AZ91D镁合金在SO2薄液膜下的电化学腐蚀行为
          
Electrochemical Corrosion Behavior of AZ91D Magnesium Alloy under Thin Electrolyte Layer Containing SO2

摘    要
利用自建厚度可控的大气腐蚀薄液膜电化学测试装置, 通过分析极化曲线以及交流阻抗谱探讨了AZ91D镁合金在含SO2薄液膜下的腐蚀电化学行为, 并观察了镁合金在薄液膜下的腐蚀形貌。结果表明: 薄液膜厚度和SO2对镁合金阴、阳极化率都有影响; SO2的存在使阴、阳极化率降低, 加速镁合金在薄液膜下的腐蚀; 随着薄液膜的减薄, 腐蚀加速, 50 μm下出现最大值, 但在极薄液膜下腐蚀产物的形成阻碍O2的扩散, 腐蚀减缓; 极限扩散电流密度随薄液膜厚度的增大先增加后减小, 薄液膜厚度小于50 μm时, 腐蚀产物的堆积使阳极过程受到抑制; 镁合金在SO2薄液膜下的阻抗谱由一个高频容抗弧和一个低频扩散阻抗组成, 表现为两个时间常数; 在不同厚度SO2薄液膜下腐蚀倾向从大到小的顺序为50, 20, 200, 300 μm。
标    签 AZ91D镁合金   薄液膜   SO2   电化学行为   腐蚀   AZ91D magnesium alloy   thin electrolyte layer   SO2   electrochemical behavior   corrosion  
 
Abstract
The self-built electrochemical measurement device for atmospheric corrosion, with a thin electrolyte layer thickness controlling set was utilized to investigate the electrochemical corrosion behavior of AZ91D magnesium alloy under thin electrolyte layer containing SO2 by means of polarization curve and electrochemical impedance spectrum. Furthermore the corrosion morphology was observed. Results show both the thickness of thin electrolyte layer and SO2 affected the anodic/cathodic polarization slope. SO2 addition reduced anodic/cathodic polarization slope, indicating the acceleration of corrosion for magnesium alloy. With the decrease of the thickness of thin electrolyte layer, the corrosion rate increased. The maximum value was found in 50 μm thickness. The formation of corrosion products under electrolyte layer with very thin thickness blocked the oxygen diffusion, leading to the slowing down of corrosion. The limited diffusion current density firstly increased and then decreased with the increase in the thickness of thin electrolyte layer. When the thickness of electrolyte layer was less than 50 μm, anodic process was inhibited because of pileup of corrosion products. The Nyquist curve consisted of high frequency capacity reactance arc and low frequency diffusion impedance, and showed two time constants. The order of corrosion tendency under electrolyte layer containing SO2 in different thickness was 50, 20, 200, 300 μm.

中图分类号 TG172.3

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及其应用

基金项目 国家自然科学基金资助项目(50601012); 江西省自然科学基金资助项目(2009GQC0110)

收稿日期 2012/5/21

修改稿日期 2013/3/28

网络出版日期

作者单位点击查看

备注林翠(1976—), 女, 广东蕉岭人, 教授, 博士。

引用该论文: LIN Cui,XIAO Zhi-yang,LIANG Jian-neng. Electrochemical Corrosion Behavior of AZ91D Magnesium Alloy under Thin Electrolyte Layer Containing SO2[J]. Materials for mechancial engineering, 2013, 37(6): 55~60
林翠,肖志阳,梁健能. AZ91D镁合金在SO2薄液膜下的电化学腐蚀行为[J]. 机械工程材料, 2013, 37(6): 55~60


被引情况:


【1】张鹏,马金福,王飞, "交流电流作用下X80钢在碱性溶液中阴极保护准则的适用性能",腐蚀与防护 35, 175-178(2014)

【2】高继峰,刘德绪,龚金海,王勇, "磷酸一氢钠对AZ91镁合金的缓蚀作用",腐蚀与防护 35, 233-238(2014)

【3】吉先武,邓承佯,熊懿,吴根林,张伟, "飞机铸造镁合金件螺栓孔的开裂原因",腐蚀与防护 37, 171-174(2016)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】宋光铃. 镁合金腐蚀与防护[M].北京: 化学工业出版社, 2006.
 
【2】SONG G L, HAPUGODA S, JOHN D S. Degradation of the surface appearance of magnesium and its alloys in simulated atmospheric environments[J].Corrosion Science, 2007, 49(3): 1245-1265.
 
【3】LINDSTROM R, JOHANSSON L G, THOMPSON G E, et al. Corrosion of magnesium in humid air[J].Corrosion Science, 2004, 46(5): 1141-1158.
 
【4】JOHANSSON M, PERSSON D, LEYGRAF C. Atmospheric corrosion of field-exposed magnesium alloy AZ91D[J].Corrosion Science, 2008, 50(5): 1406-1413.
 
【5】LIN C, LI X G. Roles of CO2 in the Initial stage of atmospheric corrosion of AZ91 magnesium alloy in the present of NaCl[J].Rare Metals, 2006, 25(2): 190-196.
 
【6】汪俊, 韩薇, 李洪锡, 等. 大气腐蚀电化学研究方法现状[J].腐蚀科学与防护技术, 2002, 14(6): 333-336.
 
【7】WALL F D, MARTINEZ M A, MISSERT N A, et al. Characterizing corrosion behavior under atmospheric conditions using electrochemical techniques[J].Corrosion Science, 2005, 47(1): 17-32.
 
【8】JOHANSSON M, THIERRY D, LEBOZEC N. The influence of microstructure on the corrosion behaviour of AZ91D studied by scanning Kelvin probe force microscopy and Scanning Kelvin probe[J].Corrosion Science, 2006, 48(5): 1193-1208.
 
【9】李明齐, 蔡铎昌, 何晓英.H2S薄层液膜下16Mn钢腐蚀的电化学研究[J].材料保护, 2006, 39(1): 1-5.
 
【10】李明齐, 何晓英, 蔡铎昌.薄层液膜下金属电化学腐蚀电池的设计[J].腐蚀科学与防护技术, 2005, 17(5): 355-357.
 
【11】何晓英, 邓祖宇, 邓海英.(NH4)2SO4薄层液膜下X70钢腐蚀的电化学研究[J].腐蚀科学与防护技术, 2008, 20(3): 213-215.
 
【12】周和荣, 李晓刚, 董超芳.7A04铝合金在薄液膜下腐蚀行为[J].北京科技大学学报, 2008, 30(8): 880-887.
 
【13】EL-MAHDY G A, NISHIKATA A, TSURU T. AC impedance study on corrosion of 55%Al-Zn alloy-coated steel under thin electrolyte layers[J].Corrosion Science, 2000, 42(9): 1509-1521.
 
【14】CHENG Y L, ZHANG Z, CAO F H, et al. A study of the corrosion of aluminum alloy 2024-T3 under thin electrolyte layers[J].Corrosion Science, 2004, 46(7): 1649-1667.
 
【15】陈崇木, 崔宇, 张涛.电化学方法研究纯镁在薄液膜下的腐蚀行为I-O2对纯镁在薄液膜下的腐蚀行为的影响[J].腐蚀科学与防护技术, 2009, 21(2): 94-96.
 
【16】陈崇木, 张涛, 邵亚薇.电化学方法研究纯镁在薄液膜下的腐蚀行为П―薄液膜对纯镁腐蚀阳极过程的影响[J].腐蚀科学与防护技术, 2009, 21(2): 97-100.
 
【17】林翠, 洪昕培.一种气体环境中薄液膜下金属腐蚀行为测试方法: 中国, CN101788454A[P].2010-07-28.
 
【18】林翠, 洪昕培.用于大气腐蚀测试的薄液膜控制装置: 中国, CN201477032U[P].2010-05-19.
 
【19】林翠, 李晓刚.AZ91D镁合金在SO2大气环境中的初期腐蚀行为[J].中国有色金属学报, 2004, 14(10): 1658-1665.
 
【20】邓祖宇, 廖钫, 何晓英.NaCl薄层液膜下X70钢腐蚀的电化学研究[J].西华师范大学学报, 2008, 29(1): 89-92.
 
相关信息
   标题 相关频次
 碳钢在NaCl薄液膜下的电化学腐蚀行为
 10
 AZ91D镁合金在模拟酸雨环境中的腐蚀行为
 8
 含SO2大气中湿度对低碳钢腐蚀行为的影响
 5
 AZ91D镁合金在模拟酸雨溶液中的腐蚀行为
 4
 三价铁离子对低合金钢在硼酸溶液中腐蚀的影响
 4
 AZ91D镁合金在两种盐溶液和空气中的一般腐蚀和应力腐蚀
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 200 ℃回火对X80管线钢在NaHCO3溶液中电化学腐蚀的影响
 2
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 2
 20G/316L双金属复合管失效的原因
 2
 20号钢在HCl-H2S-H2O溶液中的腐蚀行为
 2
 220kV钢芯铝绞线断股事故化学分析
 2
 2507双相不锈钢钾盐蒸发罐腐蚀的原因分析
 2
 2A12铝合金当量加速腐蚀试验
 2
 2-吡啶甲酸在玻碳电极表面的电化学行为
 2
 2-甲基咪唑啉及其复配缓蚀剂在高硬度电解质水溶液中的缓蚀性能
 2
 304L不锈钢焊接接头表面状态对其在硼酸溶液中腐蚀行为的影响
 2
 304不锈钢在高温环烷酸介质中的腐蚀行为
 2
 30CrMnSiA合金钢当量加速腐蚀试验
 2
 316L不锈钢在熔融LiCl-3%Li2O中的腐蚀行为
 2
 316L不锈钢在有机胺脱硫溶液中的耐蚀性
 2
 445铁素体不锈钢内胆水箱的加工性能和耐蚀性
 2
 45号钢在硫化氢水溶液中的腐蚀行为
 2
 500 kV输电线路铁塔塔脚腐蚀原因及处理方案
 2