AISI316L和SAF2205不锈钢在含溴醋酸溶液中腐蚀行为的研究
          
Corrosion Behavior of AISI316L and SAF2205 Stainless Steels in Acetic Acid Solution Containing Br Ion

摘    要
用化学浸泡法对奥氏体不锈钢316L和双相不锈钢SAF2205在含溴醋酸溶液中的腐蚀行为进行了研究,并观察了腐蚀形貌.结果发现:随着温度和Br-浓度的增加,腐蚀速率增大,点蚀程度加剧;随着浸泡时间的增加,不锈钢AISI316L的腐蚀速率迅速降低,而不锈钢SAF2205的腐蚀速率缓慢增大,72h后,两者腐蚀速率的变化都很小;醋酸环境下,Cl-比Br-对两种不锈钢的点蚀危害性更大.在含Cl-醋酸溶液中加入少量Br-,对腐蚀有一定的抑止作用,而在含Br-醋酸溶液中加入少量Cl-,并没有严重的有害影响.
标    签 醋酸   不锈钢   溴离子   腐蚀   acetic acid   stainless steel   Br-   corrosion  
 
Abstract
Corrosion behavior of AISI316L and SAF2205 stainless steels in acetic acid solution containing Br- was investigated by measuring the corrosion weight loss.Pitting characteristic was inspected by optical microscope.The corrosion rate was markedly increased with increasing temperature and Br- concentration.The pitting resistance of SAF2205 stainless steel was superior to that of AISI316L.The corrosion rate of AISI316L stainless steel rapidly decreased with increasing exposure time,while the corrosion rate of SAF2205 stainless steel slowly increased.The corrosion rate of AISI316L and SAF2205 stainless steels slightly changed after 72h.Cl- was more aggressive than Br- in 80% acetic acid solution at 80℃.Small amount of Br- had a remarkable inhibiting effect on corrosion behavior in acetic acid solution containing Cl-,whereas addition of small amount of Cl- to acetic acid solution containing Br- did not have significant harmful effects.

中图分类号 TG142.71

 
  中国光学期刊网论文下载说明


所属栏目

基金项目

收稿日期 2004/10/8

修改稿日期 2004/12/22

网络出版日期

作者单位点击查看

备注梁斌(1978-),男,河南鹿邑人,硕士研究生.

引用该论文: LIANG Bin,GONG Jian-ming,TU Shan-dong. Corrosion Behavior of AISI316L and SAF2205 Stainless Steels in Acetic Acid Solution Containing Br Ion[J]. Materials for mechancial engineering, 2006, 30(1): 56~59
梁斌,巩建鸣,涂善东. AISI316L和SAF2205不锈钢在含溴醋酸溶液中腐蚀行为的研究[J]. 机械工程材料, 2006, 30(1): 56~59


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】余存烨.PTA装置腐蚀与防护分析[J].化工设备与管道,2000,37(4):54-58.
 
【2】Sekine I,Masuko A,Senoo K.Corrosion behavior of AISI 316 stainless steel in formic and acetic acid solutions[J].Corrosion,1987,43(9):553-560.
 
【3】Katsumi Yamamoto,Keizo Hosoya.Corrosivity of Br- and Cl- on duplex stainless steel[J].Materials Science and Engineering,1995,A198(1-2):239-243.
 
【4】Suter T,Bohni H.New microelectrochemical method to study pit initiation on stainless steels[J].Electrochimica Acta,1997,42(20-22):3275-3280.
 
【5】张庭凯,杨长强.不锈钢[M].北京:原子能出版社,1995.330.
 
【6】Bogaerts W,Van Haute A,Brabers M J.Localized corrosion[M].Houston:NACE,1981.31.
 
【7】Alan Turnbull,Mary Ryan,Anthony Willetts,et al.Corrosion and electrochemical behaviour of 316L stainless steel in acetic acid solutions[J].Corrosion Science,2003,45(5):1051-1072.
 
【8】Guo R,Ives M B.Pitting susceptibility of stainless steels in bromide solutions at elevated temperatures[J].Corrosion,1990,46(2):125-129.
 
【9】Ratzer-Scheibe H J,Teller H G.Der einflu β der spezifischen adsorption von halogenidionen auf das elektrochemische verhalten der nickel-elektrode[J].Corrosion Science,1973,13(1):11-15.
 
相关信息
   标题 相关频次
 冷加工变形对1Cr18Ni9Ti不锈钢在含溴醋酸溶液中耐腐蚀性能的影响
 11
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 6
 醋酸回收罐进口管泄漏原因
 6
 316L不锈钢在有机胺脱硫溶液中的耐蚀性
 4
 445铁素体不锈钢内胆水箱的加工性能和耐蚀性
 4
 AISI304不锈钢钝化膜在电解质溶液中腐蚀时的半导体性质
 4
 CdSe-TiO2复合材料对304不锈钢的光生阴极保护性能
 4
 Cl-,CO2和微量H2S共存时13Cr不锈钢的腐蚀性能
 4
 不锈钢中铬在氢和氯离子作用下的腐蚀反应机理
 4
 草甘膦生产用不锈钢反应釜腐蚀的显微分析
 4
 超临界CO2条件下钢的腐蚀行为研究进展
 4
 醋酸浓度和温度对超级13Cr不锈钢电化学腐蚀行为的影响
 4
 锅炉水冷壁下联箱定排管泄漏的原因
 4
 幕墙不锈钢挂件的腐蚀问题
 4
 纳米化304不锈钢在硫酸溶液中的腐蚀行为
 4
 浓度和温度对316L不锈钢在NaOH溶液中应力强激光与粒子束腐蚀开裂行为的影响
 4
 氢对304L奥氏体不锈钢力学性能的影响
 4
 溴化锂机组不锈钢焊接管腐蚀失效的原因
 4
 烟草真空回潮机真空装置的腐蚀原因探讨及技术改进
 4
 组氨酸衍生物自组装膜的缓蚀性能
 4
 A3钢在乙酸中的腐蚀行为和机理
 3
 高温高压条件下13Cr钢的乙酸腐蚀
 3
 凝汽器不锈钢管锰致腐蚀初探
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 0Cr18Ni9/20G钢异质焊接接头的耐硫化氢应力腐蚀开裂性能
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2