13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
          
Corrosion Behavior of 13Cr Stainless Steel and Nickel-base Alloy Tubes Caused by Surface Scratch Damage

摘    要
以B13Cr110不锈钢和Ni基合金G3油管为对象,分别用45#钢和黄铜在试样表面制造划伤,采用盐雾试验和电化学试验方法研究了划伤后B13Cr110油管的腐蚀行为与机理.结果表明,13Cr不锈钢和镍基合金钢管被45#钢划伤后划痕处出现明显锈蚀,原因是划伤时残留在不锈钢表面的45#钢在腐蚀环境中发生腐蚀并对不锈钢造成污染;而被黄铜划伤时虽然也发生铜残留,但黄铜具有较好的耐蚀性,不发生明显腐蚀.
标    签 13Cr不锈钢   镍基合金   油管   划伤   腐蚀   13Cr stainless steel   nickel-base alloy   oil tube   scratch damage   corrosion  
 
Abstract
The corrosion behavior and mechanism of 13Cr stainless steel and nickel-base alloy tubes caused by surface scratch damage were studied by using salt spray testing and electrochemical testing.The results showed that different corrosion behaviors appeared after 13Cr stainless steel and nickel-base alloy scratched by copper or 45# steel.The corrosion pouduct of 45# steel retained on the surface was the main reason of the corrosion of 13Cr stainless steel and nickel-base alloy.

中图分类号 TG172.2

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2009/11/18

修改稿日期

网络出版日期

作者单位点击查看


引用该论文: ZHOU Qing-jun,QI Hui-bin,QIAN Yu-hai,WANG Wei. Corrosion Behavior of 13Cr Stainless Steel and Nickel-base Alloy Tubes Caused by Surface Scratch Damage[J]. Corrosion & Protection, 2010, 31(9): 694~695


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】周波,崔润炯,刘建中.增强型13Cr钢抗CO2腐蚀套管的研制[J].钢管,2006,35(6):22-26.
 
【2】廖建国.耐蚀性好的油井用高强度高Cr钢管[J].焊管,2006,29(5):83-88.
 
【3】吕祥鸿,赵国仙,杨延清,等.13Cr钢高温高压CO2腐蚀电化学特性研究[J].材料工程,2004,10:16-20.
 
【4】International Standard ISO 13680:2000,Petroleum and natural gas industries corrosion resistant alloy seamless tubes for use as casing,tubing and coupling stock-Technical delivery conditions[S].
 
【5】Kimura Mitsuo,Tamari Takanori,Shimamoto Ken.High Cr stainless steel OCTG with high strength and superior corrosion resistance[C]//Jfe Technical Report,2006:7-9.
 
【6】王保峰,卢建树,张九渊,等.不锈钢及镍基合金在高温水中的腐蚀研究[J].腐蚀与防护,2001,22(5):187-190.
 
【7】罗正贵,闻荻江.铜的腐蚀及防护研究进展[J].武汉化工学院学报,2005,27(2):17-21.
 
相关信息
   标题 相关频次
 SS400热轧碳钢氧化皮的结构改变与保护性
 6
 汽车热轧钢板的锈蚀行为及预防措施
 6
 某天然气井13Cr油管腐蚀原因
 5
 GL-A32和B610E板坯再热温度下的氧化行为
 4
 井下油井单根连接刺漏失效分析
 4
 水淬高强钢板酸洗行为与缓蚀剂效果评价
 4
 塔里木油田某井酸化管柱腐蚀的原因
 4
 超临界水氧化环境下合金腐蚀研究进展
 3
 川东北高含硫天然气对管道的腐蚀
 3
 单氟磷酸钠在混凝土模拟孔隙液中的缓蚀特性
 3
 高压气井不锈钢油管特殊螺纹接头工厂端泄漏和腐蚀原因分析
 3
 炼油厂埋地水管网的腐蚀与阴极保护
 3
 某井S13Cr特殊螺纹接头油管柱腐蚀原因
 3
 某井修井遇阻及油管和套管失效原因分析
 3
 酸性气田井下油管腐蚀失效原因
 3
 钨镍合金镀层油管适用性
 3
 牙哈301井油管腐蚀原因分析
 3
 雅克拉井下油管结垢腐蚀分析及防治措施
 3
 乙烯装置压缩系统腐蚀原因分析
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 2
 20G/316L双金属复合管失效的原因
 2
 20号钢在HCl-H2S-H2O溶液中的腐蚀行为
 2
 220kV钢芯铝绞线断股事故化学分析
 2
 2507双相不锈钢钾盐蒸发罐腐蚀的原因分析
 2