CdSe-TiO2复合材料对304不锈钢的光生阴极保护性能
          
Photogenerated Cathodic Protection Properties of CdSe-TiO2 Composite Material on 304 Stainless Steel

摘    要
采用电化学二次阳极氧化法制备了二氧化钛纳米管,采用动电位沉积法在纳米管上进行CdSe沉积;采用扫描电镜(SEM)、X射线衍射(XRD)等测试方法来观察复合材料的表面形貌与晶相特征.采用开路电位(OCP)、电化学阻抗谱(EIS)、Tafel极化曲线等电化学方法来研究其光电转化性能及其对304不锈钢的阴极保护效果.结果表明,可见光照射下,304不锈钢的开路电位从-190 mV(SCE)降至约-500 mV(SCE),闭光后,电极电位缓慢上升至约-250 mV(SCE),说明暗态下材料仍能维持对不锈钢的保护作用.在可见光范围内,与纯二氧化钛相比,制备的CdSe-TiO2复合材料对304不锈钢的阴极保护性能显著提高.
标    签 光生阴极保护   CdSe-TiO2复合材料   腐蚀   不锈钢   电化学   photogenerated cathodic protection   CdSe-TiO2 composite material   corrosion   stainless steel   electrochemistry  
 
Abstract
TiO2 nanotubes were fabricated by two-step anode oxidation method,and CdSe was deposited on the nanotubes by potentiodynamic deposition.Scanning electron microscopy (SEM),X ray diffraction (XRD) test methods were used to observe the surface morphology and phase characteristics of the composite material.According to the open circuit potential (OCP),electrochemical impedance spectroscopy (EIS),Tafel polarization curve and other electrochemical methods,the optical properties of the composite and its cathodic protection effect on 304 stainless steel were investigated.The results showed that,under visible light irradiation,the open circuit potential of 304 stainless steel shifted from -190 mV(SCE)to -500 mV(SCE),after turning off the light,the electrode potential slowly increased to about -220 mV(SCE),and it showed a protective effect on stainless steel in dark environment.In the visible range,the cathodic protection performance of CdSe-TiO2 composite material was significantly improved compared with pure TiO2.

中图分类号 TG174 O6466

 
  中国光学期刊网论文下载说明


所属栏目 阴极保护

基金项目 国家科技支撑计划(2012BAB15B01);国际科技合作项目(2010DFR50860)

收稿日期 2014/5/24

修改稿日期

网络出版日期

作者单位点击查看


备注王秀通(1977-),副研究员,博士,从事金属腐蚀与防护的研究.

引用该论文: ZHANG Liang,WANG Xiu-tong,LI Hong,SUN Hao-fen,ZHUANG Nan,HOU Bao-rong. Photogenerated Cathodic Protection Properties of CdSe-TiO2 Composite Material on 304 Stainless Steel[J]. Corrosion & Protection, 2015, 36(3): 258


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】KIM S,HONG S.Kinetic study of photocatalytic degradation of volatile organic compound in air using thin film TiO2 photo-catalyst[J].Appl Catal B:Environ,2002,15:305-315.
 
【2】RDGAN O,GRATZEL M.A low-cost-efficiency solar cell based on dye-sensitized colloidal TiO2[J].Nature,1991,93:737-739.
 
【3】VINODGOPAL K,HOTCHANDANI S,KAMAT P V.Electro-chemically assisted photocatalysis:titania particulate film electrodes for photocatalytic degradation of 4-chlo-rophenol[J].J Phys Chem,1993,97:9040-9044.
 
【4】ASAHI R,MORIKAWA T,OHWAKI T,et al.Visible-light photocatalysis in nitrogen-doped titanium oxides[J].Science,2001,293:269-271.
 
【5】YUAN J G,SHIGEO T.Characterization of sol-gel-derived TiO2 coatings and their photoeffects on copper substrates[J].Journal of the Electrochemical Society,1995,142(10):3444-3450.
 
【6】YUAN J G,SHIGEO T.Photopotentials of copper coated with TiO2 by sol-gel method[J].Corrosion Engineering,1994,43(8):433-440.
 
【7】SHEN G X,CHEN Y C,LIN C J.Corrosion protection of 316L stainless steel by a TiO2 nanoparticle coating prepared by sol-gel method[J].Thin Solid Films,2005,489(1/2):130-136.
 
【8】YOSHIHISA O,SHUICHI S,TETSU T,et al.Photoelectrochemical anticorrosion and self-cleaning effects of a TiO2 coating for type 304 stainless steel[J].Journal of the Electrochemical Society,2001,148(1):B24-B28.
 
【9】LI Y,BAI X D,LING Y H,et al.Fabrication of titania nanotubes as cathode protection for stainless steel[J].Electrochemical and Solid-State Letters,2006,9(5):B28-B31.
 
【10】FUJISAWA R,TSUJIKAWA S.Photo-protection of 304 stainless steel with TiO2 coating[J].Journal of Sol-Gel Science,1994(2):529-534.
 
【11】LEI C X,FENG Z D,ZHOU H.Effect of liquid-phase-deposited parameters on the photogenerated cathodic protection properties of TiO2 films[J].Journal of Alloys and Compounds,2012,542:164-169.
 
【12】李静,云虹,林昌健.铁掺杂TiO2纳米管阵列对不锈钢的光生阴极保护[J].物理化学学报,2007,23(12):1886-1892.
 
【13】林成钢,林泽泉,李静等.钴离子(Co2+)掺杂TiO2纳米管阵列的光生阴极保护行为[J].电化学,2011,17(3):312-317.
 
【14】洪海霞.Ag+掺杂TiO2薄膜在304不锈钢上的制备及其抗海水腐蚀性能研究[D].青岛:中国海洋大学硕士学位论文,2010,6.
 
【15】LI J,LIN C J,LAI Y K,et al.Photogenerated cathodic protection of flower-like,nanostructured,N-doped TiO2 film on stainless steel[J].Surface & Coatings Technology,2010,205:557-564.
 
【16】云虹,林昌健,李静.N,S和Cl改性纳米TiO2薄膜的光电性能[J].电化学,2010,16(4):411-415.
 
【17】LEI C X,FENG Z D,ZHOU H.Visible-light-driven photogenerated cathodic protection of stainless steel by liquid-phase-deposited TiO2 films[J].Electrochimica Acta,2012,68:134-140.
 
【18】曾振鸥,周民杰,钟理,等.纳米TiO2/SnO2涂层的制备与光阴极保护性能[J].华南理工大学学报,2009,37(6):1-6.
 
【19】HYUNWOONG P,AYOUNG B,TAE H J,et al.Photo-chargeable and dischargeable TiO2 and WO3 heterojunction electrodes[J].Applied Catalysis B:Environmental,2012,115:74-80.
 
【20】周民杰,曾振欧,钟理,等.纳米TiO2/Sb2O5涂层的光生阴极保护研究[J].无机材料学报,2009,24(3):525-530.
 
【21】李立群,刘爱萍,赵海新,等.TiO2/CdSe多层膜结构的制备及光电化学性能研究[J].物理学报,2012,61(10):1-6.
 
【22】张含平,林原,周晓文,等.CdSe敏化TiO2纳米晶多孔膜电极的制备及其光电性能研究[J].化工新型材料,2006,34(11):17-19.
 
【23】沈广霞,陈艺聪,李静,等.纳米TiO2-SnO2复合薄膜的光生阴极保护作用及机理研究[J].中国腐蚀与防护学报,2006,26(2):109-114.
 
相关信息
   标题 相关频次
 CdSe/石墨烯/TiO2纳米管复合膜的制备及其对金属的保护性能
 11
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 4
 2205双相钢临界点蚀温度测量方法的比较
 4
 316L不锈钢在有机胺脱硫溶液中的耐蚀性
 4
 445铁素体不锈钢内胆水箱的加工性能和耐蚀性
 4
 A508III低合金钢在不同浓度硼酸溶液中的腐蚀与电化学行为
 4
 AISI304不锈钢钝化膜在电解质溶液中腐蚀时的半导体性质
 4
 AISI316L和SAF2205不锈钢在含溴醋酸溶液中腐蚀行为的研究
 4
 Cl-,CO2和微量H2S共存时13Cr不锈钢的腐蚀性能
 4
 Fe-Me(Me=Co,Ni,Co-Ni)合金化层表面钝化膜的电化学行为
 4
 N80钢模拟全浸区和干湿交替试样的腐蚀行为
 4
 pH和Cl-对Cu-Cr-Zr合金电化学腐蚀的影响
 4
 草甘膦生产用不锈钢反应釜腐蚀的显微分析
 4
 超临界CO2条件下钢的腐蚀行为研究进展
 4
 低碳钢表面Fe-Co合金层的热扩渗制备及腐蚀电化学行为
 4
 电化学方法研究海底管线腐蚀行为
 4
 电解锰在NaCl溶液中的腐蚀行为
 4
 海洋浪溅区钢铁腐蚀与防护进展
 4
 含聚合物油田采出水的腐蚀电化学试验
 4
 硫酸溶液中Fe3+对TC4腐蚀行为的影响
 4
 氯离子侵蚀下异类钢筋的腐蚀行为
 4
 某电厂3号机组发电机内冷水系统碱性富氧运行工况评价
 4
 幕墙不锈钢挂件的腐蚀问题
 4
 纳米化304不锈钢在硫酸溶液中的腐蚀行为
 4
 凝汽器管在循环冷却水中的腐蚀评价方法
 4
 热喷涂复合牺牲阳极在混凝土中的电化学性能
 4
 溶解氧浓度对船体钢在海水中腐蚀行为的影响
 4
 胜利油田集输系统腐蚀在线监测的试验与应用
 4
 时间、pH和Cl-对既成膜管线钢腐蚀电化学行为的影响
 4
 塑变拉应力下304不锈钢在稀硫酸中的腐蚀电化学行为
 4