铝合金阳极氧化膜醋酸镍封闭方法耐蚀性研究
          
CORROSION RESISTANCE OF ALUMINUM ALLOY ANODIC FILM SEALED BY NICKEL ACETATE

摘    要
研究了醋酸镍封闭方法对不同铝合金阳极氧化膜在NaCl溶液中电化学行为的影响,并与沸水封闭方法和重铬酸钾封闭方法作了比较.利用扫描电子显微镜(SEM)观察了封闭后阳极氧化膜的表面形貌.利用能量散射谱(EDS)分析了封闭后阳极氧化膜表面和截面成分.利用动电位极化和电化学阻抗谱(EIS)研究了封闭后阳极氧化膜的腐蚀行为.结果表明:醋酸镍封闭方法可以使铝合金阳极氧化膜具有平整均匀的表面形貌,镍元素分布于整个阳极氧化膜层中.在酸性和碱性溶液中,醋酸镍封闭的铝合金阳极氧化膜比沸水封闭和重铬酸钾封闭的铝合金阳极氧化膜具有更高的耐蚀性,是一种较好的封闭方法.
标    签 阳极氧化   醋酸镍封闭   电化学阻抗谱   Anodizing   Nickel acetate sealing   EIS  
 
Abstract
Electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization were used to study the corrosion behavior of different sealed aluminum alloy anodic films in 1mol/L NaCl solution.The anodic films were sealed by the methods of boiling water,potassium dichromate and nickel acetate,respectively. The surface morphology and element contents of anodic oxide films were studied with field emission scanning electron microscopey (SEM) and X-ray energy dispersive spectroscopy (EDS).The nickel acetate sealing could make the anodic films more uniform and nickel was present through the whole depth of the anodic films.Nickel acetate sealed films provided relatively high resistance in both acidic and basic solutions.

中图分类号 TG174

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2005/4/25

修改稿日期 2005/8/26

网络出版日期

作者单位点击查看

引用该论文: TIAN Lian-peng,ZUO Yu,ZHAO Jing-mao,XIONG Jin-ping,ZHAO Xu-hui. CORROSION RESISTANCE OF ALUMINUM ALLOY ANODIC FILM SEALED BY NICKEL ACETATE[J]. Corrosion & Protection, 2006, 27(2): 58~62


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】Skeldon P,Habazaki H,Thompson G E,et al.Formation of amorphous anodic oxide films of controlled composition on aluminium alloys[J].Thin Solid Films,1997,300:131-137.
 
【2】赵旭辉,左 禹,赵景茂.铝阳极氧化膜在NaCl溶液中的电化学性能[J].中国有色金属学报,2004,14(4):562-567.
 
【3】Zuo Yu,Zhao Penghui,Zhao Jingmao.The influences of sealing methods on corrosion behavior of anodized aluminum alloys in NaCl solution[J].Surface and Coatings Technology,2003,166:237-242.
 
【4】Hao L,Cheng B R.Sealing processes of anodic coatings-past,present,and future[J].Metal Finish,2000,12(8):8-18.
 
【5】Hitzig J,Juttner K,Lorenz W J,et al.AC-impedance measurements on porous aluminium oxide films[J].Corrosion Science,1984,24(11/12):945-952.
 
【6】Juttner K.Electrochemical impedance spectroscopy (EIS) of corrosion processes on inhomogeneous surfaces[J].Electrochimica Acta,1990,35(10):1501-1508.
 
相关信息
   标题 相关频次
 镍钛合金在磷酸盐缓冲溶液中的亚稳态点蚀行为
 8
 几种封闭方法处理后铝阳极氧化膜的耐蚀性比较
 7
 Cr13钢在含饱和CO2介质中腐蚀的影响因素
 6
 氯离子浓度和温度对Cr3钢CO2/H2S腐蚀的影响
 6
 载荷对砂浆中碳钢腐蚀的影响
 6
 环氧厚涂底漆在干湿交替环境条件下的劣化过程
 5
 铝阳极氧化膜绿色封闭工艺
 5
 铝阳极氧化膜在去离子水中的自封闭效应
 5
 C12-6-C12型Gemini阳离子表面活性剂缓蚀性能与行为的研究
 4
 表面电镀钯膜的316L不锈钢在高温稀硫酸/硫酸盐溶液中的耐蚀性
 4
 掺杂纳米钛导静电涂层的耐蚀性能
 4
 环氧涂层中锌铬黄颜料对镁合金的防蚀机理
 4
 咪唑啉季铵盐对A3碳钢在NaNO2+NaCl溶液中点蚀行为的影响
 4
 富镁涂层对LY12铝合金点蚀的抑制作用
 3
 纳米二氧化硅对铝合金表面环氧涂层耐蚀性能的影响
 3
 铁红颜料颜基比对含纳米氧化物的水性环氧涂层耐蚀性的影响
 3
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 2-(4-吡啶基)苯并咪唑对碳钢的缓蚀行为
 2
 20#钢在三元复合驱弱碱体系采出液中的腐蚀与防护
 2
 200 ℃回火对X80管线钢在NaHCO3溶液中电化学腐蚀的影响
 2
 304L不锈钢在硼酸水溶液中的腐蚀行为
 2
 6063铝合金阳极氧化过程中麻点问题分析
 2
 7A04-T6铝合金中金属间化合物对其阳极氧化膜耐蚀性的影响
 2
 AZ31镁合金的阳极氧化新工艺
 2
 Cu-15Ni-8Sn合金在海水中的耐腐蚀性研究
 2
 Gemini表面活性剂作为金属缓蚀剂的研究进展
 2
 H2S/CO2环境中Gemini表面活性剂对L360钢的缓蚀性能
 2
 HF-HNO3体系中Ti70合金的电化学腐蚀行为
 2
 L360钢在高压H2S/CO2环境气液两相中的腐蚀行为
 2
 LF21铝合金稀土转化膜的开裂及其钼酸盐后处理
 2