AZ31镁合金的阳极氧化新工艺
          
A Novel Anodizing Process for AZ31 Magnesium Alloy

摘    要
开发了一种应用于AZ31镁合金的环保型阳极氧化工艺,讨论了电解液成分、电参数、控制方式、封孔工艺和溶液温度等对阳极氧化的成膜过程以及膜层性能的影响.结果表明:选用KOH、Na2B4O7、Na3PO4及成膜添加剂组成的环保型电解液,控制适当的反应参数,能在镁合金AZ31上形成耐蚀性能高、膜层致密的阳极氧化膜,其性能与电解液的组分有较大的关系,最后的封孔处理能提高阳极氧化膜的耐蚀性.
标    签 镁合金   阳极氧化   腐蚀   magnesium alloy   anodizing   corrosion  
 
Abstract
An environmentally friendly anodizing process for AZ31 magnesium alloy was developed.The factors including components of the electrolyte,electrical parameters,controlling methods,process of sealing and electrolyte temperature that affect the film forming process and the properties of the film were analyzed.High corrosion resistant and compact anodized films were formed on AZ31 magnesium alloy by anodizing in environmentally friendly electrolyte composed of KOH,Na2B4O7,Na3PO4 and addictives.The properties of the anodized film were greatly affected by the composition of the electrolyte and the corrosion resistance of the anodized films was enhanced by sealing process.

中图分类号 TG146.2 TG174.41

 
  中国光学期刊网论文下载说明


所属栏目

基金项目 湖南省科技厅重点资助项目(03JKY1016);湖南省重大专项计划资助项目(04GK1008-1,05GK1006-1)

收稿日期 2005/9/5

修改稿日期 2005/11/12

网络出版日期

作者单位点击查看

备注林燕(1980-),女,四川眉山人,硕士研究生.

引用该论文: LIN Yan,YAN Hong-ge,CHEN Zhen-hua,WANG Hui-min,CHENG Ying-liang,XIE Hong-cai. A Novel Anodizing Process for AZ31 Magnesium Alloy[J]. Materials for mechancial engineering, 2006, 30(10): 38~42
林燕,严红革,陈振华,王慧敏,程英亮,谢洪财. AZ31镁合金的阳极氧化新工艺[J]. 机械工程材料, 2006, 30(10): 38~42


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】Raymond F,Decker.The renaissance of magnesium[J].Adv Mater Process,1998,154(3):31-33.
 
【2】Froes F H,Eliezer D.The Science,Technology and application of magnesium[J].Mine Metals and Mater Soc,1998,5(9):30-34.
 
【3】Makar G L,Kruger J.Corrosion of magnesium[J].International Materials Reviews,1993,38(3):138-153.
 
【4】Rudd A L,Breslin C B,Manfeld F.The corrosion protection afforded by rare earth conversion coatings applied to magnesium[J].Corrosion Science,2000,42(2):275-288.
 
【5】伯克斯 N,迈耶 G H.高温氧化导论[M].北京:冶金工业出版社,1989.
 
【6】吴纯素.化学转化膜[M].北京:化学工业出版社,1989.
 
【7】Zozulin A J.Anodizing coating for magnesium Mg-Al alloys[J].Metal Finishing,1994,92:39-44.
 
【8】Zhang Y J,Yan C W,Wang F H,et al.Study on the environmentally friendly anodizing of AZ91D magnesium alloy[J].Surface and Coatings Technology,2002,161:36-43.
 
【9】Yahalom J.Experimental evaluation of some electrolytic breakdown hypothesis[J].Electrochim Acta,1970,15(9):603-607.
 
相关信息
   标题 相关频次
 镁合金的腐蚀与防护研究进展
 5
 一种新的AZ40镁合金阳极氧化工艺
 5
 AZ31镁合金表面沉积类金刚石薄膜在Hank′s体液中的腐蚀行为
 4
 AZ91铸造镁合金缺陷的超声检测技术
 4
 Sr对AZ31B镁合金微观组织和腐蚀性能的影响
 4
 ZK60镁合金CO2激光焊接接头的显微组织与性能
 4
 变形量和变形速率对AM60铸锭压缩过程中孪晶的影响
 4
 固液混合铸造Al-10Cr合金的耐磨损性能
 4
 含稀土耐蚀Mg-9Al铸造镁合金腐蚀行为研究
 4
 快速凝固结合粉末冶金法制备Al2O3颗粒增强AZ91镁基复合材料的组织与力学性能
 4
 快速凝固结合粉末冶金法制备SiCp/AZ91复合材料的组织及性能
 4
 镁合金腐蚀的影响因素
 4
 热拉深工艺对镁合金制品成形性能的影响
 4
 外框限制轧制工艺在喷射沉积板坯加工中的应用
 4
 硝酸铈对镁合金在硝酸铵溶液中的缓蚀作用
 4
 一种铝基复合材料制动盘用树脂基摩擦材料
 4
 锰粉在水溶液中球磨生成相的研究
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 2
 20G/316L双金属复合管失效的原因
 2
 20号钢在HCl-H2S-H2O溶液中的腐蚀行为
 2
 220kV钢芯铝绞线断股事故化学分析
 2
 2507双相不锈钢钾盐蒸发罐腐蚀的原因分析
 2
 2A12铝合金当量加速腐蚀试验
 2