聚氨酯增韧改性环氧树脂粘接SiC颗粒耐磨涂层的耐冲蚀性能
          
Erosive Wear Resistance of Epoxy Resin/SiC Wear Resistant Coating Modified by Polyurethane

摘    要
通过改变增韧剂聚氨酯(PU)的加入量,研究了聚氨酯改性环氧树脂粘接SiC颗粒耐磨涂层的粘接强度和耐冲蚀磨损性能.结果表明:加入适量的PU可有效改善环氧树脂胶体的粘接性能,PU加入量(质量分数)为15%时,改性环氧树脂粘接SiC颗粒耐磨涂层的粘接强度最高;涂层的耐冲蚀性能则随冲蚀角度的不同而变化,在大角度冲蚀时,PU加入量30%~35%的耐冲蚀性能最好,而小角度冲蚀时,PU加入量5%~15%的耐冲蚀性能最好;无论大角度还是小角度其耐冲蚀磨损性能都好于相同试验条件下白口铸铁的耐冲蚀性能.
标    签 聚氨酯   环氧树脂   SiC颗粒   粘接强度   冲蚀   polyurethane   epoxy resin   SiC particle   bonding strength   erosion  
 
Abstract
The adhesive strength and erosive wear resistance of SiC particles wear resistant coating bonded by polyurethane modified epoxy resin were studied by changing additive content of toughening agent polyurethane (PU).The results show that proper addition of PU could improve the bond behavior of epoxy resin.When PU addition was 15wt%,the bonding strength of SiC wear resistant coating bonded by modified epoxy resin was the highest.The erosion wear properties would be changed as the impact angle changed.The best erosion wear resistance would be obtained at large impact angle when the PU content was 30wt%-35wt%,and at small impact angle when the PU content was 5wt%-15wt%.The erosion wear property of SiC wear resistant coating bonded by modified epoxy resin was better than the white iron under the same impact condition at both small and large impact angles.

中图分类号 TG146.1

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及其应用

基金项目 陕西省重点学科建设专项经费资助项目

收稿日期 2009/1/13

修改稿日期 2009/9/5

网络出版日期

作者单位点击查看

备注邢志国(1979-),男,吉林通化人,博士研究生.

引用该论文: XING Zhi-guo,Lv Zhen-lin,CUI Yong. Erosive Wear Resistance of Epoxy Resin/SiC Wear Resistant Coating Modified by Polyurethane[J]. Materials for mechancial engineering, 2010, 34(1): 84~87
邢志国,吕振林,崔永. 聚氨酯增韧改性环氧树脂粘接SiC颗粒耐磨涂层的耐冲蚀性能[J]. 机械工程材料, 2010, 34(1): 84~87


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】材料耐磨抗蚀及其表面技术丛书编委会编.材料的磨料磨损[M].北京:机械工业出版社,1990.
 
【2】WANG Yi-san,ZHANG Xin-yuan.Casting sintering techno-logy for producing iron base surface composites[J].Material and Design,2000,21:447-452.
 
【3】CHAO P C.Tarbela dam-problems solved by novel concretes[J].Civ Eng,1990,50(12):59-62.
 
【4】马海波,卿宁.聚氦酯互穿网络结构聚合物侧研究进展及应用[J].皮革化学,2003,21(3):4-9.
 
【5】NUTTALL R J.Selection of abrasion resistant lining materials[J].Bulk Solids Handling,1985,5(5):1053-1055.
 
【6】ARGARWALV K,MILLS D,MASON J S.A comparison of the erosion wear of steel and rubber in pneumatic conveying system pipelines[C]//Proc 6th Int Conf on Erosion by Liquid and Solid Impact.Cambridge:Cavendish Laboratory,2003.
 
【7】施利毅,陈伟,陆永生,等.PU/EP共混物中的化学反应及粘接性能的研究[J].中国胶粘剂,1998,7(1):20-22.
 
【8】徐化兵.金属基环氧/聚氨酯梯度耐磨涂层的制备及性能研究[D].长沙:湖南大学,2005.
 
【9】WATSON J D,MUTTON D J.Metalographic observations of abrasive wear mechanisms[J].Aust Inst Met,1976,21(4):255-271.
 
【10】崔佳,曲敏杰,刘伟,等.聚氨酯改性环氧树脂的研究[J].工程塑料应用,2009,37(2):24-27.
 
【11】呈军,毕曙光,陈雷,等.聚氨酯改性环氧树脂的研究[J].热固性树脂,2009,24(3):25-28.
 
【12】黄先威,刘竞超,万金涛,等.刚性聚氨酯增韧改性环氧树脂的研究[J].工程塑料应用,2005,33(2):19-22.
 
【13】WATSON J D,MUTTON D J.Metalographic observations of abrasive wear machanisms[J].Aust Inst Met,1976,21(4):255-271.
 
【14】周永欣.SiC颗粒增强钢基表面复合材料的制备及冲蚀磨损性能研究[D].西安:西安建筑科技大学,2007.
 
【15】FINNIE I.Some reflections on the past and furture of erosion[J].Wear,1995,186/187:1-10.
 
相关信息
   标题 相关频次
 环境温度对聚氨酯弹性体/环氧复合板力学性能的影响
 3
 消失模铸渗法制备SiC颗粒增强钢基表面复合材料
 3
 14%SiC/7A04铝基复合材料的加工图
 2
 Al2O3连续增强铝基复合材料的干摩擦磨损特性
 2
 API油管接箍液固两相流体冲蚀数值模拟
 2
 SiCp增强镁-锌-锆合金基复合材料的阻尼性能
 2
 SiC和石墨颗粒混杂增强铜基复合材料的摩擦磨损性能
 2
 SiC质量分数对SiCp/6061铝基复合材料组织和性能的影响
 2
 Ti3SiC2材料的力学性能及抗损伤机制
 2
 材料冲蚀磨损的数值模拟研究现状及展望
 2
 测试温度范围对环氧树脂平均线膨胀系数的影响
 2
 超高效液相色谱-质谱法测定环氧树脂粘结剂中双酚A
 2
 超速预加载叶轮弹塑性模拟与试验验证
 2
 氮气钻井过程中的耐冲蚀涂层
 2
 氮气钻井过程中井口多功能四通的使用寿命
 2
 导电防腐蚀涂层对电网接地体碳钢的防护行为
 2
 恶劣大气环境中输变电金属设施防腐蚀涂层制备及性能
 2
 反应熔渗烧结法制备Ti3SiC2材料及其抗弯强度
 2
 反应烧结制备Ti3SiC2材料
 2
 非等温DSC法研究环氧树脂/空心玻璃微珠体系固化动力学
 2
 废碱处理塔纯镍蒸汽分布器失效分析
 2
 改性丙烯酸酯金属防腐蚀涂料的研究进展
 2
 高温高硫油气管线的腐蚀分析及对策
 2
 硅烷和聚氨酯复合改性醇酸树脂双组份涂料的性能
 2
 杭州湾跨海大桥钢管桩的涂层防护
 2
 核电厂二回路冷却系统的冲蚀管理
 2
 环氧树脂基固体浮力材料的吸水性及压缩性
 2
 环氧树脂及环氧树脂基固体浮力材料吸水性研究进展
 2
 基于CFD软件的管道弯头冲蚀数值模拟及弯头测厚布点优化
 2
 基于斯托克斯数的弯管冲蚀数值模拟
 2