CeO2-MnO2 nano-oxide/graphene composite electrode materials were prepared by hydrothermal method. The morphology, crystal structure of composite electrode materials and functional group on the surface graphene were investigated by SEM, TEM, XRD and Raman microscopy. And the electrochemical performance of the composite electrode materials was also studied using constant current charging-discharging and cyclic voltammetry (CV). The results indicate that the addition of CeO2 could improve cycle number on electrode cycles. When the mole ratio of cerium to manganese was 2∶8, the best specific capacitance with maximum value of 157 F·g-1 under the scanning speed of 10 mV·s–1 in 1 mol·L-1 Na2SO4 electrolyte, and capacitance loss of 23% after 1 000 cycles of charging and discharging were achieved.
引用该论文:XU Zheng,CHEN Zhi-gang,QIAN Jun-chao,LIU Cheng-bao,ZHANG Yu-zhu. Preparation of CeO2-MnO2 Nano-Oxide/Graphene Composite Electrode Materials and Their Performance of Supercapacitor[J]. Materials for mechancial engineering, 2015, 39(8): 70～74 徐政,陈志刚,钱君超,刘成宝,张玉珠. CeO2-MnO2纳米氧化物/石墨烯复合电极材料的制备及其超级电容性能[J]. 机械工程材料, 2015, 39(8): 70～74
【1】WANG Guo-ping, ZHANG Lei, ZHANG Jie. A review of electrode materials for electrochemical supercapacitors［J］. Chem Soc Rev, 2012, 41(2): 797-828.
【2】CAO Ze-yuan, WEI Bing-qing. A perspective: carbon nanotube macro-films for energy storage［J］. Energy Environ Sci, 2013,6: 3183-3201.
【3】LIU Wen-wen, YAN Xing-bin, LANG Jun-wei, et al. Flexible and conductive nanocomposite electrode based on graphene sheets and cotton cloth for supercapacitor［J］. J Mater Chem, 2012, 22(33): 17245-17253.
【4】WANG Yan, SHI Zhi-qiang, HUANG Yi, et al. Supercapacitor devices based on graphene materials［J］. J Phys Chem C, 2009, 113(30): 13103-13107.
【5】STOLLER M D, PARK S, ZHU Yan-wu, et al. Graphene-based ultracapacitors［J］. Nano Lett, 2008, 8(10): 3498-3502.
【6】ZHAO Dan, GUO Xin-ying, GAO Yue, et al. An electrochemical capacitor electrode based on porous carbon spheres hybrided with polyaniline and nanoscale ruthenium Oxide［J］. ACS Appl Mater Interfaces, 2012, 4(10): 5583-5589.
【7】GAO Zan, YANG Wan-lu, WANG Jun, et al. A new partially reduced graphene oxide nanosheet/polyaniline nanowafer hybrid as supercapacitor electrode material［J］. Energy Fuels, 2012, 27(1): 568-575.
【8】LEE M T, FAN Chen-yen, WANG Yi-chen, et al. Improved supercapacitor performance of MnO2-graphene composites constructed using a supercritical fluid and wrapped with an ionic liquid［J］. J Mater Chem: A, 2013, 1(10): 3395-3405.
【9】HUANG Hua-jie, WANG Xin. Graphene nanoplate-MnO2 composites for supercapacitors: a controllable oxidation approach［J］. Nanoscale, 2011, 3(8): 3185-3191.
【10】WU Zhong-shuai, REN Wen-cai, WANG Da-wei, et al. High-energy MnO2 nanowire/graphene and graphene asymmetric electrochemical capacitors［J］. ACS Nano, 2010, 4(10): 5835-5842.
【11】DENG Ling-juan, ZHU Gang, WANG Jian-fang, et al. Graphene-MnO2 and graphene asymmetrical electrochemical capacitor with a high energy density in aqueous electrolyte［J］. Journal of Power Sources, 2011, 196(24): 10782-10787.
【12】ZHAI Teng, WANG Fu-xin, YU Ming-hao, et al. 3D MnO2-graphene composites with large areal capacitance for high-performance asymmetric supercapacitors［J］. Nanoscale, 2013, 5(15): 6790-6796.
【13】LEE H, KANG J, CHO M S, et al. MnO2/graphene composite electrodes for supercapacitors: the effect of graphene intercalation on capacitance［J］. J Mater Chem, 2011, 21(45): 18215-18219.
【14】HUANG Yu, LI Yuan-yuan, HU Zuo-qi, et al. A carbon modified MnO2 nanosheet array as a stable high-capacitance supercapacitor electrode［J］. J Mater Chem: A, 2013, 1(34): 9809-9813.
【15】XIE Xiao-ying, ZANG Chen, WU Ming-bo, et al. Porous MnO2 for use in a high performance supercapacitor: replication of a 3D graphene network as a reactive template［J］. Chem Commun, 2013, 49(94): 11092-11094.