304L不锈钢焊接接头表面状态对其在硼酸溶液中腐蚀行为的影响
          
Effect of Surface Condition of Welded Joint of 304L Stainless Steel on Its Corrosion Behavior in Boric Acid Solution

摘    要
采用浸泡腐蚀试验和电化学试验,以及光学显微镜、扫描电镜、三维形貌测试仪等研究了304L不锈钢焊接接头表面状态对其在硼酸溶液中腐蚀行为的影响。结果表明:打磨能够改善304L不锈钢焊接接头在硼酸水溶液中的耐蚀性,与未经打磨的焊接接头相比,经2 000号砂纸打磨后,焊接接头的腐蚀速率在整个浸泡过程中比较稳定,且远小于未经打磨焊接接头的;经40号砂纸打磨后焊接接头的表面粗糙度远大于机械抛光后焊接接头的,但前者的自腐蚀电位低于后者的,说明表面粗糙度越小耐蚀性越好。
标    签 304L不锈钢   焊接接头   腐蚀   核电站   304L stainless steel   welded joint   corrosion   nuclear power plant  
 
Abstract
The effect of surface condition of the welded joint of 304L stainless steel on its corrosion behavior in boric acid solution was studied by immersion corrosion testing,electrochemistry testing, optical microscopy, scanning electron microscopy (SEM) and 3D morphology testing. The results show that the corrosion resistance of the 304L stainless steel welded joint in boric acid solution was improved by sanding. The welded joint sanded with No. 2000 sandpaper had a stable corrosion rate throughout the immersion process, and the corrosion rate was far lower than that of the unsanded welded joint. The surface roughness of the welded joint after being sanded with No. 40 sandpaper was much larger than that of the mechanically polished joint, but the former had a lower corrosion potential than the latter, which means that the smaller the surface roughness is, the better the corrosion resistance is.

中图分类号 TG172   DOI 10.11973/fsyfh-201806009

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2017/9/5

修改稿日期

网络出版日期

作者单位点击查看


引用该论文: XU Weimin,ZHAN Jing,LI Chengtao,CHEN Jianjun,FANG Kewei. Effect of Surface Condition of Welded Joint of 304L Stainless Steel on Its Corrosion Behavior in Boric Acid Solution[J]. Corrosion & Protection, 2018, 39(6): 459


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】王轲,柳俊良,韩翠. 奥氏体不锈钢焊缝接头腐蚀性分析[J]. 焊接技术,2014,5(4):16-18.
 
【2】吕虹玮,董士刚,王静静. 316L不锈钢焊缝腐蚀行为的电化学研究[J]. 科技导报,2013,31(Z1):25-28.
 
【3】李岩,方可伟,刘飞华. Cl-对304L不锈钢从点蚀到应力腐蚀转变行为的影响[J]. 腐蚀与防护,2012,33(11):955-959.
 
【4】曾荣昌,韩恩厚. 材料的腐蚀与防护[M]. 北京:化学工业出版社,2006.
 
【5】GARCIA C,MARTIN F,DE TIEDRA P,et al. Pitting corrosion of welded joints of austenitic stainless steels studied by using an electrochemical minicell[J]. Corrosion Science,2008,50:1184-1194.
 
【6】GARCIA C,TIEDRA M,BLANCO Y,et al. Intergranular corrosion of welded joints of austenitic stainless steels studied by using an electrochemical minicell[J]. Corrosion Science,2008,50:2390-2397.
 
【7】GHOSH S,KAIN V. Microstructural changes in AISI 304L stainless steel due to surface machining:effect on its susceptibility to chloride stress corrosion cracking[J]. Journal of Nuclear Materials,2010,403:62-67.
 
相关信息
   标题 相关频次
 304L不锈钢在硼酸水溶液中的腐蚀行为
 5
 核电厂换料水箱底板检测与老化评估
 5
 304不锈钢在核电站二回路水环境中的应力腐蚀开裂行为
 4
 40CrNiMoA高强钢氢脆敏感性和氢含量的关系
 4
 Cu2+对材料在海水中腐蚀行为的影响
 4
 EB104/EB202涂层对904L不锈钢的防腐蚀效果
 4
 Inconel加热组件在高温高压水环境中的腐蚀机理及改善措施
 4
 TP439不锈钢在高温高压水中的应力腐蚀开裂行为
 4
 核电站PTR换料水箱地脚螺栓注蜡防腐蚀
 4
 温度对904L不锈钢耐点蚀性能的影响
 4
 在不同碱化剂溶液中TU48C钢的均匀腐蚀及流动加速腐蚀速率
 4
 Cl-对304L不锈钢从点蚀到应力腐蚀转变行为的影响
 3
 EPR法在评价304L不锈钢晶间腐蚀敏感性中的应用
 3
 大亚湾核电站核岛重要厂用水系统(SEC)典型的腐蚀事件及评价
 3
 海水管路黄铜焊接接头在人工海水中的电化学阻抗谱
 3
 核电厂设备典型腐蚀损伤及其防护技术
 3
 核电厂蒸汽发生器SA213T22传热管表面氧化膜的耐蚀性
 3
 核电站高温取样冷却器失效机理
 3
 核电站工程阶段的腐蚀问题及管理建议
 3
 核电站海水冷却系统的腐蚀与防腐蚀设计
 3
 力学/化学交互作用对钢质输油管道焊接接头电化学性能的影响
 3
 秦山二核安全厂用水系统管道防腐蚀设计评价
 3
 燃气余热锅炉高压蒸发器管SA210钢焊缝腐蚀特征分析
 3
 异材焊接件A508III-52M-316L基本材料在高温水环境中的电化学特性
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 10Ni5CrMoV钢MAG焊接接头的显微组织与力学性能
 2
 10号碳钢在NaOH溶液中的腐蚀电化学行为
 2
 12Cr2Mo1R钢焊条电弧焊焊接接头的性能
 2