超声波对AZ31B镁合金凝固组织和力学性能的影响
          
Effect of Ultrasonic Wave on Solidified Structure and Mechanical Properties of AZ31B Magnesium Alloy

摘    要
在铸造过程中引入超声场制备出了AZ31B镁合金铸锭,研究了超声波对镁合金凝固组织及轧制后性能的影响.结果表明:在铸造过程中施加超声场,能显著细化AZ31B镁合金铸锭的晶粒,其平均粒径由未加超声场时的250~350 μm减小至120 μm左右;施加超声场还能促进第二相的析出,强化基体相,提高材料的强度;将铸锭轧制成3.0 mm厚板材后镁合金的抗拉强度和屈服强度分别提高了18.6%和25.8%,而伸长率变化不明显.
标    签 AZ31B镁合金   铸造   超声波   晶粒尺寸   力学性能   AZ31B magnesium alloy   casting   ultrasonic wave   grain size   mechanical property  
 
Abstract
The ingot of AZ31B magnesium alloy was prepared by casting in ultrasonic field.The effect of ultrasonic wave on solidified structure and properties of the alloy after rolling was studied.The results show that compared with the ingot casted without ultrasonic field the grain size of the AZ31B magnesium alloy ingot after casting in ultrasonic field could reduce from 250-350 μm to 120 μm.The ultrasonic vibration promoted the precipitation of the second phase which strengthened the base and improved the strength of the material.The tensile strength and yield strength were improved by 18.6% and 25.8% respectively after rolling the magnesium plate to 30 mm,and the elongation value had no significant change.

中图分类号 TG244

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 国家“973”计划资助项目(2007CB613706)

收稿日期 2009/6/24

修改稿日期 2010/4/5

网络出版日期

作者单位点击查看

备注毛大恒(1946-),男,湖南道县人,教授.

引用该论文: MAO Da-heng,QIU Ling,LI Ting,ZHANG Jia-fu,XUE Xin-ying. Effect of Ultrasonic Wave on Solidified Structure and Mechanical Properties of AZ31B Magnesium Alloy[J]. Materials for mechancial engineering, 2010, 34(8): 12~14
毛大恒,仇灵,李婷,张家富,薛新颖. 超声波对AZ31B镁合金凝固组织和力学性能的影响[J]. 机械工程材料, 2010, 34(8): 12~14


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】翟春泉,曾小勤,丁文江,等.镁合金的开发与应用[J].机械工程材料,2001,25(1):6-10.
 
【2】吕宜振,尉胤红,曾小勤,等.镁合金铸造成形技术的发展[J].铸造,2000,49(7):383-387.
 
【3】卫英慧,焦少阳,侯利峰,等.铸造缺陷对镁合金压铸件性能的影响[J].机械工程材料,2008,32(1):84-86.
 
【4】付彭怀,蒋海燕,翟春泉.显微特征与缺陷对铸造镁合金AZ91D力学性能的影响[J].有色合金,2007(2):20-24.
 
【5】GAO De-ming,LI Zhi-jun,HAN Qing-you,et al.Effect of ultrasonic power on microstructure and mechanical properties of AZ91 alloy[J].Materials Science and Engineering A,2009,502:2-5.
 
【6】RAMIREZ A,MA Q,DAVIS B,et al.Potency of high-intensity ultrasonic treatment for grain refinement of magnesium alloys[J].Scripta Materialia,2008,59:19-22.
 
【7】李晓谦,刘诗月,蒋日鹏.超声场对7B50铝合金凝固组织的影响[J].上海有色金属,2008,29(2):92-95.
 
【8】李英龙,李宝绵,刘永涛,等.功率超声对Al-Si合金组织和性能的影响[J].中国有色金属学报,1999,9(4):719-722.
 
【9】马立群,舒光冀,陈锋.金属熔体在超声场中凝固的研究[J].材料科学与工程,1995,13(4):227.
 
【10】黎文献.镁及镁合金[M].长沙:中南大学出版社,2005:1-10.
 
【11】屠怡范,陈晶益,张波萍,等.AZ31铸造镁合金的物相和显微组织[J].铸造,2006,55(5):509-512.
 
相关信息
   标题 相关频次
 复合能场铸轧和普通铸轧AZ31B镁合金板轧制后的组织与力学性能
 6
 超声波/电磁复合能场对1060铝合金铸轧板带组织和力学性能的影响
 4
 超声和电磁复合能场对铸轧铅合金板带显微组织与力学性能的影响
 4
 搅拌轴线速度对MWCNTs/Cu复合粉体和材料性能的影响
 4
 等径角挤压对铸造GH696合金力学性能的影响
 3
 电磁超声铸轧AZ31B镁合金板的热拉深性能
 3
 热处理条件对X60钢高频焊管焊缝组织和性能的影响
 3
 1.25Cr0.5MoSi钢的焊接工艺评定
 2
 1060工业纯铝累积叠轧后的力学性能
 2
 1060铝在累积轧制中组织和性能的演变
 2
 10Ni5CrMoV钢MAG焊接接头的显微组织与力学性能
 2
 12Cr13钢预热处理工艺参数优化
 2
 14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能
 2
 15Ni3CrMoV与10Ni5CrMoV异种钢对接接头的显微组织及力学性能
 2
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 2
 2 000 t水压机立柱断裂分析
 2
 2024铝合金电子束焊接接头的显微组织与力学性能
 2
 20Cr钢与B级钢焊接接头的组织和性能
 2
 2124铝合金超厚板热轧过程温度场的数值模拟
 2
 2197铝锂合金的化学铣切工艺
 2
 2205双相不锈钢/Q345低合金钢爆炸复合板的组织与力学性能
 2
 22Mn2SiVBS热轧无缝钢管控冷时的组织与性能
 2
 240 MPa级高强IF钢的冷轧压下率和退火温度
 2
 25Cr2MoVA钢调质规范对力学性能的影响
 2
 2A12铝合金喷射沉积坯的形状控制及显微组织
 2
 2GPa高压处理对铜铝合金显微组织和性能的影响
 2
 300 MW机组锁口叶片断裂原因分析
 2
 3003铝合金无缝管制备过程中的显微组织与力学性能变化
 2
 3D打印18Ni300模具钢的显微组织及力学性能
 2
 40CrNi2Mo钢的低温力学性能
 2