38CrMoAl钢表面不同厚度搪瓷涂层的组织和性能
          
Microstructure and Properties of Enamel Coating with Different Thicknesses on Surface of 38CrMoAl Steel

摘    要
以A8005搪瓷粉为原料,在900℃保温45 min条件下在38CrMoAl钢表面烧结制备不同厚度(116,256,352,470 μm)搪瓷涂层,研究了涂层的微观结构、硬度、耐磨性能和耐腐蚀性能。结果表明:随着厚度的增加,搪瓷涂层的气孔数量先减后增,硬度、耐腐蚀性能、耐磨性能先增后降;当厚度为256 μm时,搪瓷涂层的性能最佳,内部气孔数量最少,表面光滑致密,硬度为720 HV0.1,磨损率为2.9×10-13 m3·N-1·m-1,耐蚀性能评级RP/RA为10/10vsB。
标    签 搪瓷涂层   气孔   耐磨性能   耐腐蚀性能   enamel coating   pore   wear resistance   corrosion resistance  
 
Abstract
With A8005 enamel powder as raw material, the enamel coating with different thicknesses (116, 256, 352, 470 μm) were prepared on the surface of 38CrMoAl steel after sintering at 900℃ for 45 min, and then the microstructure, hardness, wear resistance and corrosion resistance of the coating were studied. The results show that with increasing thickness, the pore amount in the enamel coating decreased and then increase, while the hardness, corrosion resistance and wear resistance increased and then decreased. When the thickness was 256 μm, the performance of the enamel coating was the best; the inner pore amount was the smallest, the surface was smooth and dense, the hardness was 720 HV0.1, the wear rate was 2.9×10-13 m3·N-1·m-1, and the corrosion resistance rating RP/RA was 10/10vsB.

中图分类号 TG174.45   DOI 10.11973/jxgccl201804017

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及应用

基金项目 宁波市工业重大专项项目(201601ZD-A01085);宁波工业重大(重点)择优委托科技攻关项目(2016B10023)

收稿日期 2017/7/25

修改稿日期 2018/2/20

网络出版日期

作者单位点击查看

备注杨梦梦(1992-),女,陕西渭南人,硕士研究生

引用该论文: YANG Mengmeng,DAI Jiaoyan,HE Huabo,XU Yiku,XU Jinfu. Microstructure and Properties of Enamel Coating with Different Thicknesses on Surface of 38CrMoAl Steel[J]. Materials for mechancial engineering, 2018, 42(4): 78~81
杨梦梦,戴姣燕,何骅波,徐义库,徐金富. 38CrMoAl钢表面不同厚度搪瓷涂层的组织和性能[J]. 机械工程材料, 2018, 42(4): 78~81


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】骆芳,丁建波,孙东跃,等.激光合金化对注塑机螺杆使用寿命影响的研究[J].应用激光,2006, 26(5):323-326.
 
【2】朱计,类彦威,文耀锋,等.螺杆机筒表面处理的新方法及其工艺分析[J].橡塑技术与装备,2007, 33(8):42-47.
 
【3】侯海涛.扫描欧洲陶瓷釉料新技术[J].建材发展导向,2005(3):53-54.
 
【4】於福海,刘轶,蔡起康.关于创新发展开辟搪瓷新产品[J].中国搪瓷,2000,21(3):7-10.
 
【5】王恩泽,鲍崇高,邢建东.涂层对氧化铝/耐热钢基复合材料磨料磨损性能的影响[J].西安交通大学学报, 2003, 37(9):945-948.
 
【6】夏艳红.钢铁表面低温搪瓷改性研究[D].长春:吉林大学,2010:31-33.
 
【7】PAPARAZZO E, FIERRO G, INGO G M, et al. Microchemistry and mechanisms of adherence in steel/enamel interfaces[J]. Journal of the American Ceramic Society,1988,71(12):494-497.
 
【8】BOROM M P, PASK J A. Role of "adherence oxides" in the development of chemical bonding at glass-metal interface[J]. Journal of the American Ceramic Society,1966,49(1):1-6.
 
【9】PASK J A, FULRATH R M. Fundamental of glass-to-metal bonding:VⅢ, nature of wetting and adherence[J]. Journal of the American Ceramic Society,1962,45(12):592-596.
 
相关信息
   标题 相关频次
 螺杆钢表面不同激光熔覆层的耐磨与耐腐蚀性能
 11
 等离子体源渗氮2Cr13马氏体不锈钢的耐磨与耐腐蚀性能
 4
 轻轨铁路支压板与销轴表面热处理工艺的选择
 4
 0Cr18Ni9Ti不锈钢表面渗锆合金层的耐腐蚀性能及抗高温氧化性能
 2
 11Cr17马氏体不锈钢浸硫氮化后的耐磨性能
 2
 17-4PH不锈钢表面TiO2膜及其多层膜的结构与性能
 2
 350 MW亚临界机组T91钢再热器管泄漏失效分析
 2
 Al2O3掺杂与超声辅助对纯铝表面微弧氧化层结构与性能的影响
 2
 AZ91D镁合金表面化学镀Ni-P-SiC复合镀层的结构与性能
 2
 B4C增强铁基活性氩弧熔覆层的制备与耐磨性能
 2
 CT80钢级连续油管焊接接头在不同质量分数NaCl溶液中的电化学腐蚀行为
 2
 KI体系下制备纯银镀层和纯银/银石墨复合镀层的性能
 2
 MnO含量对SJ612焊剂焊接18-8不锈钢接头组织和性能的影响
 2
 Mo元素对货油舱下底板用船板钢耐腐蚀性能的影响
 2
 NixAlTiCrFeCoCu高熵合金的显微组织与性能
 2
 NiCrAlY合金粉添加量对超音速火焰喷涂WC-10Co4Cr涂层组织及性能的影响
 2
 NiTi形状记忆合金表面辉光离子氮化层的结构与性能
 2
 S355J2W耐候钢的耐腐蚀性能
 2
 SiC颗粒增强铝基复合材料的摩擦磨损性能
 2
 TC4钛合金表面低压渗氮层的显微组织与耐磨性能
 2
 Ti3AlC2/Cu复合材料的制备与性能
 2
 TiNi合金表面钼合金层的物相与性能
 2
 W4Mo3Cr4V高速钢稀土多元共渗层的性能
 2
 X80管线钢包埋渗铝层的显微组织和耐腐蚀性能
 2
 X80管线钢在库尔勒土壤模拟溶液中的腐蚀行为
 2
 X80管线钢在酸性土壤模拟溶液中的腐蚀行为
 2
 ZG45钢表面镍钴基熔覆层的显微组织与耐腐蚀性能
 2
 Zr-0.8Sn-0.35Nb-0.4Fe-0.1Cr-xBi合金在400 ℃过热蒸汽中的腐蚀行为
 2
 闭孔泡沫铝的表面积与耐腐蚀性能
 2
 变质处理对过共晶铝硅合金组织和性能的影响
 2