Cl-,CO2和微量H2S共存时13Cr不锈钢的腐蚀性能
          
Corrosion Resistance of 13Cr Stainless Steel in the Cl-, CO2 Environment with Microamount H2S

摘    要
通过高温高压釜模拟油气田现场环境,采用扫描电镜、能谱和X射线衍射方法对油气田现场水样腐蚀后1Cr13和0Cr13两种钢的表面形貌及成分进行了分析,对比研究了Cl-,CO2和微量H2S共存时在气、液两相中的耐蚀性能。结果表明:1Cr13和0Cr13钢在气、液两相中的平均腐蚀速率均较小,但均有不同程度的点蚀发生,且0Cr13钢点蚀比1Cr13钢点蚀严重; 1Cr13和0Cr13钢主要靠钝化膜中铬的化合物降低腐蚀速率。并探讨了影响不锈钢耐蚀性能的因素,包括化学成分、夹杂、晶粒度、显微组织和腐蚀介质,并采用金相分析法进行了验证。
标    签 13Cr钢   钝化膜   不锈钢   腐蚀   点蚀   13Cr steel   passive film   stainless steel   corrosion   pitting corrosion  
 
Abstract
To evaluate the corrosion resistance of 1Cr13 and 0Cr13 in the Cl-, CO2 environment with microamount H2S, the autoclave was employed to investigate their corrosion behavior in simulating environment of oil and gas field. The corrosion product scale was analyzed by scanning electron microscope (SEM), energy dispersive X-ray spectrometer (EDS) and X-ray diffraction (XRD). The results showed that the average corrosion rate of 1Cr13 and 0Cr13 were very low, but there were localized corrosion exist. The pitting of 0Cr13 was more serious than 1Cr13. The corrosion rate was reduced rely on the compound of Cr in the passive film. The stainless steel corrosion resistance factors were discussed, including chemical composition, inclusion, grain size, microstructure and corrosion medium, and proved by metallographic examination.

中图分类号 TG172.8 TE983

 
  中国光学期刊网论文下载说明


所属栏目 试验与研究

基金项目

收稿日期 2009/7/21

修改稿日期

网络出版日期

作者单位点击查看

备注韩 燕(1981-),女,工程师,硕士。

引用该论文: HAN Yan,LI Dao-de,LIN Guan-fa,WANG Yuan,ZHANG Juan-tao. Corrosion Resistance of 13Cr Stainless Steel in the Cl-, CO2 Environment with Microamount H2S[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(3): 145~150
韩 燕1,李道德2,林冠发1,王 远1,张涓涛1. Cl-,CO2和微量H2S共存时13Cr不锈钢的腐蚀性能[J]. 理化检验-物理分册, 2010, 46(3): 145~150


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】BAROUX B. Further Insights in Pitting Corrosion of Stainless Steels, Corrosion Mechanisms in Theory and Practice[M]. New York: Marcel Dekker, 1995.
 
【2】POHJANNE P, CARPN L,HAKKARAINEN T, et al. A method to predict pitting corrosion of stainless steels in evaporative conditions[J]. Journal of Constructional Steel Research, 2008, 64(11):1325-1331.
 
【3】董晓焕.13Cr不锈钢CO2腐蚀行为及机理研究[D]. 西安: 西安石油大学, 2004.
 
【4】林冠发,胥勋源,白真权,等.13Cr油套管钢CO2腐蚀产物膜的能谱分析[J]. 中国材料科技与设备, 2008(3): 75-79.
 
【5】MASAMURA K, INOHARA Y, MINAMI Y. Effects of C and N on corrosion resistance of high Cr alloys in CO2 and H2S environments[C]// Corrosion98. Houston, TX:\[s.n.\],1998: 116.
 
【6】IKEDA A,VEDA M. CO2 corrosion behaviour of Cr-containing steel, working party report on prediction CO2 corrosion in oil and gas industry[C]// Corrosion94. Houston, TX: NACE International,1994: 59-93.
 
【7】徐金璋.合金元素和组织对马氏体不锈钢的耐蚀性和硬度的影响[J]. 上海钢研, 2001(2): 40-44.
 
【8】吴剑.不锈钢的腐蚀破坏与防蚀技术(一)点腐蚀的形成条件、形貌特征及其预防[J]. 腐蚀与防护, 1998, 18(1):38-42.
 
【9】徐祖耀,黄本立,鄢国强.中国材料工程大典(第26卷): 材料表征与检测技术[M]. 北京: 化学工业出版社, 2006:719-721.
 
【10】周卫军,严密林,王成达.N80S抗硫油管钢在含CO2、微量H2S及高浓度Cl-腐蚀介质中的腐蚀行为[J].腐蚀科学与防护技术, 2007,19(3):192-195.
 
【11】王明德.不锈钢和合金的点腐蚀及缝隙腐蚀[J]. 仪表材料,1981, 12(4):1-17.
 
相关信息
   标题 相关频次
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 4
 316L不锈钢在FeCl3溶液中点蚀行为的电化学噪声检测
 4
 316L不锈钢在有机胺脱硫溶液中的耐蚀性
 4
 445铁素体不锈钢内胆水箱的加工性能和耐蚀性
 4
 AISI304不锈钢钝化膜在电解质溶液中腐蚀时的半导体性质
 4
 AISI316L和SAF2205不锈钢在含溴醋酸溶液中腐蚀行为的研究
 4
 CdSe-TiO2复合材料对304不锈钢的光生阴极保护性能
 4
 HastelloyB3合金在盐酸中的腐蚀行为
 4
 TP304不锈钢凝汽器管在不同工况下的腐蚀行为
 4
 不锈钢点蚀行为及研究方法的进展
 4
 草甘膦生产用不锈钢反应釜腐蚀的显微分析
 4
 超临界CO2条件下钢的腐蚀行为研究进展
 4
 高流速凝析气田地面管线腐蚀原因分析
 4
 高温高压条件下13Cr钢的乙酸腐蚀
 4
 节镍型不锈钢的耐腐蚀性能比较
 4
 冷加工变形对1Cr18Ni9Ti不锈钢在含溴醋酸溶液中耐腐蚀性能的影响
 4
 利用SECM技术研究304不锈钢的点蚀行为
 4
 某304不锈钢管道泄漏的失效分析
 4
 幕墙不锈钢挂件的腐蚀问题
 4
 纳米化304不锈钢在硫酸溶液中的腐蚀行为
 4
 镍基合金G3在高含H2S和CO2环境中的腐蚀行为
 4
 凝汽器材料的耐磨蚀性能及电化学性能
 4
 四种不锈钢在含不同浓度Cl-的高炉煤气管道冷凝模拟液中的腐蚀行为
 4
 溴化锂机组不锈钢焊接管腐蚀失效的原因
 4
 烟草真空回潮机真空装置的腐蚀原因探讨及技术改进
 4
 组氨酸衍生物自组装膜的缓蚀性能
 4
 304不锈钢点腐蚀的声发射检测
 3
 C和Si含量对车轮钢腐蚀行为的影响
 3
 不同温度下超级13Cr在Cl-/CO2环境中的腐蚀行为
 3
 电化学测量技术在不锈钢点蚀研究中的应用与进展
 3