316L不锈钢在熔融LiCl-3%Li2O中的腐蚀行为
          
Hot Corrosion Behaviors of 316L Stainless Steel in LiCl-3%Li2O Molten Salt

摘    要
采用浸没法腐蚀试验研究了在真空及空气两种环境中316L不锈钢在700 ℃熔融LiCl-3%Li2O混合熔盐中的热腐蚀行为.结果表明:316L不锈钢在两种条件下的腐蚀产物均为LiCrO2,腐蚀质量损失均随时间的延长而增大;在真空条件下腐蚀质量损失明显小于空气条件下,氧分压对腐蚀行为的影响显著.
标    签 316L不锈钢   熔盐   腐蚀   316L stainless steel   molten salt   corrosion  
 
Abstract
The hot corrosion behaviors of 316L stainless steel have been studied by immersion experiments in molten LiCl-3%Li2O in air and vacuum at 700 ℃.The corrosion product of both in air and vacuum at 700 ℃ in molten LiCl-3%Li2O is LiCrO2.The weight loss in the two conditions increased with increasing time.The weight loss in vacuum condition is obviously less than that in air condition.The corrosion behavior was obviously affected by the partial pressure of oxygen.

中图分类号 TG172.6

 
  中国光学期刊网论文下载说明


所属栏目

基金项目

收稿日期 2006/5/22

修改稿日期 2006/7/30

网络出版日期

作者单位点击查看

备注常晓亮(1980-),男,吉林长春人,硕士研究生.

引用该论文: CHANG Xiao-liang,WANG Xu,WANG Lan-fang,ZHANG Jun-shan,ZHU Mei-li. Hot Corrosion Behaviors of 316L Stainless Steel in LiCl-3%Li2O Molten Salt[J]. Materials for mechancial engineering, 2007, 31(4): 11~13
常晓亮,王旭,王兰芳,张俊善,祝美丽. 316L不锈钢在熔融LiCl-3%Li2O中的腐蚀行为[J]. 机械工程材料, 2007, 31(4): 11~13


被引情况:


【1】王兰芳,王旭,张俊善,邹龙江, "0Cr18Ni9、1Cr13和1Cr17不锈钢在熔融LiCl-5%Li2O中的腐蚀行为",机械工程材料 32, 19-22(2008)

【2】石照夏,宋志刚,郑文杰,徐瑞东,季祥民,丰涵, "镍铬钼合金在真空熔融CaCl2-20%CaF2盐中的腐蚀行为",机械工程材料 34, 9-13(2010)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】Indacochea J E,Smith J L.Corrosion performance of ferrous and refractory metals in molten salt under reducing conditions[J].J Mater Res,1999,14(5):1990-1995.
 
【2】Indacochea J E,Smith J L,Kitko K R.High-temperature oxidation and corrosion of structural materials in molten chorlides[J].Oxidation of Metals,2001,55(1/2):1-16.
 
【3】Cho S H,Zhang J S,Shins P K,et al.A study on the corrosion behavior of austenitic stainless steel in hot molten salt of LiCl and LiCl-Li2O[J].Korean Journal of Mater Research,1999,9(2):211-216.
 
【4】化学工业部化工机械研究所.腐蚀于防护手册[M].北京:化学工业出版社,1990.
 
【5】Spiegel M,Biedenkopf P,Grabke.Corrosion of iron base alloys and high alloy steels in the Li2CO3-K2CO3 eutectic mixture[J].Corrosion Science,1997,39:1193-1210.
 
【6】李远士,牛焱,吴维詜.金属材料的高温氯化腐蚀[J].腐蚀科学与防护技术,2000,12(1):41-44.
 
【7】马海涛.高温氯盐环境中金属材料的腐蚀[D].大连:大连理工大学,2003.
 
相关信息
   标题 相关频次
 Ti3Al金属间化合物在熔融LiCl-Li2O中的热腐蚀行为
 8
 0Cr18Ni9、1Cr13和1Cr17不锈钢在熔融LiCl-5%Li2O中的腐蚀行为
 6
 T0103苯甲酸蒸馏塔内壁腐蚀沟槽产生原因
 4
 超临界水氧化城市污泥中316L不锈钢的腐蚀行为
 4
 醋酸回收罐进口管泄漏原因
 4
 腐蚀对TC17钛合金超高周疲劳性能的影响
 4
 海上某油田生产井316L不锈钢毛细管泄漏失效分析
 4
 海水泵叶轮316L不锈钢螺钉的腐蚀原因分析
 4
 聚多巴胺自组装膜对316L不锈钢缓蚀性能的影响
 4
 管线钢在干湿交替环境下的腐蚀
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 2
 20G/316L双金属复合管失效的原因
 2
 20号钢在HCl-H2S-H2O溶液中的腐蚀行为
 2
 220kV钢芯铝绞线断股事故化学分析
 2
 2507双相不锈钢钾盐蒸发罐腐蚀的原因分析
 2
 2A12铝合金当量加速腐蚀试验
 2
 2-甲基咪唑啉及其复配缓蚀剂在高硬度电解质水溶液中的缓蚀性能
 2
 304L不锈钢焊接接头表面状态对其在硼酸溶液中腐蚀行为的影响
 2
 304不锈钢在高温环烷酸介质中的腐蚀行为
 2
 30CrMnSiA合金钢当量加速腐蚀试验
 2
 310S和AL-6XN不锈钢在熔融MgCl2中的腐蚀行为
 2
 316L奥氏体不锈钢在高温水中的应力腐蚀
 2
 316L不锈钢、690合金在氢氧化钠溶液中的电化学性能
 2