Ultrasonic irradiation was utilized to improve the microhardness and corrosion resistance of Co-W nanocrystalline coatings on cabon steel substrate.The composition and microstructure of the coatings were characterized by XRD,EDX and SEM.The results showed that the coatings exhibited hexagonal close-packed (hcp) crystal structure,which became compact and smooth with the decrease of grain size and internal stress due to the application of a proper ultrasonic power(40-100 W).The tungsten content in coatings increased with the increase in the applied ultrasonic power.It is interesting to find that the coatings with tungsten content higher than 20% was not exhibit amorphous.Smaller grain size,higher tungsten content and lower density of surface defects favor the improvement of the hardness and of the corrosion resistance for Co-W nanocrystalline coatings.
引用该论文:Lv Chen-kai,SHENG Min-qi,ZHONG Qing-dong. Electrodeposition of Co-W Nanocrystalline Alloy Coatings under Ultrasonic Irradiation Action[J]. Corrosion & Protection, 2015, 36(2): 192
【1】PARTHASARATHI B,SEENIVASAN H,RAJAM K S,et al.XRD,FESEM and XPS studies on heat treated Co-W electrodeposits[J].Materials Letters,2012,76:103-105.
【2】WESTON D P,HARRIS S J,SHIPWAY P H,WESTON N J,et al.Establishing relationships between bath chemistry,electrodeposition and microstructure of Co-W alloy coatings produced from a gluconate bath[J].Electrochimica Acta,2010,55(20):5695-5708.
【3】SU F H,HUANG P.Microstructure and tribological property of nanocrystalline Co-W alloy coating produced by dual-pulse electrodeposition[J].Materials Chemistry and Physics,2012,134(1):350-359.
【4】SRIRAMAN K R,GANESH S,SUNDARA R,et al.Corrosion behaviour of electrodeposited nanocrystalline Ni-W and Ni-Fe-W alloys[J].Materials Science and Engineering:A,2007,460:39-45.
【5】GHAFERI Z,RAEISSI K,GOLOZAR M A,et al.Characterization of nanocrystalline Co-W coatings on Cu substrate,electrodeposited from a citrate-ammonia bath[J].Surface and Coatings Technology,2011,206(2):497-505.
【6】Tsyntsaru N,Cesiulis H,Budreika A,et al.The effect of electrodeposition conditions and post-annealing on nanostructure of Co-W coatings[J].Surface and Coatings Technology,2012,206(19):4262-4269.
【7】MRINALINI M,VAMSI K K,SANDIP P H.Pulsed electrodeposition of Co-W amorphous and crystalline coatings[J].Applied Surface Science,2012,258(7):2886-2893.
【8】SU F H,LIU C,PING H.Establishing relationships between electrodeposition techniques,microstructure and properties of nanocrystalline Co-W alloy coatings[J].Journal of Alloys and Compounds,2013,557:228-238.