T700和T300碳纤维增强环氧树脂基复合材料耐湿热老化性能的对比
          
Comparison of Wet and Hot Aging Resistance of T700 and T300 Carbon Fiber Strengthened Epoxy Resin Composites

摘    要
在温度为70 ℃、相对湿度为85%的湿热环境下,分别对T700碳纤维/环氧树脂基复合材料、T300碳纤维/环氧树脂基复合材料以及两种复合材料/金属胶接结构进行了70 d的加速老化试验,并对老化前后的试样进行了力学性能试验和无损检测.结果表明:湿热环境没有改变两种复合材料的破坏模式,但使复合材料的纵、横向压缩强度和剪切强度略有降低;对复合材料/金属胶接结构,湿热老化环境不会导致胶接界面产生损伤,但会使胶接强度下降;老化前两种复合材料的力学性能基本相当,老化70 d后T700碳纤维/环氧树脂基复合材料的性能保持率略优.
标    签 复合材料   湿热老化   加速试验   性能保持率   composite   hydrothermal aging   accelerated experiment   property conservation percentage  
 
Abstract
Accelerated aging experiments of T700 and T300 carbon fiber/epoxy resin composites,as well as two types of composite/metal adhesive joints were carried out respectively for 70 d in a hot-wet environment with temperature of 70 ℃ and relative humidity of 85%.Mechanical property tests and nondestructive test (NDT) of the samples before and after aging were also performed.The results show that the hygrothermal environment did not change the failure modes of the two types of composite samples,but decreased slightly the longitudinal/lateral compressive strength and shear strength.For composite/metal joints,the hydrothermal environment could not bring about damage at the bonding interface,but could bring down its shear strength.The mechanical properties of T700/epoxy resin composite were equivalent to those of T300/epoxy resin composite before aging,while the former was superior to the latter in respect to the property conservation percentage after aging for 70 d.

中图分类号 V258.3

 
  中国光学期刊网论文下载说明


所属栏目 新材料 新工艺

基金项目

收稿日期 2008/6/5

修改稿日期 2009/1/21

网络出版日期

作者单位点击查看

备注余治国(1977-),男,湖南临湘人,博士研究生.

引用该论文: YU Zhi-guo,YANG Sheng-chun,SONG Bi-feng. Comparison of Wet and Hot Aging Resistance of T700 and T300 Carbon Fiber Strengthened Epoxy Resin Composites[J]. Materials for mechancial engineering, 2009, 33(6): 48~51
余治国,杨胜春,宋笔锋. T700和T300碳纤维增强环氧树脂基复合材料耐湿热老化性能的对比[J]. 机械工程材料, 2009, 33(6): 48~51


被引情况:


【1】王占彬,张天骄,范金娟,黄超, "T300/648复合材料的湿热老化行为",机械工程材料 39, 44-47(2015)

【2】赵庆,秦旭达,张心沛,李永行,吉春辉, "基于响应曲面法的碳纤维增强复合材料螺旋铣孔轴向切削力预测",机械工程材料 39, 108-112(2015)

【3】回丽,张旭,许磊,王勇刚, "纤维/环氧树脂复合材料湿热老化后的力学性能",机械工程材料 40, 62-65(2016)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】李晓骏,许风和,陈新文.先进聚合物基复合材料的热氧老化研究[J].材料工程,1999(12):19-22.
 
【2】过梅丽,肇研,许凤和.先进聚合物基复合材料的老化研究-Ⅰ.热氧老化[J].航空学报,2000,21(4):62-65.
 
【3】KUMAR B G,SINGH R P.Degradation of carbon fiber-reinforced epoxy composites by ultraviolet radiation and condensation[J].Journal of Composite Materials,2002,36(24):2713-2733.
 
【4】SELZER R,FRIEDRICH K.Influence of water up-take on inter-laminar fracture properties of carbon fibre-reinforced polymer composites[J].Journal of Materials Science,1995,30:334-338.
 
【5】SELZER R,FRIEDRICH K.Mechanical properties and fai-lure behavior of carbon fibre-reinforced polymer composites under the influence of moisture[J].Composites A,1997,28:595-604.
 
【6】李晓骏,陈新文.复合材料加速老化条件下的力学性能研究[J].航空材料学报,2003,23(增刊):286-290.
 
【7】王再玉,喻国生,严旭,等.T700碳纤维增强树脂复合材料力学性能试验研究[J].洪都科技,2007(2):42-46.
 
【8】WANG J Z,PARVATAREDDY T,CHANG T,et al.Physical aging behavior of high-performance cornposites[J].Composites Science and Technology,1995,54(4):405-415.
 
【9】王晓洁,梁国正,张炜,等.湿热老化对高性能复合材料性能的影响[J].固体火箭技术,2006,29(3):301-304.
 
【10】PASRICHA A,DILLARD D A,TUTTLE M E.Effect of physical aging and variable stress history on the strain response of polymeric composites[J].Composites Science and Technology,1997,57(9/10):1271-1279.
 
【11】叶宏军,詹美珍.T300/4211复合材料的使用寿命评估[J].材料工程,1995(10):3-5.
 
【12】中国航空研究院.复合材料结构设计手册[M].北京:航空工业出版社,2001.
 
【13】陈明安,谢玄,李慧中,等.湿热条件对于含硫SCA处理LY12与环氧树脂粘接强度的影响规律[J].航空材料学报,2007,27(2):46-51.
 
【14】陈纲,郦正能,寇长河.湿热环境对缝纫层合板及含孔板压缩性能的影响[J].强度与环境,2004,31(1):46-49.
 
相关信息
   标题 相关频次
 复合材料L型筋条-蒙皮胶接界面失效过程的数值模拟
 4
 T300/648复合材料的湿热老化行为
 3
 C/SiC复合材料拉伸过程的声发射研究
 2
 Ca-α/β-Sialon结合刚玉复合材料的力学性能
 2
 MGF/PLA复合材料的制备及性能
 2
 MoS2、CdO及聚全氟乙丙烯填充改性聚四氟乙烯
 2
 PP-g-MAH改性SGF+POE/FPP复合材料的制备及性能
 2
 Si3N4p-SiCw/MoSi2复合材料的强韧化效果与机制
 2
 SiCf/Ti-6Al-4V复合材料的界面反应及其影响
 2
 SiCP/6061Al复合材料高温单轴拉伸时相关棘轮行为的细观本构模型
 2
 SiC颗粒增强铝基复合材料的摩擦磨损性能
 2
 TiB2/Al复合材料喷丸后微区残余应力的有限元模拟
 2
 YANG XiaoLin,LV BoPing,XIAN MingLe
 2
 ZrO2与HA复合粉体的烧结行为
 2
 包覆镍CNTs/AM60复合材料铸态显微组织与力学性能
 2
 包覆镍的碳纳米管增强AZ91镁基复合材料的显微组织与力学性能
 2
 表面处理方法对剑麻纤维/酚醛树脂复合材料性能的影响
 2
 波音737飞机发动机反推装置内侧壁板复合材料的无损检测
 2
 残余热应力对复合材料双面胶接含裂纹铝合金板修复结构疲劳寿命的影响
 2
 层压结构复合材料的激光剪切散斑检测
 2
 电化学阻抗法研究土壤模拟溶液中CFRP/碳钢体系的腐蚀行为
 2
 芳纶毡体/阻尼弹性薄膜复合材料的吸声隔声性能
 2
 放电等离子烧结制备M42/45钢双金属复合材料及界面形成机理
 2
 飞机复合材料构件的原位红外热成像检测
 2
 飞机结构健康监测传感器新技术
 2
 分层损伤和完好复合材料薄壁加筋板的后屈曲承载能力及破坏形式
 2
 复合材料结构中R区超声反射信号特征及其检测应用
 2
 高速剪切对碳纳米管/环氧树脂复合材料导电性能的影响
 2
 高速列车制动盘材料的研究现状与展望
 2
 红外热波技术在飞机复合材料损伤检测中的应用
 2