海洋飞溅区钢结构的腐蚀规律与防护措施
          
Corrosion and Protection of Offshore Steel Structures in Splash Zone

摘    要
飞溅区是钢结构在海洋环境中腐蚀最严重和防腐蚀保护措施最容易失效的部位.文章综述了海上钢结构在飞溅区的腐蚀规律和防腐蚀保护方法,并针对飞溅区的腐蚀特点提出了改进措施.
标    签 飞溅区   腐蚀   防护   海洋钢结构   splash zone   corrosion   protection   offshore steel structure  
 
Abstract
The most severe corrosion of offshore steel Structures occurs in the splash zone,where anticorrosive measures are most easily failed.The corrosion rules and anticorrosive measures of offshore steel Structures in the splash zone are summarized,and the improved anticorrosive methods are presented based on the corrosion characteristics in the splash zone.

中图分类号 TG172.5

 
  中国光学期刊网论文下载说明


所属栏目 专论

基金项目 国家863计划海洋领域重大项目“南海深水油气勘探开发关键技术及装备”(2006AA09A104)

收稿日期 2007/10/15

修改稿日期 2007/11/28

网络出版日期

作者单位点击查看

引用该论文: SHAO Huai-qi,HAN Wen-li,WANG Xue-ying,Li Ai-gui. Corrosion and Protection of Offshore Steel Structures in Splash Zone[J]. Corrosion & Protection, 2008, 29(11): 646~649


被引情况:


【1】刘建国,李言涛,侯保荣, "海洋浪溅区钢铁腐蚀与防护进展",腐蚀与防护 33, 833-836(2012)

【2】刘建国,李言涛,侯保荣, "N80钢模拟全浸区和干湿交替试样的腐蚀行为",腐蚀与防护 33, 925-927(2012)

【3】李琳,徐小连,艾芳芳,高鹏,陈义庆,钟彬,肖宇, "工艺和组织对桥梁钢在模拟海洋飞溅区环境中腐蚀行为的影响",腐蚀与防护 34, 503-506(2013)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】黄桂桥,郁纯娟.金属材料在海洋飞溅区的腐蚀[J].材料保护,1999,32(2):28-30.
 
【2】侯保荣.海洋环境下钢结构物浪花飞溅区的腐蚀灾害[J].科学中国人,2006,(11):21-22.
 
【3】李言涛,李延旭,侯保荣,等.低合金钢在海洋各腐蚀区带的锈层研究[J].海洋与湖泊,1998,29(6):651-655.
 
【4】侯保荣,西方笃,水流彻.钢材在海水-海气交换界面区的腐蚀行为[J].海洋与湖沼,1995,26(5):514-519.
 
【5】卡尔坡 菲希.热喷涂铝涂层在石油平台上应用[J].中国海洋平台,1996,11(2):68-73.
 
【6】D K-K Tiong.Experiences on “thermal spay aluminum(TSA)” coating on offshore structures[C]//Corrosion/2004,Houston:NACE,2004.
 
【7】Thomason W H,Olsen S,Haugen T ,et al.Deterioration of thermal sprayed aluminum coatings on hot risers due to thermal cycling[C]//Corrosion/2004,Houston:NACE,2004.
 
【8】周学杰,张三平,付志勇,等.金属喷涂层在海水中的腐蚀研究[J].腐蚀科学与防护技术,2004,16(4):236-239.
 
【9】Kawakita J,Kuroda S,Fukushima T,et al.Development of dense corrosion resistant coatings by an improved HVOF spraying process[J].Science and Technology of Advanced Materials,2003(4):281-289.
 
【10】朱相荣,王相润,黄桂桥.钢在海洋飞溅带的腐蚀与防护[J].海洋科学,1995(3):23-26.
 
【11】刘登良.海洋涂料与涂装技术[M],北京:化学工业出版社,2002.
 
【12】刘鸿升,刘长江,韩清国.埕岛滩海油田平台的涂层防腐技术[J].石油工程建设,1999,(4):18-20.
 
【13】Greenwood-Sole G,Watkinson C J.New glassflack coating technology for offshore applications[C]//Corrosion/2004,Houston:NACE,2004.
 
【14】Mohei-Eldin M S.Splash/tidal zone active shielding spiral sleeve[P].Can Pat Appl,2005-2494608,2006.
 
【15】Smith M,Bowley C.In situ protection of splash zones-30 years on[C]//Corrosion/2002,Houston:NACE,2002.
 
【16】侯保荣.钢铁设施在海洋浪花飞溅区的腐蚀行为及其新型包覆防护技术[J].腐蚀与防护,2007,28(4):174-175,187.
 
【17】W W 柯克.海水中钢的腐蚀保护用金属包套[J].思捷,译.造船技术,1988,(8):37-42.
 
【18】顾正贤,陈树深.海运码头钢管桩在潮差区和飞溅区的防护技术[J].腐蚀与防护,2002,23(3):119-120,123.
 
【19】黄彦良.一种浪花飞溅区钢铁设施腐蚀防护方法[P].CN 1477232A,2004-02-25.
 
相关信息
   标题 相关频次
 外防腐蚀涂层对管道阴极保护电流屏蔽的研究进展
 6
 海洋浪溅区钢铁腐蚀与防护进展
 5
 超临界火电厂海水循环水泵的防腐蚀方案
 4
 芳烃抽提装置中碳钢设备腐蚀原因分析与措施
 4
 腐蚀与防护专家系统简介
 4
 高含硫气田A333管材腐蚀情况及防护措施
 4
 海洋石油平台外加电流阴极保护延寿修复技术
 4
 户内燃气立管的腐蚀与防护
 4
 化工设备选用锆的基本考虑
 4
 火力发电厂空冷凝汽器的腐蚀与防护
 4
 加氢装置设备腐蚀分析与安全防护
 4
 埋地重要管线的腐蚀与防护
 4
 扫描电化学技术在腐蚀研究中的应用
 4
 胜利油田孤六联合站污水腐蚀与防护措施
 4
 胜利油田立式常压储罐的腐蚀分析及检测技术
 4
 石化钛设备腐蚀实例
 4
 石油生产中腐蚀的原因及缓蚀剂的应用
 4
 顺丁溶剂油回收系统的腐蚀与防护
 4
 西宁火车站下穿隧道钢筋混凝土结构的腐蚀与防护
 4
 重有色金属冶炼中混凝土槽罐的腐蚀与防护
 4
 注氮气井井下设备腐蚀原因分析及相应对策
 4
 悬索桥主缆的腐蚀与防护
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 2017第四届海洋材料与腐蚀防护大会 暨海洋耐蚀钢铁材料学术交流大会 暨海洋新材料及防护新技术展览会 第一轮通知
 2