压片法制备氯离子传感器的工作性能
          
Working Performance of Chloride Ion Sensor Fabricated by Compression Method

摘    要
采用压片法制备了以Ag/AgCl为工作电极,MnO2为参比电极的氯离子传感器.并且对传感器进行了长期稳定性试验、能斯特方程测试、温度试验、离子干扰试验和恒电流极化试验.结果表明,氯离子传感器稳定性良好,能斯特方程线性相关性强.温度对传感器工作性能影响不大,但是其他离子的存在对传感器电位值有一定影响.恒定流极化试验表明氯离子传感器抵抗极化能力较差.
标    签 混凝土   耐久性   氯离子   传感器   concrete   durability   chloride ion   sensor  
 
Abstract
A chloride ion sensor with Ag/AgCl as working electrode and MnO2 as reference electrode was fabricated by a compression method.A series of tests were conducted to examine the performance of the sensor.The test results showed that the stability of the sensor was excellent.The Nernst equation test showed a strong linear correlation.Temperature had little effect on the results,but the presence of other ions had a certain impact on the sensor's potential value.The resistance of the sensor against the constant current polarization was weak.

中图分类号 TU528.063   DOI 10.11973/fsyfh-201506009

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 山东省杰出青年基金(2012JQF01002)

收稿日期 2014/5/12

修改稿日期

网络出版日期

作者单位点击查看


备注李伟华(1971-),教授,博士,从事环海洋工程材料的腐蚀与防护研究.

引用该论文: LI Zhen-lei,LI Wei-hua. Working Performance of Chloride Ion Sensor Fabricated by Compression Method[J]. Corrosion & Protection, 2015, 36(6): 547


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】ISAO S,HIROYUKI K,MASAYUKI I.Improvement in the long-term stability of screen-printed planar type solid-state Ag/AgCl reference electrode by introducing poly (dimethylsiloxane) liquid juction[J].Electrochimica Acta,2011,58:528-531.
 
【2】SUZUKI H,SUGAMA A,KOJIMA N.Micromachined clark oxy-gen electrode[J].Sens Actuators,1993(B10):91-98.
 
【3】MURALIDHARAN S,HA T,BAE J,et al.Electrochemical studies on the solid embeddable reference sensors for corrosion monitoring in concrete structure[J].Materials Letters,2006,60(5):651-655.
 
【4】THANGAVEL K,RENGASAMY N S.Relationship between chloride/hydride and corrosion rate of steel in concrete[J].Cement and Concrete Composites,1998,20(4):283-292.
 
【5】DE VERA G,CLIMENT M A,ANTONC,et al.Determination of the selectivity coefficient of a chloride ion selective electrode in alkaline media simulating the cement paste pore solution[J].Journal of Electroanalytical Chemistry,2010(639):43-49.
 
【6】ATKINS C P,SCANTLEBURY J D,NEDWELL P J,et al.Monitoring chloride concentrations in hardened cement pastes using ion selective electrodes[J].Cement and Concrete Research,1996,26(2):319-324.
 
【7】MONTENOR M F,SIMOES A M P,FERREIRA M G S.Chloride-induced corrosion on reinforcing steel:From the fundamentals to the monitoring techniques[J].Cement and Concrete Composites,2003,24(5):491-502.
 
相关信息
   标题 相关频次
 不同状态的钢筋在氯离子入侵过程中的腐蚀行为
 4
 非饱和混凝土中氯离子的毛细吸附
 4
 粉煤灰与表面涂层对混凝土抗氯离子侵蚀能力的影响
 4
 混凝土硫酸杆菌腐蚀研究进展
 4
 搅拌工艺和粉煤灰掺量对混凝土氯离子渗透性的影响
 4
 可溶性盐对混凝土材料物理侵蚀的研究评述
 4
 桥梁腐蚀与耐久性监测
 4
 水环境腐蚀与混凝土的耐久性
 4
 盐污染混凝土电化学除盐研究
 4
 氯离子环境下混凝土钢筋的锈蚀过程
 3
 0Cr18Ni9不锈钢换热管应力腐蚀开裂原因分析
 2
 304不锈钢表面直流磁控溅射钛膜的耐蚀性
 2
 316L不锈钢在普光净化厂含氯胺液中的应力腐蚀开裂
 2
 CECS21-2000标准中混凝土不密实区和空洞检测数据处理及判断的探讨
 2
 D210塔筒体泄漏原因分析
 2
 PTA装置碱洗对设备腐蚀开裂影响讨论
 2
 WBE技术研究氯离子对存在针孔缺陷的涂层下金属腐蚀行为的影响
 2
 X80钢在0.5 mol/L NaCl溶液中的交流电流腐蚀行为
 2
 半电池电位法在混凝土外加电流阴极保护中的应用
 2
 不锈钢丝网断裂原因分析
 2
 测定盐酸西布曲明的电位传感器的研制与应用
 2
 超声回弹测强数据分形分析法评价混凝土高温破坏安全性能
 2
 超声有限幅度法检测混凝土孔洞缺陷
 2
 大孔型阴树脂交换性能测定的流动注射分析法
 2
 地下不锈钢供水管道腐蚀渗漏失效分析
 2
 电化学方法判断混凝土中钢筋腐蚀的临界状态
 2
 镀镍钻杆内壁腐蚀原因
 2
 镀锌板无铬钝化技术进展
 2
 端面处理对钻芯法检测混凝土强度的影响
 2
 废水中COD的测定——高浓度氯及溴离子干扰的消除
 2