A3钢在海泥中的腐蚀行为
          
Corrosion Behavior of A3 Steel in Sea Mud

摘    要
对A3钢在模拟海泥环境中进行了埋片试验和电化学试验,以研究海底管道在含硫酸盐还原菌(SRB)海泥中的腐蚀行为.结果表明,A3钢在砂泥中的腐蚀速率明显高于在海砂中的腐蚀速率,随温度的升高,A3钢在海砂中的腐蚀速率升高;且随温度的升高、SRB和SO2-4含量的增加,A3钢在砂泥中的腐蚀速率随之升高;在无菌海泥中A3钢的腐蚀速率随温度升高而增大,主要是由于作为阴极去极化剂的氧的扩散速度随温度升高而增大;在有菌海泥中SO2-4能参与阴极去极化而加速A3钢的腐蚀.
标    签 A3钢   海泥   SRB   腐蚀   A3 steel   sea mud   SRB   corrosion  
 
Abstract
The corrosion rate of seabed pipeline in sea mud was studied by weight-loss experiments and electrochemical measurements with A3 steel in simulated sea mud.The results showed that the corrosion rate of A3 steel in sandy soil was significantly higher than that in sea sand.The corrosion rate of A3 steel in sea sand increased with the increase of temperature.With the increase of SRB and SO2-4,the corrosion rate of A3 steel increased in sandy soil.The increase of corrosion rate of A3 steel in marine mud without SRB with the increase of temperature was mainly due to the increase of diffusion rate of oxygen as a depolarizing agent of cathode.SO2-4 could participate in the cathodic depolarization and accelerate the corrosion rate of A3 steel in sea mud with SRB.

中图分类号 TG172

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2008/1/6

修改稿日期 2008/4/22

网络出版日期

作者单位点击查看

引用该论文: WEI Ai-jun,HUO Fu-yong,XIONG Xiang-jun,JIANG Hua-yi,YANG Hai-long. Corrosion Behavior of A3 Steel in Sea Mud[J]. Corrosion & Protection, 2009, 30(2): 99~101


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】马士德,侯保荣.海底沉积物腐蚀的基本观点[C]//中国腐蚀与防护学会.中国腐蚀与防护学会建会十五周年学术年会论文集.北京:化学工业出版社,1994:111-112.
 
【2】Ma Shide,Huang Yanliang.Effects of anaerobe in sea bottom sediment on the corrosion of carbon steel[J].Oceanologia et Linnologia Sinica,1998,16(3):253-257.
 
【3】Tributsch H,Rojas-Chapana J A.Role of transient iron sulfide films in microbial corrosion of steel[J].Corrosion,1998,54(3):216-227.
 
【4】Jack T R,Wilmott M.Corrosion consequences of secondary oxidation of aricrobial corrosion[J].Corrosion,1998,54(3):246-252.
 
【5】Dean Jizhou,Hou Baorong,Li Yan,et al.Corrosion of steel in sea mud containing active sulfate-reducing bateria[R].Osaka:Osaka University,2003.
 
【6】Jia Wang.Electrochemical study on corrosion behaviour of steels in sand with water[J].Chinese Journal of Oceanlogy and Limnology,1997.
 
【7】马士德,朱素兰,孙家瑞.海底泥温度对API 5L X60管线钢腐蚀影响研究[J].海洋科学,1995,12(4):20-22.
 
【8】张经磊,侯保荣.海泥中SRB对A3钢电偶效应的影响[J].海洋与湖沼,2000,31(4):448-452.
 
【9】魏 华,高荣杰,王秀通,等.管线钢在海泥中的腐蚀行为[D].青岛:中国海洋大学.2005.
 
相关信息
   标题 相关频次
 温度对A3钢在海水中电化学腐蚀的影响
 7
 X80钢的CO2腐蚀电化学行为与机理研究
 6
 CO2对碳钢腐蚀影响的模拟试验及缓蚀剂评价
 4
 CO2驱油地面集输管道的腐蚀电化学行为
 4
 不同温度下X80钢的CO2腐蚀电化学特性
 4
 油田产出水中饱和CO2和SRB共存条件下十二胺缓蚀剂的缓蚀行为
 4
 俄罗斯西伯利亚南部原油中的细菌及其腐蚀性
 3
 胜利油田孤六联合站污水腐蚀与防护措施
 3
 杏南地区集输管线腐蚀原因初步分析
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 2
 20G/316L双金属复合管失效的原因
 2
 20号钢在HCl-H2S-H2O溶液中的腐蚀行为
 2
 220kV钢芯铝绞线断股事故化学分析
 2
 2507双相不锈钢钾盐蒸发罐腐蚀的原因分析
 2
 2A12铝合金当量加速腐蚀试验
 2
 2-甲基咪唑啉及其复配缓蚀剂在高硬度电解质水溶液中的缓蚀性能
 2
 304H弹簧钢丝及弹簧表面腐蚀的原因
 2
 304L不锈钢焊接接头表面状态对其在硼酸溶液中腐蚀行为的影响
 2
 304不锈钢在高温环烷酸介质中的腐蚀行为
 2
 30CrMnSiA合金钢当量加速腐蚀试验
 2
 316L不锈钢在熔融LiCl-3%Li2O中的腐蚀行为
 2
 316L不锈钢在有机胺脱硫溶液中的耐蚀性
 2
 445铁素体不锈钢内胆水箱的加工性能和耐蚀性
 2