麦秸纤维/聚丙烯复合材料的制备与力学性能
          
Preparation and Mechanical Properties of Wheat Straw Fiber/Polypropylene Composites

摘    要
采用热磨提取法提取麦秸纤维,研究了硅烷偶联剂种类、麦秸纤维含量以及相容剂MAPP含量对麦秸纤维与废旧聚丙烯间的界面相容性以及制备的复合材料力学性能的影响;用扫描电镜和三维体视显微镜观察了麦秸纤维的分散性以及复合材料冲击断口形貌.结果表明:经3% KH550处理后,麦秸纤维与废旧聚丙烯间的相容性得到明显改善,提高了复合材料的力学性能;当麦秸纤维质量分数为20%左右时,其在废旧聚丙烯基体中分散均匀,增强效果最佳;且当MAPP质量分数为8%左右时,材料的抗拉、抗弯以及抗冲击强度均达到最大值,分别为61.14 MPa、68.25 MPa和11.25 kJ·m-2.
标    签 麦秸纤维   聚丙烯   相容性   力学性能   wheat straw fiber   polypropylene   compatibility   mechanical property  
 
Abstract
Effects of the kinds of coupling agent,amount of wheat straw fibers obtained by thermal-mechanical extraction and compatibilizer MAPP on the interfacial compatibility between wheat straw fibers and waste polypropylene as well as the mechanical properties of the composites were studied.Dispersion of wheat straw fibers and surface morphology of impact fracture were observed by SEM and stereo-microscope.The results showed that after wheat straw fibers treated by 3% KH550,the mechanical properties of composites were significantly improved because of the good interfacial adhesion.When the amount of wheat strow fibers was about 20wt%,they dispersed evenly in waste polypropylene and the reinforced effect was the best.Tensile strength,flexile strength and impact strength of the composites with 8wt% MAPP were maximum,which were 61.14 MPa,68.25MPa and 1125 kJ·m-2 respectively.

中图分类号 TB332

 
  中国光学期刊网论文下载说明


所属栏目 新材料 新工艺

基金项目

收稿日期 2007/10/5

修改稿日期 2008/1/10

网络出版日期

作者单位点击查看

备注孟召辉(1982-),女,天津人,硕士研究生.

引用该论文: MENG Zhao-hui,YAO Zheng-jun,LIANG En-quan,ZHOU Jin-tang. Preparation and Mechanical Properties of Wheat Straw Fiber/Polypropylene Composites[J]. Materials for mechancial engineering, 2008, 32(10): 35~39
孟召辉,姚正军,梁恩泉,周金堂. 麦秸纤维/聚丙烯复合材料的制备与力学性能[J]. 机械工程材料, 2008, 32(10): 35~39


被引情况:


【1】梁恩泉,姚正军,周娟娟,周金堂, "Al(OH)3阻燃剂含量对麦秸纤维/废旧聚丙烯再生复合材料性能的影响",机械工程材料 34, 56-59(2010)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】Ayse Alemdar,Mohini Sain.Isolation and characterization of nanofibers from agricultural residues-Wheat straw and soy hulls[J].Bioresource Technology,2007,97(2):1-8.
 
【2】Panthapulakkal S,Zereshkian A,Sain M.Preparation and characterization of wheat straw fibers for reinforcing application in injection molded thermoplastic composites[J].Bioresource Technology,2006,97(2):265-272.
 
【3】Suhara Panthapulakkal,Mohini Sain.Injection molded wheat straw and corn stem filled polypropylene composites[J].Journal of Polymers and the Environment,2006,14(3):265-272.典平鸽,杜玲枝.废旧塑料的综合利用[J].浙江化工,2006,37(3):28-32.
 
【4】赵正湘.废塑料物品是值得开发利用的再生资源[J].中国资源综合利用,2006,24(2):36-38.
 
【5】吴自强,唐四丁,胡海.废旧聚丙烯回收利用技术的现状及发展趋势[J].再生资源研究,2002(1):25-27.
 
【6】李本贵.植物纤维与热塑性塑料复合界面相容性研究[J].企业技术开发,2006,25(1):24-26.
 
【7】郑玉涛,陈就记,曹德榕.改进植物纤维/热塑性塑料复合材料界面相容性的技术进展[J].纤维素科学与技术,2005,13(1):45-55.
 
【8】吴章康,周定国.稻草原料表面特性FTIR和XPS分析[J].木材工业,2003,17(6):6-8.
 
【9】鲁博,张林文,曾竟成.天然纤维复合材料[M].北京:化学工业出版社,2005.
 
相关信息
   标题 相关频次
 Al(OH)3阻燃剂含量对麦秸纤维/废旧聚丙烯再生复合材料性能的影响
 8
 POE增韧改性回收PP的注塑成型工艺及其性能
 6
 PP-g-MAH改性SGF+POE/FPP复合材料的制备及性能
 4
 表面处理对剑麻纤维增强聚丙烯复合材料力学性能的影响
 4
 纳米二氧化钛增强聚丙烯复合泡沫材料的性能
 4
 稀土钕对亚共晶铝硅合金组织及性能的影响
 4
 中空玻璃微珠改性PP泡沫复合材料的发泡效果和力学性能
 4
 纳米CaCO3添加量对其改性聚丙烯复合材料发泡效果及力学性能的影响
 3
 1.25Cr0.5MoSi钢的焊接工艺评定
 2
 1060工业纯铝累积叠轧后的力学性能
 2
 1060铝在累积轧制中组织和性能的演变
 2
 14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能
 2
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 2
 2 000 t水压机立柱断裂分析
 2
 2024铝合金电子束焊接接头的显微组织与力学性能
 2
 20Cr钢与B级钢焊接接头的组织和性能
 2
 20钢表面双辉等离子钨-碳渗镀层制备及其耐磨性能
 2
 2205双相不锈钢/Q345低合金钢爆炸复合板的组织与力学性能
 2
 22Mn2SiVBS热轧无缝钢管控冷时的组织与性能
 2
 240 MPa级高强IF钢的冷轧压下率和退火温度
 2
 25Cr2MoVA钢调质规范对力学性能的影响
 2
 2GPa高压处理对铜铝合金显微组织和性能的影响
 2
 300 MW机组锁口叶片断裂原因分析
 2
 3003铝合金无缝管制备过程中的显微组织与力学性能变化
 2
 3D打印18Ni300模具钢的显微组织及力学性能
 2
 40CrNi2Mo钢的低温力学性能
 2
 5083铝合金搅拌摩擦焊接头的显微组织与力学性能
 2
 600 MW机组次末级叶片断裂原因分析
 2
 6061-T6铝合金超声辅助搅拌摩擦焊接头的组织与力学性能
 2
 6061-T6铝合金搅拌摩擦焊接头的组织和性能
 2