微孔发泡聚丙烯材料泡孔尺寸测量的新方法
          
A New Measurement Method for Cell Dimension of Microcellular Foaming Material of Polypropylene

摘    要
通过使用高精度分光光度仪测量微孔发泡聚丙烯材料表面可见光的反射率来定量表征发泡材料内部的泡孔尺寸及分散状态,得到了发泡材料泡孔尺寸与反射率之间的关系.结果表明:微孔发泡聚丙烯表面光的反射率能够反映材料的发泡情况,反射率越大泡孔越小,反之则泡孔越大;通过最佳平方逼近建立起泡孔直径y与反射率x的函数关系:y=-12.772 8 x+798.553 7.
标    签 发泡   聚丙烯   可见光   泡孔直径   反射率   foaming   PP   visible light   cell diameter   reflectivity  
 
Abstract
Spectrophotometer was used to measure the visible light reflectivity on the surface of foaming polypropylene material to quantitatively characterize the cell dimension and dispersing state of the foaming material.The relationship between the cell dimension and visible light reflectivity was discussed.The visible light reflectivity of the surface of polypropylene foaming material reflect foaming instance.When the reflectivity is greater,the cell is smaller,and the reverse is true.Through best square approximation the relationship between cell diameter y and reflectivity x was established as following:y=-12.772 8 x+798.553 7.

中图分类号 TG146.1

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 国家863计划资助项目(2003AA33X080)

收稿日期 2008/11/4

修改稿日期 2008/3/26

网络出版日期

作者单位点击查看

备注朱坤鹏(1982-),男,辽宁沈阳人,硕士研究生.

引用该论文: ZHU Kun-peng,HE Li,ZHOU Yi,LI Liang,ZHANG Chun. A New Measurement Method for Cell Dimension of Microcellular Foaming Material of Polypropylene[J]. Materials for mechancial engineering, 2008, 32(11): 13~15
朱坤鹏,何力,周义,李良,张纯. 微孔发泡聚丙烯材料泡孔尺寸测量的新方法[J]. 机械工程材料, 2008, 32(11): 13~15


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】Kumar V,Vandarwel M,Weller J.Experimental characterization of the tensile behavior of microcellar polycarhonate foam[J].Eng Mat Tech,1994,116(4):439-445.
 
【2】Park C B,Cheung L K.A study of cell nucleation in the extrusion of polypropylene foam[J].Polymer Engineering and Science,1997,37:1-5.
 
【3】Sato Y,Yamasaki Y,Takishima S H,et al.Precise measurements of PVC of polypropylene and polycarbonate[J].Appl Polym Sci,1997,66:141-150.
 
【4】Van Calster M.High melt strength PP foams for the automotive and packaging industries[J].Foamplas,1997,97:149-151.
 
【5】何颖,周丽,龚维,等.微孔发泡聚丙烯的性能研究[J].现代机械,2006(3):67-68.
 
【6】徐志娟,何继敏,朱复华,等.聚丙烯挤出发泡中“熔体破裂”现象分析[J].塑料工业,2005,31(1):30-34.
 
【7】李小梅,马如,陈立荣,等译.颜色技术原理[M].北京:化学工业出版社,2002:124-126.
 
【8】何曼君,陈维孝,董西侠.高分子物理[M].上海:复旦大学出版社,2005:38-40.
 
相关信息
   标题 相关频次
 反相高效液相色谱法测定N-{3-[3-(二甲基氨基)-1-氧基-2-丙烯基]-苯基}乙酰胺及其相关物质
 2
 高效液相色谱法测定(E)-3-乙基-(2,3-二氢苯并呋喃-5-基)-2-丙烯酸乙酯及其相关物质的含量
 2
 高效液相色谱法测定制药中间体7-甲氧基-1-萘基乙腈
 2
 高效液相色谱法同时测定复方草珊瑚含片中四种活性成分
 2
 聚丙烯发泡成型技术的研究进展
 2
 可见光催化剂La/S-TiO2/SBA-15的表征及其对2,4-二氯酚的降解
 2
 可见光响应TiO2/Bi4Ti3O12复合粉的制备及表征
 2
 拉伸速度和制样方式对聚苯乙烯和聚丙烯拉伸性能的影响
 2
 离子色谱法同时测定奶粉中亚硝酸根、硝酸根、氯离子和磷酸根
 2
 青铜文物修复与保护进展
 2
 牺牲阳极法阴极保护在南水北调预应力钢筒混凝土管道上的应用
 2
 #高分子周报#北美树脂生产商的新年愿望
 1
 #高分子周报#替代传统聚氨酯的可再生泡沫
 1
 2017年聚丙烯改性三大新方向!
 1
 3微米超薄型薄膜实现量产 打破国外垄断局面
 1
 600 MW超临界机组低压转子叶片开裂分析
 1
 Laves相Ta-Cr系合金的高温抗氧化性研究进展
 1
 PP-g-MAH改性SGF+POE/FPP复合材料的制备及性能
 1
 PP改性塑料性能大幅上涨 成为中国保险杠专用材料
 1
 TC4合金微动疲劳损伤研究
 1
 表面处理对剑麻纤维增强聚丙烯复合材料力学性能的影响
 1
 布氏硬度试验标准GB/T 231与ASTM E10的差异分析及其在石油装备行业中的应用
 1
 二维红外光谱法分析聚丙烯C-H伸缩振动
 1
 分散液液微萃取-气相色谱-质谱法测定水样中4种环境激素
 1
 粉煤灰/聚丙烯复合材料的非等温结晶动力学行为
 1
 复旦大学武利民教授团队在可见光超材料研究中取得重要进展
 1
 过氧化苯甲酰对偶氮二甲酰胺在硅橡胶中发泡行为的影响
 1
 华东电网统计型潮流分析指标的研究与应用
 1
 华东电网统计型潮流评价指标的分析与应用
 1
 化学镀镍反应副产物H2的影响和措施
 1