海洋石油平台外加电流阴极保护延寿修复技术
          
Repair and Prolonging Life Technology of Impressed Current Cathodic Protection for Offshore Oil Platform

摘    要
介绍了国内外海洋石油平台阴极保护延寿修复技术现状,并阐述了外加电流阴极保护技术替代牺牲阳极技术对平台进行延寿修复的必要性.并通过对外加电流阴极保护系统材料、设备及设计方面的研究构建了一种海洋石油平台外加电流阴极保护延寿修复技术.该技术适用于较深海域海洋石油平台的阴极保护延寿修复.
标    签 平台   外加电流   阴极保护   延寿修复   腐蚀   防护   platform   impressed current   catholic protection   repair and prolonging life   corrosion   protection  
 
Abstract
The repair and prolonging life technology of cathodic protection for offshore oil platforms is introduced,and the necessity of impressed current cathodic protection(ICCP) technology instead of sacrificial anode technology to repair and prolonging life for platforms is expounded.A repair and prolonging life technology of ICCP for offshore oil platforms was built by studying the materials,equipment and design of ICCP system.This technology is applicable to repair and prolonging life of cathodic protection for offshore oil platforms in relatively deeps sea.

中图分类号 TG174.41

 
  中国光学期刊网论文下载说明


所属栏目 阴极保护

基金项目

收稿日期 2014/6/11

修改稿日期

网络出版日期

作者单位点击查看


备注尹鹏飞(1983-),工程师,硕士,从事海洋构筑物防腐蚀研究.

引用该论文: LIU Fu-guo,YIN Peng-fei,ZHANG Guo-qing,ZHANG Wei,HAN Bing. Repair and Prolonging Life Technology of Impressed Current Cathodic Protection for Offshore Oil Platform[J]. Corrosion & Protection, 2015, 36(3): 276


被引情况:


【1】杨璐嘉,钟文军,曹亚洲,刘福国,宋世德,黄一, "基于数值模拟计算的铺管船阴极保护系统设计",腐蚀与防护 36, 1072-1076(2015)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】李妍,刘忠斌.海洋平台的阴极保护[J].中国造船,2002,10(43):162-164.
 
【2】FFRENCH-MULLEN T.An impressed current system for the protection of offshore platform[J].Materials Performance,1980,19:15-20.
 
【3】JAMES N B.Cathodic protection surveys of offshore platforms-A new approach[C]//Corrosion 98,San Diego Ca:[s.n.],1998:22-27.
 
【4】CABE R L,MUSSINELLLI G L,TETTAMANTI M,et al.Impressed current cathodic protection systems of offshore structures[C]//Corrosion 89,New Orleans,LA(USA):[s.n.],1989:17-21.
 
【5】夏定健.近海固定平台阴极保护阳极系统设计原则及应用[C]//第三届中国国际腐蚀控制大会,郑州:[s.n.],2005:118-126.
 
【6】武列,吴晨阳,倪政瑜,等.近海港工钢结构阴极保护工程设计应用研究的实践[C]//第十四届亚太腐蚀控制会议,上海:[s.n.],2006:29-45.
 
【7】DNV-RP-B401-2010Cathodic protection design[S].
 
【8】NACE SP0176-2007Corrosion control of submerged areas of permanently installed steel offshore structures associated with petroleum production[S].
 
【9】DEGIORGIA V G,THOMAS E D,LUCASB K E.Scale effects and verification of modeling of ship cathodic protection systems[J].Engineering Analysis with Boundary Elements,1998,22:41-49.
 
【10】于楠,梁成浩,吴建华,等.基于缩比模型理论的船舶外加电流阴极保护系统水线下表面电位的研究[J].腐蚀与防护,2006,5(28):369-372.
 
【11】吴建华,梁成浩,于楠,等.基于缩比模型模拟的船体单区域外加电流阴极保护系统[J].大连海事大学学报,2010,36(1):35-38.
 
【12】刘福国,武素茹.导管架平台外加电流阴极保护数值模拟计算研究[J].石油化工腐蚀与防护,2011,28(6):9-11.
 
【13】杜艳霞,张国忠,李健.阴极保护电位分布的数值计算[J].中国腐蚀与防护学报,2008,28(1):53-58.
 
【14】DEGIORGI V G,WIMMER S A.Geometric details and modeling accuracy requirements for shipboard impressed current cathodic protect ion system modeling[J].Engineering Analysis with Boundary Elements,2005(29):15-28.
 
【15】韩冰,贾思洋,陈学政.海水环境中水流对辅助阳极体及其托架材料的影响[C]//第七届海峡两岸腐蚀与防护研讨会,昆明:[s.n.],2010:275-279.
 
【16】尹鹏飞,马长江,许立坤.工程用Ag/AgCl参比电极性能对比研究[J].装备环境工程,2011,8(5):27-31.
 
相关信息
   标题 相关频次
 基于数值模拟计算的铺管船阴极保护系统设计
 5
 超临界火电厂海水循环水泵的防腐蚀方案
 4
 大型海水循环泵腐蚀与防护技术应用
 4
 芳烃抽提装置中碳钢设备腐蚀原因分析与措施
 4
 腐蚀与防护专家系统简介
 4
 高含硫气田A333管材腐蚀情况及防护措施
 4
 海洋飞溅区钢结构的腐蚀规律与防护措施
 4
 海洋浪溅区钢铁腐蚀与防护进展
 4
 户内燃气立管的腐蚀与防护
 4
 化工设备选用锆的基本考虑
 4
 火力发电厂空冷凝汽器的腐蚀与防护
 4
 加氢装置设备腐蚀分析与安全防护
 4
 埋地重要管线的腐蚀与防护
 4
 胜利油田孤六联合站污水腐蚀与防护措施
 4
 胜利油田立式常压储罐的腐蚀分析及检测技术
 4
 石化钛设备腐蚀实例
 4
 石油生产中腐蚀的原因及缓蚀剂的应用
 4
 顺丁溶剂油回收系统的腐蚀与防护
 4
 西宁火车站下穿隧道钢筋混凝土结构的腐蚀与防护
 4
 重有色金属冶炼中混凝土槽罐的腐蚀与防护
 4
 注氮气井井下设备腐蚀原因分析及相应对策
 4
 5083铝壳艇外加电流阴极保护系统研制
 3
 长输埋地管道阴极保护故障诊断与排除
 3
 城市燃气管网阴极保护可行性与设计要点
 3
 船体压载舱牺牲阳极阴极保护的数值模拟
 3
 大型储罐器壁腐蚀减薄的自动超声扫查
 3
 大亚湾某码头钢管桩阴极保护工程
 3
 钢铁材料在武汉长江中的现场腐蚀试验结果
 3
 核电站PTR换料水箱地脚螺栓注蜡防腐蚀
 3
 基于数值模拟计算的腐蚀防护状态评估方法
 3