl deposit[J]. Fuel, 2014, 133:173-181.
 
【8】ANTUNES R A, DE OLIVEIRA M C L. Corrosion in biomass combustion:A materials selection analysis and its interaction with corrosion mechanisms and mitigation strategies[J]. Corrosion Science, 2013, 76:6-26.
 
【9】NIELSEN H P, FRANDSEN F J, DAM-JOHANSEN K. Lab-scale investigations of high-temperature corrosion phenomena in straw-fired boilers[J]. Energy & Fuels, 1999, 13(6):1114-1121.
 
【10】FANG W C, RAPP R A. Electrochemical reactions in a pure Na2SO4 melt[J]. Journal of the Electrochemical Society, 1983, 130(12):2335-2341.
 
【11】李萍, 李安娜, 庞胜娇, 等. Super304H抗碱金属硫酸盐的腐蚀行为[J]. 材料工程, 2015, 43(1):54-58.
 
【12】卢旭东, 田素贵, 陈涛, 等. 高铬镍基合金熔融硫酸盐热腐蚀过程中内氧化和内硫化行为的研究[J]. 稀有金属材料与工程, 2014, 43(1):79-84.
 
【13】李灼贤, 王准, 余春江. 生物质锅炉典型过热器金属材料表面钝化膜腐蚀特性研究[J]. 能源工程, 2015(3):34-37.
 
相关信息
   标题 相关频次
 浆液冲击角度对Cr30A高铬铸铁冲蚀行为的影响
 6
 汉代铜镜的耐蚀性分析
 4
 12Cr1MoV钢在高温混合碱金属氯盐中的热腐蚀行为
 3
 高压汽包炉水冷壁爆管原因分析
 3
 颗粒粒径对喷射沉积制备SiC颗粒增强铝硅合金复合材料显微组织及拉伸性能的影响
 3
 w(Ti+B4C+C)/w(Ni60A)对等离子熔覆镍基复合涂层结构与性能的影响
 2
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1 000 MPa级超高强度热镀锌钢板耐腐蚀性能
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 10号碳钢在NaOH溶液中的腐蚀电化学行为
 2
 12Cr1MoV钢高温过热器管爆裂分析
 2
 12Cr1MoV钢过热器爆管的显微组织和力学性能
 2
 12Cr1MoV珠光体耐热钢长期服役中碳化物的变化及对性能的影响
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 14Cr1MoR钢在高温硫环境中的失效行为
 2
 15CrMo钢和12Cr1MoV钢的快速金相制样方法
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 2
 20G/316L双金属复合管失效的原因
 2
 20号钢在HCl-H2S-H2O溶液中的腐蚀行为
 2
 20号钢在气田站场分离器积液中的腐蚀行为
 2
 220kV钢芯铝绞线断股事故化学分析
 2
 2507双相不锈钢钾盐蒸发罐腐蚀的原因分析
 2
 2A12铝合金当量加速腐蚀试验
 2
 2-甲基咪唑啉及其复配缓蚀剂在高硬度电解质水溶液中的缓蚀性能
 2
 304H弹簧钢丝及弹簧表面腐蚀的原因
 2
 304L不锈钢焊接接头表面状态对其在硼酸溶液中腐蚀行为的影响
 2