包覆镍CNTs/AM60复合材料铸态显微组织与力学性能
          
Microstructure and Mechanical Properties of Carbon Nanotubes Coated by Ni/AM60 Alloy Composite

摘    要
采用机械搅拌铸造法制备了包覆镍碳纳米管(CNTs)/AM60复合材料,研究了包覆镍CNTs加入量对铸态复合材料力学性能的影响规律,并用扫描电子显微镜观察了复合材料的拉伸断口形貌以及显微组织.结果表明:复合材料显微组织为等轴晶,包覆镍的CNTs主要分布在α-Mg共晶相内和晶界处,不仅起到细化晶粒的作用,而且还起到搭接晶粒和强化晶界的作用;复合材料的力学性能随CNTs加入量的增多呈现先增大后减小的趋势,当其质量分数为1%时,抗拉强度、显微硬度、伸长率同时达到最大,比AM60镁合金分别提高了46.23%,41.82%,74.52%,弹性模量在其质量分数为1.2%时达到最大.
标    签 AM60镁合金   碳纳米管   复合材料   显微组织   力学性能   AM60 magnesium alloy   carbon nanotube   composite   microstructure   mechanical property  
 
Abstract
Carbon nanotubes(CNTs) coated by Ni/AM60 magnesium alloy composite was fabricated by mechanical stirring casting technology.The effect of carbon nanotubes content on the mechanical properties of as-cast composites was studied.The microstructure and fractographs were observed and analyzed by using scanning electron microscopy.The results show that the microstructure of the composite was equiaxed grains and the CNTs coated by Ni mainly distributed on the eutectic phase and eutectic boundaries,which not only had the role of refining grains,but also played the role of lapping grains and strengthening grain boundaries.Mechanical properties of the composite first increased and then decreased as the CNTs addition increased when the mass fraction was 1%.The tensile strength,microhardness and elongation were maximized at the same time,increased 46.23%,41.82%,7452% respectively compared to the AM60 magnesium alloy.The elastic modulus was maximized when mass fraction was 1.2%.

中图分类号 TG146.2 TB333

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及其应用

基金项目 江西省科技厅攻关项目(z02727)

收稿日期 2008/9/16

修改稿日期 2009/4/15

网络出版日期

作者单位点击查看

备注徐强(1985-),男,江西萍乡人,硕士研究生.

引用该论文: XU Qiang,ZENG Xiao-shu,XU Yao-yong,YUAN Qiu-hong. Microstructure and Mechanical Properties of Carbon Nanotubes Coated by Ni/AM60 Alloy Composite[J]. Materials for mechancial engineering, 2009, 33(10): 53~56
徐强,曾效舒,徐耀勇,袁秋红. 包覆镍CNTs/AM60复合材料铸态显微组织与力学性能[J]. 机械工程材料, 2009, 33(10): 53~56


被引情况:


【1】袁秋红,曾效舒,吴俊斌, "石墨烯增强AZ91镁基复合材料的力学性能",机械工程材料 40, 43-48(2016)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】师昌绪,李恒德,王淀佐,等.加速我国金属镁工业发展的建议[J].材料导报,2001,15(4):5-6.
 
【2】刘正,张奎,曾小勤.镁基轻质合金理论基础及其应用[M].北京:机械工业出版社,2002:199-201.
 
【3】胡茂良,吉泽升,宋润宾,等.镁基复合材料国内外研究现状及展望[J].轻合金加工技术,2004,32(11):10-15.
 
【4】张修庆,腾新营,王浩伟.镁基复合材料的制备工艺[J].热加工工艺,2004(3):58-61.
 
【5】IIJIMA S.Helical microtubules of graphitic carbon[J].Nature,1991,354:56-58.
 
【6】BAUGHMAN R H,ZAKHIDOV A A,HEER W A.Carbon nanotubes-the route toward applications[J].Science,2002,297:787-792.
 
【7】DENG C F,WANG D Z,ZHANG X X,et al.Processing and properties of carbon nanotubes reinforced aluminum composites[J].Mater Sci Eng A,2007,444:138-145.
 
【8】KUZUMAKI T,MIYAZAWA K,ICHINOSE H,et al.Processing of carbon nanotube reinforced aluminum composite[J].J Mater Res,1998,13(9):2445-2449.
 
【9】KYUNG T K,SEUNG I C,SEONG H H,et al.Microstructures and tensile behavior of carbon nanotube reinforced Cu matrix nanocomposites[J].Mater Sci Eng A,2006,430:27-33.
 
【10】MORISADA Y,FUJII H,NAGAOKA T,et al.MWCNTs/AZ31 surface composites fabricated by friction stir processing[J].Mater Sci Eng A,2006,419:344-348.
 
【11】YANG J,SCHALLER R.Mechanical spectroscopy of Mg reinforced with Al2O3 short fibers and C nanotubes[J].Mater Sci Eng A,2004,370:512-515.
 
【12】WANG F X,GAO X P,LU Z W,et al.Electrochemical properties of Mg-based alloys containing carbon nanotubes[J].Journal of Alloys and Compounds,2004,370(12):326-330.
 
【13】XI Y L,CHAI D L,ZHANG W X,et al.Titanium alloy reinforced magnesium matrix composite with improved mechanical properties[J].Sci Mater,2006,54(1):19-23.
 
【14】BAUGHMAN R H,ZAKHIDOV A A,HEER W A.Carbon nanotubes-the route toward applications[J].Science,2002,297:787-792.
 
【15】GOH C S,WEI J,LEE L C,et al.Simultaneous enhancement in strength and ductility by reinforcing magnesium with carbon nanotubes[J].Mater Sci Eng A,2006,423:153-156.
 
【16】袁秋红,曾效舒,戚道华.T4态CNTs/ZM5镁基复合材料的研究[J].特种铸造及有色金属合金,2007,27(12):963-965.
 
相关信息
   标题 相关频次
 包覆镍的碳纳米管增强AZ91镁基复合材料的显微组织与力学性能
 8
 石墨烯增强AZ91镁基复合材料的力学性能
 8
 碳纳米管/ZM5复合材料的高温拉伸性能与显微组织
 7
 CNTs/AZ91复合材料的摩擦磨损性能
 6
 高速剪切对碳纳米管/环氧树脂复合材料导电性能的影响
 6
 钕对AM60镁合金显微组织和力学性能的影响
 6
 碳纳米管/酚醛树脂基复合材料的研究进展
 5
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 4
 2024铝合金电子束焊接接头的显微组织与力学性能
 4
 240 MPa级高强IF钢的冷轧压下率和退火温度
 4
 300 MW机组锁口叶片断裂原因分析
 4
 3003铝合金无缝管制备过程中的显微组织与力学性能变化
 4
 3D打印18Ni300模具钢的显微组织及力学性能
 4
 600 MW机组次末级叶片断裂原因分析
 4
 6061-T6铝合金搅拌摩擦焊接头的组织和性能
 4
 6082-T6铝合金搅拌摩擦焊接头的显微组织与力学性能
 4
 7075/6009铝合金层状复合板材的固溶时效热处理工艺
 4
 7A60-T6超高强铝合金搅拌摩擦焊接头的组织及性能
 4
 960MPa级含钼低碳钢钼含量与热处理工艺的确定
 4
 9Ni钢手工电弧焊和自动埋弧焊接头的组织及力学性能
 4
 B-HARD400钢板自动火焰切割热影响区深度的判定
 4
 Ca-α/β-Sialon结合刚玉复合材料的力学性能
 4
 Domex700MC低合金高强钢药芯焊丝CO2气体保护焊焊接接头的组织与性能
 4
 Fe24Mn0.5C形变孪晶诱发塑性钢的显微组织和力学性能
 4
 Mg-5Zn-xEr-1.5Nd-0.5Zr(1.1
 4
 Mg-6Al-2Sr-xY镁合金的显微组织和力学性能
 4
 MGF/PLA复合材料的制备及性能
 4
 PP-g-MAH改性SGF+POE/FPP复合材料的制备及性能
 4
 QT400-18L铸件的缩松缺陷对其力学性能的影响
 4
 R60702锆材CO2激光焊的气体保护及接头的组织、力学性能
 4