聚氨酯/Q235钢配副滚动摩擦磨损行为
          
Rolling Friction and Wear Behavior of Polyurethane/Q235 Steel Pair

摘    要
采用自行研制的双盘摩擦磨损试验机对不同硬度聚氨酯与Q235钢组成的配副进行滚动摩擦磨损试验,探讨了载荷、转速以及聚氨酯的硬度对聚氨酯摩擦因数的影响,并研究了载荷和聚氨酯的硬度对聚氨酯磨损率的影响。结果表明:载荷对聚氨酯摩擦因数的影响较为明显,摩擦因数随着载荷的增大而减小;转速对聚氨酯摩擦因数的影响不大,也无明显的变化规律;随着聚氨酯硬度的升高,摩擦因数略有增大,但其变化幅度很小;磨损率随聚氨酯硬度的增大而减小,随载荷的增大而增大。
标    签 聚氨酯   滚动摩擦磨损   摩擦因数   polyurethane   rolling friction and wear   friction coefficient  
 
Abstract
The friction and wear test for the pair between polyurethane with different hardness and Q235 steel was carried out by using a self-made double disks friction and wear testing machine. The effect of load, rotational speed and hardness of polyurethane on the friction coefficient of polyurethane was discussed. The influence of load and hardness of polyurethane on the wear rate of polyurethane was studied. The results show that load had an obvious effect on the friction coefficient of polyurethane, the friction coefficient decreases with the increase of load. The effect of rotational speed on the friction coefficient was not obvious and there was not any regularity. The friction coefficient increased with the increase of hardness of polyurethane, but the variation amplitude was very small. The wear rate decreased with the increase of hardness of polyurethane and increased with the increase of load.

中图分类号 TH145.4   DOI 10.11973/jxgccl201709020

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及应用

基金项目

收稿日期 2016/9/21

修改稿日期 2017/7/25

网络出版日期

作者单位点击查看

备注朱鑫波(1989-),男,浙江湖州人,硕士研究生导师:王正东教授

引用该论文: ZHU Xinbo,CHEN Jianjun,PAN Hongliang,WANG Zhengdong. Rolling Friction and Wear Behavior of Polyurethane/Q235 Steel Pair[J]. Materials for mechancial engineering, 2017, 41(9): 101~105
朱鑫波,陈建钧,潘红良,王正东. 聚氨酯/Q235钢配副滚动摩擦磨损行为[J]. 机械工程材料, 2017, 41(9): 101~105


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】余桂林. 聚氨酯胶辊的特性与应用[J]. 棉纺织技术, 2012, 40(11):1-5.
 
【2】REN C, PAN H L. An analysis of inclusion defects on strip steel surface induced by polyurethane roller[J]. Engineering Failure Analysis, 2011, 18(3):1122-1127.
 
【3】黄乐,贾晓红,郭飞,等. 基于有限元分析方法的聚氨酯磨损规律研究[J]. 橡胶工业, 2016, 63(7):398-402.
 
【4】田雨,张杰,韦永继,等. 聚氨酯弹性体摩擦系数影响因素探讨[J]. 聚氨酯工业, 2002, 17(1):37-40.
 
【5】邹丞,王家序,余江波,等. 橡胶层厚度和硬度对水润滑整体式轴承摩擦因数的影响[J]. 润滑与密封, 2006(2):40-45.
 
【6】陈吉平,白晓鹏,丁智平,等.微孔聚氨酯粘弹性材料动态力学性能的有限元模拟[J].机械工程材料, 2016,40(7):64-67.
 
【7】张文刚. 橡胶摩擦与摩擦因数的测定[J].世界橡胶工业, 1998, 1(1):52-55.
 
【8】MOORE D F. The friction and lubrication of elastomers[M]. Oxford:Pergamon Press, 1972.
 
【9】郭胤,王家序,李峰,等.弹性体摩擦的黏滞疲劳理论及实验研究[J]. 摩擦学学报, 2013, 33(5):443-448.
 
【10】韩雪英,王影.摩擦的产生机理与分类[J]. 东北电力大学学报, 2010, 30(4):79-83.
 
【11】王哲,王世杰,王爽,等.干摩擦条件下丁腈橡胶和氟橡胶摩擦磨损行为研究[J].橡胶工业, 2015, 62(7):394-398.
 
【12】黄丽坚,杨长城,王晓东,等.聚酰亚胺复合材料与不同金属间干滑动时的摩擦学性能[J]. 机械工程材料, 2009,33(10):57-59.
 
【13】UCHIYAMA Y. Development of friction and wear of rubber[J]. Japanese Journal Society of Rubber Industry, 2007, 80(4):120-127.
 
【14】王优强,林秀娟,李志文.水润滑橡胶/镀镍钢配副摩擦磨损机理研究[J]. 机械工程材料, 2006, 30(1):63-65.
 
相关信息
   标题 相关频次
 38CrSi自配副的摩擦磨损性能
 2
 Al2O3连续增强铝基复合材料的干摩擦磨损特性
 2
 MoS2基复合润滑薄膜的制备及其摩擦性能
 2
 Ti6Al4V钛合金QPQ盐浴复合处理工艺的优化
 2
 不同工况下轮轨材料间的摩擦磨损行为
 2
 不同聚晶立方氮化硼复合刀具加工等温淬火球墨铸铁的切削性能对比
 2
 不同铁含量镍-铁合金镀层的摩擦磨损性能
 2
 不同组织高铬白口铸铁低速重载滑动干摩擦磨损行为
 2
 掺杂钨类金刚石膜的显微结构与性能
 2
 常用钢磨削纹理方向与其表面摩擦因数的关系
 2
 超声表面滚压处理对45钢摩擦学性能的影响及机理
 2
 法向载荷对不锈钢/浸金属碳载流摩擦磨损性能的影响
 2
 粉末冶金法制备铬镍合金热处理前后的摩擦磨损性能
 2
 复合电镀制备Ni-Co-PTFE自润滑镀层的研究
 2
 高强钢微冲剪试验影响因素的有限元模拟
 2
 高速条件下PTFE编织复合材料的摩擦磨损性能
 2
 硅烷和聚氨酯复合改性醇酸树脂双组份涂料的性能
 2
 核电反应堆压力容器支座减摩板往复摩擦磨损性能
 2
 环境温度对聚氨酯弹性体/环氧复合板力学性能的影响
 2
 基于GTN损伤模型对含边部缺陷硅钢薄板冷轧时边裂的预测
 2
 基于最大二阶主应变和Savitzky-Golay平滑原理对热轧酸洗板成形极限的数值模拟
 2
 激光气体氮化原位合成制备TiN/Ti3Al复合涂层及其抗高温冲蚀性能
 2
 紧固螺栓开裂原因分析
 2
 聚氨酯/聚(甲基丙烯酸甲酯-共-二甲基丙烯酸乙二醇酯)互穿聚合物网络改性废胶粉体系的力学性能
 2
 聚氨酯预聚体自乳化细乳液中异氰酸酯基团水解反应模型的建立与验证
 2
 聚氨酯增韧改性环氧树脂粘接SiC颗粒耐磨涂层的耐冲蚀性能
 2
 可膨胀石墨/氢氧化铝复配改性聚氨酯泡沫的阻燃性能
 2
 类金刚石表面改性C/C复合材料的摩擦磨损性能
 2
 铝合金用水性聚氨酯涂料的研制
 2
 绿色合成法制备聚氨酯/纳米二氧化钛杂化复合材料及其荧光性能初探
 2