Ca-α/β-Sialon结合刚玉复合材料的力学性能
          
Mechanical Properties of Ca-α/β-Sialon Bonded Corundum Composites

摘    要
以硅粉、铝粉、CaCO3及不同粒径组合的刚玉为主要原料,Y2O3为添加剂,在1 500 ℃通过氮化反应制备了Ca-α/β-Sialon结合刚玉复合材料,研究了Sialon含量对该复合材料力学性能的影响.结果表明:随着Sialon含量的增加,Ca-α/β-Sialon结合刚玉复合材料的体积密度降低、气孔率增大、常温抗折强度提高;随着温度的升高,复合材料的抗折强度先升高后降低,在1 000 ℃时达到最大值.
标    签 Ca-α/β -Sialon   复合材料   力学性能   Ca-α/β-Sialon   composite   mechanical property  
 
Abstract
Ca-α/β-Sialon bonded corundum composites were fabricated by nitridation at 1 500 ℃ with Si,Al,CaCO3 powders and corundum powders and particles as main raw materials and Y2O3 as additive.The effects of Sialon content on mechanical properties for the Ca-α/β-Sialon bonded corundum composite were also studied.The results show that when the Sialon content increased,the bulk density of the Ca-α/β-Sialon bonded corundum composite decreased,the porosity and room temperature modulus of rupture (MOR) of the composites increased.Moreover,the MOR of the composite first increased and then declined with an increase of temperature,which got the highest value at 1 000 ℃.

中图分类号 TQ127.2

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及其应用

基金项目 国家自然科学基金面上基金资助项目(51272188);湖北省自然科学基金资助项目(2013CFA086);湖北省科技支撑计划对外科技合作项目 (2013BHE002)

收稿日期 2013/12/18

修改稿日期 2014/11/14

网络出版日期

作者单位点击查看

备注李发亮(1983-),男,河南南阳人,讲师,博士.

引用该论文: LI Fa-liang,MENG Lu,ZHANG Hai-jun,ZHANG Shao-wei. Mechanical Properties of Ca-α/β-Sialon Bonded Corundum Composites[J]. Materials for mechancial engineering, 2015, 39(2): 73~76
李发亮,孟录,张海军,张少伟. Ca-α/β-Sialon结合刚玉复合材料的力学性能[J]. 机械工程材料, 2015, 39(2): 73~76


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】石玉敏,赵婷,都兴红,等.Sialon体合成的研究进展[J].耐火材料,2004,38(1):46-49.
 
【2】李素平,孙宏巍,贾晓林,等.Sialon基陶瓷材料的研究进展及应用[J].金刚石与磨料磨具工程,2003(3):75-77.
 
【3】陈祖熊.Sialon的结构、性能与应用[J].材料导报,1993(1):29-32.
 
【4】BANDYOPADHYAY S.PETZOW G.Formation of multiphase SiAlON ceramic[J].Materials Chemistry and Physics,1999,61(1):9-13.
 
【5】王笑一,彭达岩,文洪杰.赛隆结合刚玉复相材料的研究进展及应用现状[J].耐火材料,2005(3):199-202.
 
【6】IBRAM G.Development of β-SiAlON based ceramics for radome applications[J].Processing and Application of Ceramics,2011,5(3):113-138.
 
【7】MANDAL H.New developments in α-SiAlON ceramics[J].Journal of the European Ceramic Society,1999,19(13/14):2349-2357.
 
【8】周艳平,庄汉锐,温树林.Ca-α-Sialon的反应致密化[J].无机材料学报,1999,14(1):185-188.
 
【9】XIE R J,HIROSAKI N,SAKUMA K,et al.Eu2+-doped Ca-α-SiAlON:a yellow phosphor for white light-emitting diodes [J].Applied Physics Letters,2004,84(26):5404-5406.
 
【10】LIU L H,ZHOU X B,XIE R J,et al.Facile synthesis of Ca-α-SiAlON:Eu2+ phosphor by the microwave sintering method and its photoluminescence properties[J].Chinese Science Bulletin,2013,58(7):708-712.
 
【11】张海军,刘战杰,钟香崇.β-Sialon结合刚玉复合材料的性能[J].硅酸盐学报,2005,33(11):1308-1313.
 
【12】刘雄章,赵会敏,仇卫华.β-Sialon及β-Sialon-Al2O3的制备与性能研究[J].耐火材料,2002,36 (增):81-84.
 
【13】李亚伟,李楠,戴汉莲,等.氮化物结合耐火材料与氧化物耐火材料的抗侵蚀性能的研究[J].武汉冶金科技大学学报,1997(3):280-284.
 
【14】周艳平,庄汉锐,温树林.Ca-α-Sialon的反应致密化[J].无机材料学报,1999,14(1):185-188.
 
【15】郭宇艳,王福明,李文超,等.Ca-α-Sialon和Y-α-Sialon的制备[J].稀有金属,2001,25(1):5-8.
 
【16】李雅文,王佩玲,严东生,等.不同工艺条件下Ca-α-Sialon显微结构的形成与发展[J].无机材料学报,1999,14(6):893-899.
 
【17】ZHONG Xiang-chong,ZHAO Hai-lei.High-temperature properties of refractory composites[J].The Amerian Ceramic Society Bulletin,1999,78(7):98-101.
 
【18】仉小猛,叶树峰,徐利华,等.铁尾矿制备SiC/FexSiy复合材料的工艺及性能研究[J].材料导报B:研究篇,2011,25(1):95-99.
 
【19】雷海波,肖汉宁,郭文明,等.粗SiC颗粒对再结晶碳化硅陶瓷抗热震性能的影响[J].机械工程材料,2010,34(8):60-63.
 
【20】许富民,李佳艳,张志军,等.烧结助剂添加方式对AlN陶瓷力学性能的影响[J].机械工程材料,2011,35(7):50-53.
 
【21】徐鹏,陈兴,杨建,等.烧结助剂La2O3含量对热压烧结制备Si3N4-AlN复相陶瓷性能的影响[J].机械工程材料,2011,35(1):11-14.
 
相关信息
   标题 相关频次
 碳热/硼热还原法制备ZrB2-SiC复合粉体
 6
 原位合成NiO催化硅粉氮化制备氮化硅
 6
 MGF/PLA复合材料的制备及性能
 4
 PP-g-MAH改性SGF+POE/FPP复合材料的制备及性能
 4
 包覆镍CNTs/AM60复合材料铸态显微组织与力学性能
 4
 包覆镍的碳纳米管增强AZ91镁基复合材料的显微组织与力学性能
 4
 芳纶纤维增强尼龙6复合材料的制备与性能
 4
 纳米CaCO3添加量对其改性聚丙烯复合材料发泡效果及力学性能的影响
 4
 偶联剂表面处理对纳米SiO2/氰酸酯树脂复合材料力学性能的影响
 4
 熔盐法合成烧绿石结构La2Zr2O7粉体
 4
 石墨烯增强AZ91镁基复合材料的力学性能
 4
 碳纳米管/酚醛树脂基复合材料的研究进展
 4
 通过硝酸镍催化热解酚醛树脂制备碳纳米管
 4
 苎麻增强环氧树脂复合材料的力学性能
 4
 风力机叶片用复合材料的拉伸及冲蚀磨损性能
 3
 熔渗法制备高强Mg(AZ91D)/NiTi阻尼复合材料及其压缩和阻尼性能
 3
 1.25Cr0.5MoSi钢的焊接工艺评定
 2
 1060工业纯铝累积叠轧后的力学性能
 2
 1060铝在累积轧制中组织和性能的演变
 2
 10Ni5CrMoV钢MAG焊接接头的显微组织与力学性能
 2
 12Cr13钢预热处理工艺参数优化
 2
 14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能
 2
 15Ni3CrMoV与10Ni5CrMoV异种钢对接接头的显微组织及力学性能
 2
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 2
 2 000 t水压机立柱断裂分析
 2
 2024铝合金电子束焊接接头的显微组织与力学性能
 2
 20Cr钢与B级钢焊接接头的组织和性能
 2
 2205双相不锈钢/Q345低合金钢爆炸复合板的组织与力学性能
 2
 22Mn2SiVBS热轧无缝钢管控冷时的组织与性能
 2
 240 MPa级高强IF钢的冷轧压下率和退火温度
 2