化工设备选用锆的基本考虑
          
Basic Consideration for Selected Use of Zirconium on Chemical Equipment

摘    要
化工设备设计只有在不锈钢与钛难以胜任时才考虑选用工业级锆.讨论了锆的耐蚀性与经济性,并分析了焊区晶间腐蚀、氢脆、点腐蚀与应力腐蚀破裂等及对应的防护方法.
标    签   化工设备   腐蚀   防护   zirconium   chemical equipment   corrosion   protection  
 
Abstract
Selected use of industrial grade zirconium for design of chemical equipment is considered only when stainless steels and titanium show difficult competence.The corrosion resistance and economial efficiency are discussed,Its intergranular corrosion,hydrogen embrittlement,pitting and stress corrosion cracking,and relevant protective methods are analyzed.

中图分类号 TG174.2

 
  中国光学期刊网论文下载说明


所属栏目 专论

基金项目

收稿日期 2008/2/21

修改稿日期

网络出版日期

作者单位点击查看

引用该论文: YU Cun-ye. Basic Consideration for Selected Use of Zirconium on Chemical Equipment[J]. Corrosion & Protection, 2008, 29(11): 650~653


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】铃木一彳韦亍,チタンとジルユニウムは腐食性环境で补完レ合ラ女市妹金属[J].チタン,2000,48(3).
 
【2】Kleefisch E W editor.Industial application of titanium and zirconium[C]//ASTM STP728,1981.
 
【3】Boyd W K.Application of titanium.Zirconium,tantalum and niobium in chemical enviroments[C]//Process Industries Corrosion,NACE,1975.
 
【4】佐藤广厶士.チタン、ジルユニウム、タンタルの耐蚀特性と适正使用[J].クミカル ユンジニヤリング,1994(2).
 
【5】高村昭.新金属材料の耐食性[J].防食技术,1967,16(3).
 
【6】R terremce.Applications of zirconium in chemical equipment[J].Metal Progrese,1978,113(2).
 
【7】Barley R W,Walton G N.Corrosion and hydrogenation of zirconium and zirconium alloys[J].Corrosion Prevention & Control,1977,24(5).
 
【8】Abo M F,Rabbok,Booder P J.Passive destruction of titanium zirconium tantalum in halide mediums[C]//Localized Corrosion(会议集),653-660.
 
【9】Palit G C,Elayaperumal K.Passivation and pitting of corrosion resistance pure metals Ta,Ti,Zr,Cr and Al in chloride solution[J].Corrosion Science,1978,18(2).
 
【10】Ddle A Vaughan,Earl L white.Corrosion absorb hydrogen of zirconium alloys in hydrous enviroment[J].Corrosion,1963,17(3).
 
【11】Edward Hillner.Corrosion of zirconium baes alloys——Review zircobium in the nuclear industry[C]//ASTM STP633,1977,221-235.
 
【12】Nadia El-Massry,S M Bedair,F H Hammad.Protective property of zirconium anodizing film,zirconium in the nuclear industry[C]//ASTM STP633,1977,643-649.
 
【13】Avoid occurs hydrogen embrittlement in zirconium[P].英国专利No.1375705,1974.
 
【14】Kenji Mori,Akira Takamura,Takaakl Shimose.Stress corrosion cracking of Ti and Zr in HCl-CH3OH solution[J].corrosion,1966,22(2).
 
【15】濑川重忠,森宪二,高村昭,等.在HCl-甲醇溶液中TiとZr的应力腐蚀破裂[J].防食技术,1964,13(5).
 
【16】袁改焕,白新德,刘振球.我国锆铪材加工技术的进步与发展[J].稀有金属快报,2004,23(10).
 
相关信息
   标题 相关频次
 锆与钛耐蚀性比较及应用互补性
 6
 石化钛设备腐蚀实例
 6
 PTA装置碱洗对设备腐蚀开裂影响讨论
 4
 超临界火电厂海水循环水泵的防腐蚀方案
 4
 芳烃抽提装置中碳钢设备腐蚀原因分析与措施
 4
 腐蚀与防护专家系统简介
 4
 高含硫气田A333管材腐蚀情况及防护措施
 4
 海洋飞溅区钢结构的腐蚀规律与防护措施
 4
 海洋浪溅区钢铁腐蚀与防护进展
 4
 海洋石油平台外加电流阴极保护延寿修复技术
 4
 户内燃气立管的腐蚀与防护
 4
 火力发电厂空冷凝汽器的腐蚀与防护
 4
 加氢装置设备腐蚀分析与安全防护
 4
 埋地重要管线的腐蚀与防护
 4
 胜利油田孤六联合站污水腐蚀与防护措施
 4
 胜利油田立式常压储罐的腐蚀分析及检测技术
 4
 石油生产中腐蚀的原因及缓蚀剂的应用
 4
 顺丁溶剂油回收系统的腐蚀与防护
 4
 钛铜共用海水冷却器的牺牲阳极保护
 4
 西宁火车站下穿隧道钢筋混凝土结构的腐蚀与防护
 4
 亚稳定奥氏体不锈钢马氏体促发脆裂分析
 4
 重有色金属冶炼中混凝土槽罐的腐蚀与防护
 4
 注氮气井井下设备腐蚀原因分析及相应对策
 4
 悬索桥主缆的腐蚀与防护
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2