电沉积制备纳米晶镍-钨-稀土合金镀层工艺及性能
          
Performance and Electrodeposition Process of Nanocrystalline Ni-W-RE Alloy Coatings

摘    要
采用电沉积技术制备了纳米晶镍-钨-稀土合金镀层,重点研究了其制备工艺及镀层性能,探讨了电流密度、电沉积时间、镀液中稀土含量、镀液pH值和镀液温度等因素对镀层沉积速率的影响;用SEM、XRD、EDS、阳极极化曲线等方法分析了镀层的表面形貌、结构、组成、耐蚀性和抗氧化性等.结果表明:合金镀层的最佳制备工艺条件为电流密度9.5 A·dm-2、镀液pH值7、电沉积时间70 min、镀液温度50 ℃、镀液中NdCl3添加量4.5 g·L-1或镀液中Ce(SO4)2添加量3 g·L-1;添加稀土元素钕、铈后合金镀层表面颗粒排列致密、均匀,表面无裂纹,其抗高温氧化性和耐蚀性能与硬铬镀层比较相差较小.
标    签 电沉积   纳米晶   镍-钨合金镀层   稀土   electrodeposition   nanocrystalline   Ni-W alloy coating   rare earth  
 
Abstract
Nanocrystalline Ni-W-RE alloy coatings were prepared by electrodeposition and the performance and preparation technology were studied.The effects of current density,time of deposition,RE content in plating solution,pH value and temperature on the deposition rate of the coatings were studied.Surface morphology,structure,composition,corrosion resistance and oxidation resistance of composite coatings were tested by SEM,XRD,EDS and anodic polarization curves etc.The results show that the optimized preparation conditions of composite coatings were current density 9.5 A·dm-2,pH=7,time of electrodeposition 70 min,temperature of the solution 50 ℃,NdCl3 content in the solution 4.5 g·L-1 and Ce(SO4)2 content 3 g·L-1.The surface grains of the alloy coatings arranged densely,uniformly and without cracks after adding the RE elements of Nd and Ce.And the high temperature oxidation resistance and corrosion resistance of Ni-W-Nd alloy coatings were only a littre different from those of the hard chromium plating.

中图分类号 TQ153.1

 
  中国光学期刊网论文下载说明


所属栏目 纳米材料

基金项目 广西自然科学基金资助项目(0731015)

收稿日期 2009/4/29

修改稿日期 2009/11/29

网络出版日期

作者单位点击查看

备注刘峥(1962-),女,江西兴国人,教授,博士.

引用该论文: LIU Zhen,ZHANG Xue-hui,ZHANG Jian-zhang. Performance and Electrodeposition Process of Nanocrystalline Ni-W-RE Alloy Coatings[J]. Materials for mechancial engineering, 2010, 34(5): 76~80
刘峥,张学会,张建章. 电沉积制备纳米晶镍-钨-稀土合金镀层工艺及性能[J]. 机械工程材料, 2010, 34(5): 76~80


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】邓姝皓,龚竹青,陈文汩.电沉积纳米晶体材料的研究现状与发展[J].电镀与涂饰,2001,20(4):37-39,50.
 
【2】TOHRU Y.High-strength nanocrystalline Ni-W alloys produced by electrodeposition and their embrittlement behaviors during grain growth[J].Scripta Mater,2001,44:1497-1502.
 
【3】YAMASAKI T,SCHLOBMACHOR P,EHRLICH K,et al.Formation of amorphous electrodeposited Ni-W alloys and their nanocrystallization[J].Nano-Structured Materials,1998,10(3):375-388.
 
【4】郑子樵,李红英.稀土功能材料[M].北京:化学工业出版社,2003:460-466.
 
【5】LOKHANDE C D.Electrodepo sition of samarium[J].Metal Finishing,1988(8):23-28.
 
【6】LOKHANDE C D.Electrodepo sition of lanthanum from aqueous baths[J].Metal Finishing,1988(8):53-57.
 
【7】JUNDHAL E S B.Electrodepo sition of samarium from tartrate bath[J].Materials Chemistry and Physics,1991,27:265-269.
 
【8】刘淑兰,覃奇贤,成旦红,等.电沉积Ni-La合金上的阴极析氢行为[J].应用化学,1995,12(5):115-118.
 
【9】李振良,杨防祖,姚士冰.镍钨合金电结晶机理[J].厦门大学学报:自然科学版,1999,38(2):230-234.
 
【10】朱明华,李立青.稀土添加剂在金属电沉积中的应用研究进展[J].电镀与涂饰,2006,25(6):46-48.
 
相关信息
   标题 相关频次
 脉冲电沉积镍-钨-铁-镧纳米晶合金镀层的电催化析氢性能
 3
 Al0.3CoCrFeNi纳米晶高熵合金在碱性溶液中的电化学性能
 2
 AZ91D镁合金Ni-P/CeO2化学复合镀层的耐蚀性
 2
 Mg-5Zn-xEr-1.5Nd-0.5Zr(1.1
 2
 Ni-P化学镀层对NdFeB永磁材料耐腐蚀性的改善
 2
 Ni-W/SiC纳米复合镀层的制备与其耐蚀性
 2
 X射线衍射法测定纳米晶纯铝的平均晶粒尺寸
 2
 Y2O3纳米颗粒对电镀Ni-W涂层组织结构和电化学腐蚀性能的影响
 2
 表面纳米化是否生成纳米晶
 2
 表面转化膜无铬化技术的研究动向
 2
 不同方式电沉积纳米TiN/Ni复合镀层的组织和耐磨损性能
 2
 不同条件下金属镍电沉积中枝晶生长的分形维数
 2
 采用叠层模板电沉积工艺制备金属零件
 2
 超声波作用下电沉积纳米晶Co-W合金镀层
 2
 电沉积Fe-Cr-Ni合金的电化学腐蚀行为
 2
 电沉积法制备316L不锈钢表面微纳结构超疏水涂层及其耐海水腐蚀性能
 2
 电沉积制备铜-锡-PTFE自润滑复合镀层工艺参数对其性能的影响
 2
 电泳-电沉积镍基纳米复合镀层Ni-Al2O3的耐蚀性能
 2
 电泳-电沉积制备纳米Al2O3增强镍基复合镀层中纳米颗粒的分布状态
 2
 复合添加稀土钕和铒的AZ91D镁合金显微组织与拉伸性能
 2
 高能球磨法制备FeSiAl纳米晶合金粉
 2
 含稀土镁铝系合金耐腐蚀性能的研究现状
 2
 含稀土耐蚀Mg-9Al铸造镁合金腐蚀行为研究
 2
 机械合金化制备FeNbVB纳米晶粉末的研究
 2
 机械合金化制备纳米晶铁-铜合金粉体
 2
 基于RBF神经网络的合金铸铁动态腐蚀性能预测
 2
 碱性锌酸盐体系中Zn-Ni合金镀层的电沉积行为
 2
 溅射纳米晶Ni20Cr涂层的高温氧化行为
 2
 镁基储氢材料的吸放氢性能
 2
 纳米ZrO2/Cr复合电沉积的工艺条件
 2