可膨胀石墨/氢氧化铝复配改性聚氨酯泡沫的阻燃性能
          
Flame Retardation of Polyurethane Foams Modified with Expandable Graphite and Aluminum Hydroxide

摘    要
将可膨胀石墨(EG)与氢氧化铝(ATH)作为阻燃剂添加到硬质聚氨酯泡沫材料(RPUF)中,制备了EG和ATH单独改性RPUF以及EG/ATH复配改性RPUF(总加入量保持30质量份不变),研究了单独改性RPUF和复配改性RPUF的氧指数及阻燃性能.结果表明:EG/ATH复配可产生明显的协同阻燃效果,EG15/ATH15复配改性RPUF的氧指数达到了31%;与未改性RPUF相比,EG15/ATH15复配改性RPUF的热释放速率峰值由148.8 kW·m-2降至66.1 kW·m-2,烟释放速率峰值由0.106 m2·s-1降至0.047 m2·s-1;复配改性的阻燃效果总体比单独改性的好.
标    签 聚氨酯   可膨胀石墨   氢氧化铝   阻燃性能   polyurethane   expandable graphite   aluminum hydroxide   flame retardation  
 
Abstract
Expandable graphite (EG) and aluminum hydroxide (ATH) were incorporated into rigid polyurethane foam (RPUF) to prepare single-modified RPUF by EG and ATH respectively,and compound-modified RPUF by EG and ATH.Oxygen index and flame retardation of the RPUFs were studied.The results indicate that the synergistic flame retardant effect was significant when EG and ATH was used in combination,and the oxygen index of the EG15/ATH15 compound-modified RPUF up to 31%.Compared with the RPUF before modification,heat release rate peak of the EG15/ATH15 compound-modified RPUF decreased from 148.8 kW·m-2 to 66.1 kW·m-2,smoke release rate peak reduced from 0.106 m2·s-1 to 0.047 m2·s-1.Flame ratardant efficiency of compound-modified RPUF was better than that of single-modified RPUF.

中图分类号 TQ328.3   DOI 10.11973/jxgccl201507019

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及其应用

基金项目 公安部应用创新项目(2013YYCXWJXY104);北京市自然科学基金资助项目(2144048)

收稿日期 2014/11/21

修改稿日期 2015/5/11

网络出版日期

作者单位点击查看

备注舒中俊(1964-),男,湖北京山人,教授,博士.

引用该论文: SHU Zhong-jun,ZHU Ning,FAN Yong,JIN Jing,WANG Wan-jin,HE Kui,WU Jing-peng,ZHANG Jin-zhuan,DONG Quan-xiao. Flame Retardation of Polyurethane Foams Modified with Expandable Graphite and Aluminum Hydroxide[J]. Materials for mechancial engineering, 2015, 39(7): 91~94
舒中俊,朱宁,樊勇,金静,王万金,贺 奎,吴敬朋,张金专,董全霄. 可膨胀石墨/氢氧化铝复配改性聚氨酯泡沫的阻燃性能[J]. 机械工程材料, 2015, 39(7): 91~94


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】周晓谦,任晶鑫,李庆雨,等.改性条件对阻燃型硬质聚氨酯泡沫塑料性能的影响[J].中国塑料,2012,26(3):71-74.
 
【2】SHI L,LI Z M,YANG M B,et al.Expandable graphite for halogen-free flame-retardant of high-density rigid polyurethane foams[J].Polymer-Plastics Technology and Engineering,2005,44(7):1323-1337.
 
【3】常海,王吉贵,甘孝贤.含磷系卤素系阻燃聚氨酯材料的研究进展[J].火炸药学报,2004,27(2):57-57.
 
【4】金军.聚氨酯硬质泡沫阻燃技术研究及趋势[J].安徽冶金科技职业学院报,2007,17(4):67-68.
 
【5】张晓光,王列平,宁斌科,等.聚氨酯泡沫塑料无卤阻燃技术的研究进展[J].化工进展,2012,31(7):1522-1523.
 
【6】THIRUMAL M,DIPAK K,NIKHIL K S,et al.Effect of expandable graphite on the properties of intumescent flame-retardant polyurethane foam[J].Journal of Applied Polymer Science,2008,110(5):2586-2594.
 
【7】高建平,边祥成,项春雷.可膨胀石墨阻燃聚氨酯泡沫塑料的研究进展[J].广东化工,2012,39(6):295-296.
 
【8】MODESTI M,LORENZETTI A.Expandable graphite as an intumescent flame retardant in polyisocyanurate-polyurethane foams[J].Polymer Degradation and Stability,2002,77:195-202.
 
【9】四季春,郑水林,路迈西.无机复合阻燃填料在软质聚氯乙烯中的应用研究[J].机械工程材料,2004,28(12):26-28.
 
【10】CINAUSERO N,AZEMA N,LOPEZ-CUESTA J M,et al.Synergistic effect between hydrophobic oxide nano-particle sand ammonium polyphosphate on fire properties of poly (methylmethacrylate) and polystyrene[J].Polymer Degradation and Stability,2011,96(8):1445-1454.
 
【11】BIAN Xiang-cheng,TANG Jian-hua,LI Zhong-ming.Flame retardancy of hollow glass microsphere/rigid polyurethane foams in the presence of expandable graphite[J].Journal of Applied Polymer Science,2008,109:1935-1943.
 
【12】GOODS S H,NEUSCHWANGER C L,WHINNERY L L,et al.Mechanical properties of a particle-strengthened polyurethane foam[J].Journal of Applied Polymer Science,1999,74:2724-2736.
 
【13】DUQUESNE S,LE BRAS M ,BOURBIGOT S.Thermal degradation of polyurethane and polyurethane/expandable graphite coatings[J].Polymer Degradation and Stability,2001,74:493-499.
 
相关信息
   标题 相关频次
 电感耦合等离子体原子发射光谱法检测产自不同地区的海洛因中15种元素
 2
 顶空-气相色谱法测定特色农产品中苯、甲苯、乙苯、间二甲苯和正己烷的残留量
 2
 硅烷和聚氨酯复合改性醇酸树脂双组份涂料的性能
 2
 化学分散法制备少数层石墨烯及其表征
 2
 环境温度对聚氨酯弹性体/环氧复合板力学性能的影响
 2
 聚氨酯/Q235钢配副滚动摩擦磨损行为
 2
 聚氨酯/聚(甲基丙烯酸甲酯-共-二甲基丙烯酸乙二醇酯)互穿聚合物网络改性废胶粉体系的力学性能
 2
 聚氨酯预聚体自乳化细乳液中异氰酸酯基团水解反应模型的建立与验证
 2
 聚氨酯增韧改性环氧树脂粘接SiC颗粒耐磨涂层的耐冲蚀性能
 2
 铝合金用水性聚氨酯涂料的研制
 2
 绿色合成法制备聚氨酯/纳米二氧化钛杂化复合材料及其荧光性能初探
 2
 南桥换流站阀水冷却系统电源开关保护分析
 2
 水性可剥离涂料研究
 2
 羧酸型聚氨酯离聚体的结构与性能
 2
 微孔聚氨酯粘弹性材料动态力学性能的有限元模拟
 2
 一种无溶剂聚氨酯补口涂料
 2
 以氢氧化铝为原料制备亚微米级α-Al2O3粉体
 2
 #高分子周报#替代传统聚氨酯的可再生泡沫
 1
 Al(OH)3阻燃剂含量对麦秸纤维/废旧聚丙烯再生复合材料性能的影响
 1
 SLENTITE?:用于定制化气候管理的全新高性能保温隔热材料成功试产
 1
 奔驰新款敞篷车将使用聚氨酯泡沫塑料
 1
 超高效液相色谱-串联质谱法测定水中4种苯脲类除草剂的含量
 1
 发泡材料带来更洁净的车内空气
 1
 放错地方的资源!美国开发出煤灰聚氨酯复合材料
 1
 高速逆流色谱法分离当归挥发油中有效成分藁本内酯及其气相色谱-质谱法的分析和鉴别
 1
 硅橡胶对无卤阻燃玻璃纤维/尼龙66复合材料性能的影响
 1
 国外高分子最近两周前沿动态(0807-0820): 聚合物变半导体?|医用超高强度韧性胶粘剂|安全性更高的电致变色油墨
 1
 将抗污染聚合物链嵌入接枝共聚物胶束的新型涂层材料
 1
 聚氨酯:材料里的变形金刚——听陶氏科普生活中的化学
 1
 聚氨酯材料大力提升高尔夫球杆性能
 1