G105钢制钻杆腐蚀失效的原因
          
Corrosion Failure Reason of a G105 Steel Drill Pipe

摘    要
某127 mm G105钢质钻杆表面在服役过程中发生了严重的局部腐蚀。通过力学性能分析、宏观及微观腐蚀形貌观察,并结合能谱(EDS)和X射线衍射(XRD)等方法研究了该钻杆腐蚀失效的原因。结果表明:钻杆管体表面发生严重了点蚀且呈条带状分布;在钻杆管体和接头的过渡区也发生了严重的点蚀;引起点蚀的主要原因是氧腐蚀、Ca2+等离子引起的垢下腐蚀;氯离子的存在加速了钻杆的局部腐蚀。
标    签 钻杆   氧腐蚀   点蚀   失效分析   drill pipe   oxygen corrosion   pitting   failure analysis  
 
Abstract
Severe localized corrosion occured on the surface of a G105 steel drill pipe with a diameter of 127 mm during the service process. Mechanical analysis, micro and macro morphology observation, EDS and XRD were employed to invesitgate the failure reason of the drill pipe. The results indicated that severe pitting occurred on the external surface of the G105 drill pipe and upset transition area; and several stripped pits were observed obviously on the surface of the drill pipe. The pitting of the G105 drill pipe was attributed to the oxygen corrosion and under-deposit corrosion induced by carbonate deposits, such as calcium carbonate. The chloride ions accelerated the localized corrosion of the drill pipe.

中图分类号 TG172   DOI 10.11973/fsyfh-201609020

 
  中国光学期刊网论文下载说明


所属栏目 失效分析

基金项目 中国石油集团大型油气田及煤层气开发项目,碳酸盐岩、火成岩及酸性气藏高效安全钻井技术课题(2011ZX05021-002)资助

收稿日期 2015/4/17

修改稿日期

网络出版日期

作者单位点击查看


备注朱丽娟(1986-),工程师, 博士,从事石油管科学技术研究与工程技术服务。

引用该论文: ZHU Li-juan,LIU Yong-gang,LI Fang-po,WANG Xin-hu,YUAN Jun-tao,LU Cai-hong. Corrosion Failure Reason of a G105 Steel Drill Pipe[J]. Corrosion & Protection, 2016, 37(9): 775


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】魏伯科,段慎修. 煤炭工业的腐蚀与防护[M]. 北京:化学工业出版社,1991.
 
【2】韩勇,冯耀荣,李鹤林. G105钻杆管体刺穿原因分析[J]. 石油机械,1990,18(1):37.
 
【3】AMEER M A,FEKRY A M,HEAKAL F E. Electrochemical behaviour of passive films on molybdenum-containing austenitic stainless steels in aqueous solutions[J]. Electrochimica Acta,2004(50):43.
 
【4】PARDO A,MERINO M C,COY A E,et al. Pitting corrosion behaviour of austenitic stainless steels-combining effects of Mn and Mo additions[J]. Corrosion Science,2008(50):1796.
 
【5】TVARA S A,CHAPETTI M D,OTEGUI J L,et al. Influence of nickel on the susceptibility to corrosion fatigue of duplex stainless steel welds[J]. International Journal of Fatigue,2001(23):619.
 
【6】ZHOU Y L,CHEN J,XU Y,et al. Effects of Cr,Ni and Cu on the corrosion behavior of low carbon microalloying steel in a Cl containing environment[J]. J Mater Sci Technol,2013,29(2):168.
 
【7】王丽萍,董文学,郭二军,等. Mn含量对00Cr22Ni5Mo3Mnχ双相不锈钢组织和性能的影响[J]. 热加工工艺,2013,42(2):63.
 
【8】TOBLER W J,VIRTANEN S. Effect of Mo species on metastable pitting of Fe18Cr alloys-A current transient analysis[J]. Corrosion Science,2006(48):1587.
 
【9】UHLIG H H,TRIADIS H H,STERN M. Effect of oxygen,chlorides,and calcium ion on corrosion inhibition of iron by polyphosphates[J]. Electrochem Soc,1995(102):59.
 
【10】马桂君,杜敏,刘福国,等. G105钻具钢在含有溶解氧条件下的腐蚀规律[J]. 中国腐蚀与防护学报,2008,28(2):108.
 
【11】谢飞,吴明,张越,等. 辽河油田注水管线结垢腐蚀原因分析及阻垢缓蚀剂应用试验[J]. 石油炼制与化工,2011,42(9):92.
 
【12】易成高,宫敬,杨勇,等. 含二氧化碳天然气集输管道管材的优选[J]. 油气储运,2009,28(6):76.
 
【13】MA H Y,YANG C,LI G Y,et al. Influence of nitrate and chloride ions on the corrosion of iron[J]. Corrosion,2003,59(12):1112.
 
【14】万里平,孟英峰,王存新,等. 西部油田油管腐蚀结垢机理研究[J]. 中国腐蚀与防护学报,2007,27(4):247.
 
【15】LIU Q Y,MA L J,ZHOU S W. Effects of chloride content on CO2 corrosion of carbon steel in simulated oil and gas well environments[J]. Corrosion Science,2014(84):165.
 
【16】崔志峰,韩一纯,庄力健,等. 在Cl-环境下金属腐蚀行为和机理[J]. 石油化工腐蚀与防护,2011,28(4):1.
 
【17】孙智,孙岚,欧雪梅,等. 金属在电导性煤层中的腐蚀[J]. 煤炭学报,1994,19(6):605.
 
相关信息
   标题 相关频次
 165.1 mm钻铤内螺纹接头失效分析
 9
 高压锅炉无缝钢管爆裂原因分析
 8
 S135钻杆刺漏失效分析及疲劳验证试验
 6
 139.7 mm×10.54 mm G105钻杆刺穿失效分析
 4
 IEU钻杆刺穿断裂原因分析
 4
 P110钢级油管接箍开裂失效分析
 4
 S135钻杆失效分析
 4
 定向钻穿越S135钢级钻杆的断裂分析
 4
 镀镍钻杆内壁腐蚀原因
 4
 水泥窑余热锅炉低压段蒸发器管屏穿孔失效分析
 4
 液压支架油缸内表面的腐蚀原因
 4
 钻杆失效分析中仿真模拟技术的应用
 4
 127 mm S135钻杆刺漏失效分析
 4
 X95钢级钻杆开裂原因分析
 3
 黄磷罐的失效分析
 3
 某304不锈钢管道泄漏的失效分析
 3
 汽车消声器的腐蚀失效分析
 3
 热交换器不锈钢管泄漏原因分析
 3
 西部油田某井油管腐蚀失效分析
 3
 ∮139.7mm钻杆摩擦对焊焊接接头缺陷产生原因
 2
 100t汽车车轴断裂分析
 2
 12Cr1MoV珠光体耐热钢长期服役中碳化物的变化及对性能的影响
 2
 15CrMo钢在含有SO42-的模拟汽轮机初凝水中的腐蚀特性
 2
 16Co14Ni10Cr2MoE钢制抽筒抓钩开裂失效分析
 2
 16Mn集输管线钢在含CO2凝析气田的腐蚀行为
 2
 2205双相不锈钢在卤水环境中的腐蚀行为
 2
 300 MW机组回转式空气预热器仓格板开裂原因分析
 2
 304不锈钢低温分离器开裂原因分析
 2
 30CrMnSiA钢螺钉断裂失效分析
 2
 30CrMnSiA螺栓失效分析
 2