阳极氧化对碳/环氧复合材料力学性能的影响
          
Effects of Anodic Oxidation of Carbon Fibers on Mechanical Properties of Carbon/Epoxy Composites

摘    要
利用真空浸渍法制得碳纤维增强环氧复合材料,研究了阳极氧化处理前后碳纤维表面状态的变化及表面处理对复合材料力学性能的影响.结果表明:适当的阳极氧化处理使复合材料的弯曲和剪切性能有很大改善,但冲击性能有所降低.
标    签 阳极氧化   碳纤维   环氧树脂   复合材料   anodic oxidation   carbon fiber   epoxy   composite  
 
Abstract
An epoxy-based composite reinforced with carbon fibers (C/EP) was prepared by vacuum impregnation process.The specific surface area and tensile fracture load of carbon fibers were determined after anodic oxidation treatment,and the effects of fibers surface treatment on mechanical properties of C/EP composites were also discussed.The anodic oxidation resulted in the reduction of fibers tensile strength,the larger the current density and the longer the oxidation time,the more the loss.The specific surface area of carbon fibers increased with the oxidation time when the current density was 2A/m2 and initially increased then decreases at 1A/m2.The flexural and shear properties of the C/EP composites with properly oxidized fibers were greatly improved,while the impact strength falled to some extent.Its believed that the interface adhesion of the C/EP composite could be enhanced by the anodic oxidation treatment of carbon fibers,but the oxidation time should not exceed 2 minute in order to obtain a better general mechanical performance.

中图分类号 TB332

 
  中国光学期刊网论文下载说明


所属栏目

基金项目

收稿日期 2004/9/17

修改稿日期 2005/3/1

网络出版日期

作者单位点击查看

备注王玉果(1975-),女,河北石家庄人,副教授,博士.

引用该论文: WANG Yu-guo,WANG Yu-lin,HU Feng-hua. Effects of Anodic Oxidation of Carbon Fibers on Mechanical Properties of Carbon/Epoxy Composites[J]. Materials for mechancial engineering, 2006, 30(1): 53~55
王玉果,王玉林,胡丰华. 阳极氧化对碳/环氧复合材料力学性能的影响[J]. 机械工程材料, 2006, 30(1): 53~55


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】宋焕成,赵时熙.聚合物基复合材料[M].北京:国防工业出版社,1986.
 
【2】Fukunaga A,Ueda S,Nagumo M.Air-oxidation and anodization of pitch-based carbon fibers[J].Carbon,1999,37(7):1081-1085.
 
【3】Fukunaga A,Ueda S,Nagumo M.Plasma treatment of pitch-based ultra high modulus carbon fibers[J].Carbon,1999,37(7):1087-1091.
 
【4】Yue Z R,Jiang W,Wang L,et al.Surface characterization of electrochemically oxidized carbon fibers[J].Carbon,1999,37(11):1785-1796.
 
【5】杨永岗,贺 福.XRD对表面处理碳纤维表面结构的分析[J].炭素,1998,(3):17-20.
 
相关信息
   标题 相关频次
 轻质复合材料获得航天航空认证
 3
 碳/玻璃混杂纤维增强环氧树脂复合材料线芯的性能
 3
 碳纤维增强树脂基复合材料的性能研究
 3
 碳纤维增强铜基复合材料的性能研究
 3
 提高硼纤维/环氧复合材料界面抗剪强度的方法
 3
 苎麻增强环氧树脂复合材料的力学性能
 3
 3D打印碳纤维复合材料的下一个目标:飞机高性能结构件
 2
 9S75铝合金的电化学腐蚀行为及阳极氧化工艺
 2
 C/SiC复合材料拉伸过程的声发射研究
 2
 Ca-α/β-Sialon结合刚玉复合材料的力学性能
 2
 CIKONI最先成功设计碳纤维复合材料结构
 2
 MGF/PLA复合材料的制备及性能
 2
 MoS2、CdO及聚全氟乙丙烯填充改性聚四氟乙烯
 2
 PP-g-MAH改性SGF+POE/FPP复合材料的制备及性能
 2
 Si3N4p-SiCw/MoSi2复合材料的强韧化效果与机制
 2
 SiCf/Ti-6Al-4V复合材料的界面反应及其影响
 2
 SiCP/6061Al复合材料高温单轴拉伸时相关棘轮行为的细观本构模型
 2
 SiC颗粒增强铝基复合材料的摩擦磨损性能
 2
 T300/648复合材料的湿热老化行为
 2
 T700和T300碳纤维增强环氧树脂基复合材料耐湿热老化性能的对比
 2
 TiB2/Al复合材料喷丸后微区残余应力的有限元模拟
 2
 TiO2纳米管阵列薄膜的水热晶化
 2
 YANG XiaoLin,LV BoPing,XIAN MingLe
 2
 ZrO2与HA复合粉体的烧结行为
 2
 阿波罗-2:采用碳纤维复合材料打造的私人飞机
 2
 包覆镍CNTs/AM60复合材料铸态显微组织与力学性能
 2
 包覆镍的碳纳米管增强AZ91镁基复合材料的显微组织与力学性能
 2
 表面处理方法对剑麻纤维/酚醛树脂复合材料性能的影响
 2
 波音737飞机发动机反推装置内侧壁板复合材料的无损检测
 2
 玻璃纤维增强环氧树脂基复合材料在温湿和紫外辐照环境中的老化行为
 2