马来酸酐等离子体改性聚丙烯薄膜表面的强激光与粒子束硫酸腐蚀行为
          
Corrosion Characters in Sulfuric Acid of Polypropylene Films Modified by Maleic Anhydride Plasma

摘    要
以马来酸酐的等离子体聚合方法对聚丙烯薄膜表面进行了亲水改性,用FT-IR、接触角等分析手段研究了等离子体处理功率对改性薄膜表面的化学结构和亲水性能的影响以及薄膜表面的马来酸酐等离子体聚合物在高温强酸环境中的腐蚀行为.结果表明,马来酸酐等离子体聚合物可水解为聚马来酸结构,改性薄膜表面接触角达到43°~50°,接触角随处理功率的提高呈上升趋势.50W的马来酸酐聚合物的耐110 ℃、40%硫酸腐蚀性优于30W的马来酸酐聚合物;在高温硫酸介质的腐蚀环境下,马来酸酐的等离子体聚合物可通过磺化反应而引入亲水的磺酸基团,腐蚀后改性薄膜的表面接触角进一步降低至30 °以下,获得了更佳的表面亲水性.
标    签 等离子体聚合   聚丙烯   马来酸酐   亲水性   硫酸腐蚀   plasma polymerization   polypropylene   maleic anhydride   hydrophilicity   sulfuric acid corrosion  
 
Abstract
Polypropylene film surfaces were modified by plasma polymerization method of maleic anhydride to improve the surface hydrophilicity.The effects of the plasma power on the surface chemistry and the surface hydrophilicity were investigated by the FT-IR and contact angle methods.The corrosion characters of poly(maleic anhydride) on modified film surfaces in sulfuric acid medium were evaluated.The surface contact angle values of the modified films were decreased to 43°~50° and increased with the increase of plasma power.The corrosion resistance properties of poly(maleic anhydride) of 50W were better than those of 30W in 40% sulfuric acid solution at 110 ℃.The sulfonic groups could be introduced to plasma polymer in sulfric acid solution at higt temperature,the contact angles of modified films were decreased to lower than 30°.

中图分类号 TG174.46

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 国家973计划资助项目(2003CB615701);国家自然科学基金资助项目(20476045)

收稿日期 2007/12/26

修改稿日期 2008/2/27

网络出版日期

作者单位点击查看

引用该论文: WU Miao,WEI Wu-ji,HUANG Jian. Corrosion Characters in Sulfuric Acid of Polypropylene Films Modified by Maleic Anhydride Plasma[J]. Corrosion & Protection, 2009, 30(1): 25~28


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】黄建中,左 禹.材料的耐蚀性和腐蚀数据[M].北京:化学工业出版社,2003:440-441.
 
【2】陈杰瑢.低温等离子体化学及其应用[M].北京:科学出版社,2001:116-131.
 
【3】Tibbitt M,Shen M,Bell A T.Structural characterization of plasma-polymerized hydrocarbons[J].Journal of Macromolecular Science Part A,1976,10(8):1623-1648.
 
【4】Ryan M E,Hynes A M,Badyal J P S.Pulsed plasma polymerization of maleic anhydride[J].Chem Mater,1996,8(1):37-42.
 
【5】Yasuda H.Plasma Polymerization[M].Orlando:Academic Press,1985:79-82.
 
【6】Huang J,Wang X L,Chen X Z,et al.Temperature-sensitive membranes prepared by plasma-induced graft polymerization of N-isopropylacrylamide into porous polyethylene membranes[J].Journal of Applied Polymer Science,2003,89(12):3180-3187.
 
【7】Gaboury S R,Urban M W.Microwave plasma reactions of solid monomers with silicone elastomer surfaces:a spectroscopic study[J].Langmuir,1993,9(11):3225-3233.
 
【8】卢涌泉,邓振桦.实用红外光谱解析[M].北京:电子工业出版社,1989:203-207.
 
【9】Mirabedini S M,Arabi H,Salem A,et al.Effect of low-pressure O2 and Ar plasma treatments on the wettability and morphology of biaxial-oriented polypropylene(BOPP) film[J].Progress in Organic Coatings,2007,60(2):105-111.
 
【10】邢其毅.基础有机化学,第二版[M].北京:高等教育出版社,1993:544-551.
 
【11】王载紘,张余善,王闻多.阴离子表面活性剂[M].北京:中国轻工业出版社,1983:131-132.
 
相关信息
   标题 相关频次
 316L不锈钢纤维在硫酸中的腐蚀行为
 2
 PP-g-MAH改性SGF+POE/FPP复合材料的制备及性能
 2
 Q235钢在采出液中表面产物膜的结构及其对腐蚀的影响
 2
 表面处理对剑麻纤维增强聚丙烯复合材料力学性能的影响
 2
 草甘膦生产用不锈钢反应釜腐蚀的显微分析
 2
 二维红外光谱法分析聚丙烯C-H伸缩振动
 2
 粉煤灰/聚丙烯复合材料的非等温结晶动力学行为
 2
 封闭式大储量圆形煤场储煤自燃分析及处理
 2
 高频炉直接燃烧-红外光谱法测定铁矿石中硫的应用
 2
 高效液相色谱-串联质谱法测定尿液中丙烯醛的代谢产物
 2
 磺酸甲胺基聚环氧琥珀酸的合成及缓蚀性能
 2
 聚丙烯/有机蒙脱土纳米复合材料的电子束辐照改性
 2
 聚丙烯溶液比浓黏度测定的影响因素
 2
 聚丙烯悬臂梁冲击强度测试的不确定度评定
 2
 麦秸纤维/聚丙烯复合材料的制备与力学性能
 2
 煤矸石/聚丙烯复合材料的非等温结晶动力学
 2
 纳米二氧化钛增强聚丙烯复合泡沫材料的性能
 2
 声发射检测的一次升压信号分析
 2
 石化装置保温材料的腐蚀性
 2
 土工格栅用聚丙烯原料的高温拉伸特性
 2
 锡掺杂量对In2O3粉体光学性能和形貌的影响
 2
 新型纳米金直接修饰玻碳电极的制备及其电催化活性
 2
 一种新型钢筋阻锈剂的阻锈性能
 2
 中空玻璃微珠改性PP泡沫复合材料的发泡效果和力学性能
 2
 #高分子周报#北美树脂生产商的新年愿望
 1
 #高分子周报#替代传统聚氨酯的可再生泡沫
 1
 2017年聚丙烯改性三大新方向!
 1
 3微米超薄型薄膜实现量产 打破国外垄断局面
 1
 CuO辅助Ag72Cu28共晶钎料在大气环境中实现Al2O3陶瓷钎焊的界面反应
 1
 R60702锆材CO2激光焊的气体保护及接头的组织、力学性能
 1