35CrMo钢带泵轴断裂原因分析
          
Failure Analysis of 35CrMo Shaft Driving Pump

杨力   王滨  
摘    要
35CrMo钢带泵轴在使用约40 h后发生断裂,通过宏观断口形貌观察、力学性能试验和金相检验及受力分析等方法对带泵轴断裂原因进行了失效分析.结果表明:带泵轴由于热处理不当造成其疲劳强度降低,服役后发生旋转弯曲疲劳断裂失效.
标    签 35CrMo钢     疲劳断裂   失效分析   35CrMo steel   shaft   fatigue fracture   failure analysis  
 
Abstract
Means of macro-analysis,mechanical property test,metallographic analysis and stress analysis were employed to analyze the cracking reason of 35CrMo shaft driving pump which broke after 40 hours using.The results indicated that fatigue strength of the shaft reduced because of the improper heat treating,which led to the rotary bending fatigue fracture of the shaft during service process.

中图分类号 TG162.71

 
  中国光学期刊网论文下载说明


所属栏目

基金项目

收稿日期 2007/8/20

修改稿日期 2008/4/3

网络出版日期

作者单位点击查看

备注杨力(1966-),女,吉林白城人,高级工程师.

引用该论文: YANG Li,WANG Bin. Failure Analysis of 35CrMo Shaft Driving Pump[J]. Materials for mechancial engineering, 2008, 32(6): 78~81
杨力,王滨. 35CrMo钢带泵轴断裂原因分析[J]. 机械工程材料, 2008, 32(6): 78~81


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】机械工业理化检验人员技术培训和资格鉴定委员会.力学性能试验[M].上海:上海科学普及出版社,2003.
 
【2】机械工程材料性能数据手册编委员.机械工程材料性能数据手册[M].北京:机械工业出版社,1994.
 
相关信息
   标题 相关频次
 脱硫氧化风机轴断裂原因分析
 6
 700 mm轧机轧辊断裂失效分析
 4
 柴油机球铁曲轴断裂失效分析
 4
 柴油机用高强度螺栓断裂失效分析
 4
 船用柴油机活塞连接螺栓断裂失效分析
 4
 大功率风力发电机增速齿轮断裂原因分析
 4
 大型柴油机曲轴断裂失效分析
 4
 大型发电机转子开裂原因初步分析
 4
 高压油泵出油阀紧座断裂失效分析
 4
 活塞销失效原因分析
 4
 纳米压痕技术表征Al2O3/3%TiO2爆炸喷涂涂层的各向异性
 4
 纳米压痕试验标准块均匀性的检验
 4
 氢气压缩机活塞杆断裂失效分析
 4
 沙滩车倒车档轴断裂分析
 4
 石油钻铤断裂原因分析
 4
 吐丝机螺栓断裂的失效分析
 4
 稀土永磁材料NdFeN三种粒度分析方法的比较
 4
 齿轮的失效分析
 3
 吊装过程中吊具断裂失效分析
 3
 10 t吊钩断裂原因分析
 2
 100t汽车车轴断裂分析
 2
 12Cr1MoV珠光体耐热钢长期服役中碳化物的变化及对性能的影响
 2
 16Co14Ni10Cr2MoE钢制抽筒抓钩开裂失效分析
 2
 16Mn集输管线钢在含CO2凝析气田的腐蚀行为
 2
 300 MW机组回转式空气预热器仓格板开裂原因分析
 2
 304不锈钢低温分离器开裂原因分析
 2
 30Cr1Mo1V钢汽轮机转子高应力段的疲劳裂纹扩展速率
 2
 30CrMnSiA钢螺钉断裂失效分析
 2
 30CrMnSiA螺栓失效分析
 2
 316L不锈钢泵轴断裂原因分析
 2