A508III低合金钢在不同浓度硼酸溶液中的腐蚀与电化学行为
          
Corrosion and Electrochemical Behavior of A508III Low Alloy Steel in Boric Acid Solutions with Different Concentrations

摘    要
采用失重试验以及电化学测试研究了A508III低合金钢在25 ℃下0.05~0.5 mol/L硼酸溶液中的腐蚀与电化学行为.A508III钢在高浓度硼酸溶液中开路电位低于-500 mV(SCE),对应低电化学阻抗和高腐蚀速率.A508III钢在低浓度硼酸溶液中的开路电位会出现三种状况:低于-500 mV、大于-200 mV和介于其间的中间电位,其中高开路电位对应高电化学阻抗,而低开路电位对应低电化学阻抗.A508III钢在所测试的几种硼酸溶液中的阳极极化曲线与阴极极化曲线均在较宽的电位范围内表现出电位-电流线性关系,与溶液的低电导率有关.开路电位值以及相应的腐蚀速率结果与电位-pH图计算结果一致.
标    签 低合金钢   压水堆核电站   硼酸   腐蚀   电化学   low alloy steel   pressurized water reactor   boric acid   corrosion   electrochemistry  
 
Abstract
The corrosion and electrochemical behavior of A508III low alloy steel in 0.05-0.5 mol/L H3BO3 solutions at 25 ℃ were studied by weight loss measurements and electrochemical measurements.Low open circuit potentials,low electrochemical impedance and high corrosion rates were observed in boric acid solutions of higher concentrations.Three levels of open circuit potentials,i.e.higher potentials (>-200 mV(SCE)),lower potentials (<-500 mV(SCE)),and intermediate potentials were observed in boric acid solutions of lower concentrations,where lower open circuit potentials corresponded to lower electrochemical impedance and higher open circuit potentials corresponded to higher electrochemical impedance.Anodic and cathodic polarization curves showed a linear relationship in a wide range of potential,which was related to the low conductivity of test solutions.The measured values of open circuit potentials,corrosion rates and the calculated E-pH diagrams were consistent.

中图分类号 TG174

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 上海市浦江人才计划(12PJ1403600);教育部博士点基金博导类项目(20123108110021);上海大学创新基金项目资助

收稿日期 2014/4/20

修改稿日期

网络出版日期

作者单位点击查看


备注吕战鹏(1967-),研究员,博士,从事材料腐蚀与防护研究.

引用该论文: XIAO Qian,Lv Zhan-peng,CHEN Jun-jie,XIA Xiao-feng,ZHOU Bang-xin. Corrosion and Electrochemical Behavior of A508III Low Alloy Steel in Boric Acid Solutions with Different Concentrations[J]. Corrosion & Protection, 2015, 36(3): 294


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】NRC IE Information Notice No.82-02,Degradation of threaded fasteners in the reactor coolant pressure boundary of PWR plants[R].US NRC,1982.
 
【2】KOOW H.Threaded-fastener experience in nuclear power plants[R].NUREG-0943,USNRC,1982.
 
【3】O′NEIL S,HALL J F.Boric acid corrosion of carbon and low alloy steel pressure boundary components in PWRs[R].EPRI Report NP-5985,EPRI,Palo Alto,CA:1988.
 
【4】CZAJKOWSKIC J.Survey of boric acid corrosion of carbon steel components in nuclear plants[R].NUREG/CR-5576,USNRC,1990.
 
【5】HALLJ F.A survey of the literature on low alloy steel fastener corrosion in PWR power plants[R].EPRI Report NP-3784,EPRI,Palo Alto,CA:1984.
 
【6】李承亮,张明乾.压水堆核电站反应堆压力容器材料概述[J].材料导报,2008,22(9):65-68.
 
【7】Boric Acid Corrosion Evaluation (BACE) Program Phase l-Task 1 Report[R].EPRI,Palo Alto,CA,1993.
 
【8】Boric Acid Corrosion Guidebook.Revision 1[R].EPRI,Palo Alto,CA:2001,No.1000975.
 
【9】PARK J H,CHOPRA O K,NATESAN K.Boric acid corrosion of light water reactor pressure vessel materials[R].NUREG/CR-6875,USNRC,2004,ANL-04/08.
 
【10】吴双成.硼酸的酸性问题探讨[J].电镀与环保,2012,32(1):52-54.
 
【11】宋立姝,周晓鸥.水溶液中硼酸的酸式离解及其强化问题[J].安庆师范学院学报,2001,7(2):80-82.
 
【12】石建敏,雷家荣,张玲,等.Al-B4C复合材料腐蚀行为研究[J].原子能科学技术,2010,44:159-165.
 
【13】魏宝明.金属腐蚀理论及应用[M].北京:化学工业出版社,1984:26-30.
 
【14】杨熙珍,杨武.金属腐蚀电化学热力学电位-pH图及其应用[M].北京:化学工业出版社,1991:100-105.
 
相关信息
   标题 相关频次
 三价铁离子对低合金钢在硼酸溶液中腐蚀的影响
 15
 预形变及模拟压水堆一回路水中预浸泡对690合金拉伸性能的影响
 12
 磁场对铜在几种酸性溶液中阳极溶解的影响
 10
 氢对纯镍及690合金在弱碱性溶液中电化学行为的影响
 9
 预变形对Q235钢在硫酸溶液中腐蚀行为的影响及硫脲的缓蚀作用
 8
 不同氧含量高温水中低合金钢/不锈钢堆焊层的氧化膜特性
 5
 磁场对铁在含亚硝酸根的氯化钠溶液中不同电位下极化电流的影响
 5
 CdSe-TiO2复合材料对304不锈钢的光生阴极保护性能
 4
 Cl-对高氮不锈钢在0.5 mol/L NaOH溶液中腐蚀行为的影响
 4
 C和Si含量对车轮钢腐蚀行为的影响
 4
 Fe-Me(Me=Co,Ni,Co-Ni)合金化层表面钝化膜的电化学行为
 4
 pH和Cl-对Cu-Cr-Zr合金电化学腐蚀的影响
 4
 醋酸浓度和温度对超级13Cr不锈钢电化学腐蚀行为的影响
 4
 低碳钢表面Fe-Co合金层的热扩渗制备及腐蚀电化学行为
 4
 电解锰在NaCl溶液中的腐蚀行为
 4
 高铬铁素体不锈钢447在浓H2SO4溶液中的腐蚀电化学行为
 4
 铬含量对低合金钢耐氯离子腐蚀的影响规律和机制
 4
 含聚合物油田采出水的腐蚀电化学试验
 4
 基于元胞自动机法的铝合金腐蚀行为模拟
 4
 硫酸溶液中Fe3+对TC4腐蚀行为的影响
 4
 氯离子侵蚀下异类钢筋的腐蚀行为
 4
 某电厂3号机组发电机内冷水系统碱性富氧运行工况评价
 4
 镍基合金堆焊层在除氧和含氢高温水中氧化膜的性能
 4
 凝汽器管在循环冷却水中的腐蚀评价方法
 4
 汽轮机叶片用1Cr13钢在初凝水中的腐蚀特性
 4
 热喷涂复合牺牲阳极在混凝土中的电化学性能
 4
 深海环境中静水压对2205钢腐蚀电化学行为的影响
 4
 时间、pH和Cl-对既成膜管线钢腐蚀电化学行为的影响
 4
 塑变拉应力下304不锈钢在稀硫酸中的腐蚀电化学行为
 4
 酸性土壤中的模拟滞留液溶液对X80钢腐蚀行为的影响
 4