7050铝合金的表面增压喷丸纳米化
          
Surface Nanocrystallization of 7050 Aluminium Alloy by Added-Pressure Shot Peening

摘    要
在普通喷丸设备上加增压罐,采用增压喷丸方法对7050铝合金表面进行喷丸处理;用X射线衍射仪、光学显微镜、透射电镜、选区电子衍射仪等对合金表层结构进行了观察与分析,并用显微硬度计测试了表层的硬度.结果表明:经增压喷丸处理后7050铝合金表层的衍射峰明显宽化,随着处理时间的增加,塑性变形层厚度增加,表层晶粒细化至纳米级,平均晶粒尺寸约为40 nm;纳米化后的合金表层硬度比心部硬度提高了1.5倍,其原因可归结为细晶强化及加工硬化.
标    签 表面纳米化   增压   喷丸   铝合金   surface nanocrystallization   added-pressure   shot peening   aluminium alloy  
 
Abstract
A technique called added-pressure shot peening (APSP),which combined with a pressurizing vessel in the common shot peening equipment,had been applied to shot peen on the surface of 7050 aluminium alloy.X-ray diffraction,optical microscope,transmission electron microscopy and selected area electron diffraction were employed to observe and analyze the surface microstructure as well as microhardness tester for the microhardness of the surface layer.The results show that after treatment the diffraction peak of the alloy surface brodened obvionsly.The thickness of plastic deformation layer increased as the treatment time increase,the surface layer grain was refined into nanometer about 40 nm.The microhardness of nanostructure surface increased by 1.5 times which could be attributed to reduction of grain size and work hardening.

中图分类号 TG142.31

 
  中国光学期刊网论文下载说明


所属栏目 新材料 新工艺

基金项目 广东省教育部产学研结合项目(2008B090500084)

收稿日期 2008/11/17

修改稿日期 2009/9/4

网络出版日期

作者单位点击查看

备注麦永津(1984-),男,广东佛山人,硕士研究生.

引用该论文: MAI Yong-jin,JIE Xiao-hua,YU Neng,ZHENG Xiang-xin,LU Guo-hui. Surface Nanocrystallization of 7050 Aluminium Alloy by Added-Pressure Shot Peening[J]. Materials for mechancial engineering, 2009, 33(12): 50~53
麦永津,揭晓华,于能,郑向新,卢国辉. 7050铝合金的表面增压喷丸纳米化[J]. 机械工程材料, 2009, 33(12): 50~53


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】ZHU K Y,VASSEL A,BRISSET F,et al.Nanostructure formation mechanism of a titanium using SMAT[J].Acta Mater,2004,52(14):4101-4110.
 
【2】LIU G,LU J,LU K,et al.Surface nanocrystallization of 316 stainless steel induced by ultrasonic shot peening[J].Mater Sci Eng A,2000,286(1):91-95.
 
【3】LIU G,WANG S C,LOU X F,et al.Low carbon steel with nanostructured surface layer induced by high energy shot peening[J].Scr Mater,2001,44(8):1791-1795.
 
【4】巴德玛,马世宁,李长青,等.超音速微粒轰击45钢表面纳米化的研究[J].材料科学与工艺,2007,5(3):342-346.
 
【5】KLUG H P,ALEXANDER L E.X-ray diffraction procedures for polycrystalline and amorphous materials[M].New York:John Wiley & Sons Wiley,1974:491-494.
 
相关信息
   标题 相关频次
 变形铝合金显微组织阳极复膜显示技术
 8
 碳纳米管/铅锡复合镀层的腐蚀特征
 4
 碳纳米管/铅锡合金复合镀层的摩擦磨损性能
 4
 共晶铝-镁-锌储能合金的热稳定性和液态腐蚀性
 3
 6061铝合金上硅烷膜的制备与性能
 2
 A356铝合金车轮T6热处理工艺的优化
 2
 AISI403钢电站汽轮机叶片喷丸残余应力分布
 2
 DD3镍基单晶高温合金喷丸层残余应力的X射线衍射分析
 2
 LY12M铝合金板同步冷却热拉伸后的组织与性能
 2
 PTFE/7075铝合金镶嵌型自润滑材料的摩擦学行为
 2
 TiB2/Al复合材料喷丸后微区残余应力的有限元模拟
 2
 表面机械研磨处理后Zr-4合金的组织与性能
 2
 表面纳米化材料横截面透射电镜试样的制备
 2
 表面纳米化处理对Cr5Mo钢流动加速腐蚀性能的影响
 2
 表面纳米化对SS400钢应力腐蚀性能的影响
 2
 表面纳米化对渗锌过程的影响
 2
 表面状态对铝合金铸件荧光渗透检测的影响
 2
 不同铝合金在硫酸液中硬质阳极氧化工艺的研究
 2
 不同强度喷丸处理后铝锂合金表面的残余应力
 2
 纯铝表面机械研磨纳米化后的显微组织和硬度
 2
 电磁连铸Al-1%Si棒材的组织和力学性能
 2
 二溴对甲基偶氮磺褪色光度法测定铝合金中微量铬
 2
 非晶态Cr-C合金镀层制备及其耐腐蚀性
 2
 高浓度氯离子溶液中Y112铝合金缓蚀剂的电化学研究
 2
 缓蚀剂对LY12铝合金搭接件疲劳寿命的影响
 2
 机械加工方式实现表面自身纳米化设备
 2
 基于蒙特卡洛法的铝合金抗拉强度测量不确定度评定
 2
 进口铸铝合金件阳极氧化膜的分析
 2
 矿用圆环链条接链环喷丸后残余应力分析
 2
 铝合金表面钴盐法制备钴-锰复合转化膜
 2