Ni-P化学镀层对NdFeB永磁材料耐腐蚀性的改善
          
Effect of Electroless Ni-P Plating on Corrosion Resistance of NdFeB Magnets

摘    要
测量了不同类型Ni-P化学镀试样和基体的孔隙率,以及在HCl、NaCl和NaOH溶液中的腐蚀速率,比较了不同类型Ni-P化学镀试样在3.5%NaCl 溶液中的极化曲线,对比分析了酸性和酸碱复合条件下所得Ni-P镀层的表面形貌.结果表明:化学镀Ni-P合金能显著改善NdFeB永磁体的耐腐蚀性和致密性,且以弱碱性化学镀为底层,酸性化学镀为表层的酸碱复合镀层的致密性和耐腐蚀性最佳,单一酸性镀层的耐腐蚀性又优于碱性镀层.
标    签 Ni-P镀层   稀土   NdFeB永磁体   耐腐蚀性   孔隙率   Ni-P plating   rare earth   NdFeB permanent magnet   corrosion resistance   porosity  
 
Abstract
The porosity of different types of Ni-P deposits and substrate were measured and the corrosion rates were studied in 3.5% NaCl,10% HCl and 20% NaOH solutions.The corrosion characteristics of different types of Ni-P deposites in 3.5% NaCl solution were envaluated by electrochemical potentiodynamic polarization curves.The microstructure of electroless Ni-P deposits in acidic and acidic-alkaline compositing baths were compared.The results showed that all the types of deposits could enhance the densification and corrosion resistance of substrate.The acidic-alkaline composite deposits composed of alkaline Ni-P plating as bottom film and acidic Ni-P plating as top film could provide the best protection,and the corrosion resistance of single acidic Ni-P deposit was better than that of single alkaline Ni-P deposit.

中图分类号 TG174.4

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 安徽省教育厅自然科学基金(kJ2009B050)

收稿日期 2008/11/11

修改稿日期 2009/2/10

网络出版日期

作者单位点击查看


备注冒爱琴,讲师.

引用该论文: MAO Ai-qin,SHA Fei. Effect of Electroless Ni-P Plating on Corrosion Resistance of NdFeB Magnets[J]. Corrosion & Protection, 2009, 30(12): 896~898


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】周寿增.稀土永磁材料及其应用[J].北京:冶金工业出版社,1990:351.
 
【2】Gurrappa I,Pandian S.Corrosion characteristics of Nd-Fe-B permanent magnets in different environments[J].Corrosion Engineering,Science & Technology,2006,41(1):57-61.
 
【3】Yu L Q,Wen Y H,Yan M.Effects of Dy and Nb on the magnetic properties and corrosion resistance of sintered NdFeB[J].Journal of Magnetism& Magnetic Materials,2004,283 (2/3):353-356.
 
【4】Li Y,Evans H E,Harris I R,et al.The oxidation of NdFeB magnets[J].Oxid.Mel.,2003,59:167-182.
 
【5】El-Moneim A A,Gebert A,Uhlemann M,et al.The influence of Co and Ga additions on the corrosion behavior of nanocrystalline NdFeB magnets[J].Corrosion Science,2002,44(8):1857-1875.
 
【6】Ma C B,Cao F H,Zhang Z,et al.Electrodeposition of amorphous Ni-P coatings onto Nd-Fe-B permanent magnet substrates[J].Applied Surface Science,2006,253(4):2251-2256.
 
【7】Yu Shengxue,Chen Ling.Preparation technology and performances of Zn-Cr coating on sintered NdFeB permanent magnet[J].Journal of Rare Earths,2006,24(2): 223-226.
 
【8】Shan Guan,Bradley J Nelson.Fabrication of hard magnetic microarrays by electroless codeposition for MEMS actuators[J].Sensors and Actuators A: Physical,2005,118(2):307-312.
 
【9】Rada M,Kardelky S,Mazilu I,et al.Corrosion behavior of polymer-bonded NdFeB-based nanocrystalline magnets[J].IEEE Transactions on Magnetics,2004,40(4):2864-2866.
 
【10】张天顺,张兆国,张晶秋,等.TL-5化学镀Ni-P合金在NdFeB永磁体上的工艺研究[J].腐蚀与防护,2002,23(4):152-154.
 
【11】吴磊,严密,应华根,等.NdFeB磁体表面化学镀Ni-P合金防腐研究[J].稀有金属材料与工程,2007,36(8):1398-1402.
 
相关信息
   标题 相关频次
 AZ91D镁合金Ni-P/CeO2化学复合镀层的耐蚀性
 3
 三种镍基合金化学镀镀层的耐蚀性能
 3
 稀土对泡沫铝及泡沫铝合金耐腐蚀性能的影响
 3
 稀土铈对热浸镀铝层组织和性能的影响
 3
 17-4PH不锈钢表面TiO2膜及其多层膜的结构与性能
 2
 5A06/T2异种材料搅拌摩擦焊接头的耐蚀性
 2
 AlCl3-NaCl熔盐扩散增强纯镁耐腐蚀性的研究
 2
 AZ31镁合金双稀土转化膜的TiO2溶胶处理
 2
 C/C复合材料显微电子计算机断层扫描成像特征
 2
 Cu-15Ni-8Sn合金在海水中的耐腐蚀性研究
 2
 Fe3Al金属间化合物多孔材料的孔隙特征
 2
 H13钢离子氮化前后表面沉积CrAlN薄膜的耐氯离子腐蚀性能
 2
 Magnaplate“协和”涂层及其在镁合金上的应用
 2
 MB2镁合金SiO2基陶瓷涂层的性能
 2
 Mg-5Zn-xEr-1.5Nd-0.5Zr(1.1
 2
 Monel合金粒子注入对MoS2固体润滑膜形貌及性能的影响
 2
 Nd对Zr基非晶合金形成能力、热稳定性及耐腐蚀性的影响
 2
 SiC颗粒增强铝基复合材料中增强体含量的超声检测
 2
 TiN和TiCrN膜层对氢燃料电池双极板材料316L不锈钢性能的影响
 2
 WE43镁合金表面电沉积羟基磷酸钙膜层在模拟体液中的耐腐蚀性
 2
 闭孔泡沫纯铝的导热性能
 2
 表面转化膜无铬化技术的研究动向
 2
 冰模板法制备仿生双孔径-定向孔隙毛细芯的结构和性能
 2
 不同孔隙率碳纤维增强环氧树脂复合材料板的压缩强度及其预测模型
 2
 采用新型硬脂酸造孔剂烧结制备多孔NiTi合金的结构及性能
 2
 超声功率谱特征参数在复合材料孔隙率检测中的应用
 2
 超音速火焰喷涂WC-CoCr涂层的腐蚀行为
 2
 超音速火焰喷涂制备WC-10Co-4Cr涂层工艺参数的优化
 2
 超音速火焰喷涂制备WC-Cr3C2-Ni涂层工艺参数的优化
 2
 船用5A01铝合金厚板的耐腐蚀性能
 2