Super304H钢700 ℃时效后组织和韧性的变化
          
Microstructure and Toughness Changes of Super304H Steel Aged at 700 ℃

摘    要
利用光学显微镜、扫描电子显微镜、X射线衍射仪和冲击试验机等研究了Super304H钢在700 ℃时效过程中的组织和韧性变化。结果表明: Super304H钢在时效过程中析出了M23C6碳化物, 其析出量在时效初期快速增加, 一定时间后析出量趋于稳定, M23C6主要在晶界上呈链状分布, 随时间延长尺寸很快长大; M23C6的沿晶析出引起了Super304H钢的时效脆化, 且M23C6析出量越多钢的时效脆化程度越大。
标    签 超超临界   Super304H钢   时效脆化   组织   韧性   ultra supercritical   Super304H steel   aging brittleness   microstructure   toughness  
 
Abstract
Microstructure and toughness changes of Super304H steel aged at 700℃ was investigated using optical microscopy, scanning electron microscopy, X-ray diffraction and impact tester. Results show that M23C6 carbide was precipitated during aging treatment. The amount of M23C6 was increased rapidly at the initial stage and then became stable. M23C6 was precipitated along grain boundary in a chain-like manner, and with the increase of time its size increased rapidly. Aging brittleness of Super304H steel was attributed to the precipitation of M23C6 along grain boundary, and the brittleness tended to be severe for the steel containing higher amount of M23C6.

中图分类号 TG142.1

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 山东电力集团公司重点科技项目(2007A-47)

收稿日期 2011/9/26

修改稿日期 2012/7/12

网络出版日期

作者单位点击查看

备注张忠文(1962-), 男, 山东烟台人, 高级工程师, 硕士。

引用该论文: ZHANG Zhong-wen,LI Xin-mei,DU Bao-shuai,ZOU Yong,WEI Yu-zhong. Microstructure and Toughness Changes of Super304H Steel Aged at 700 ℃[J]. Materials for mechancial engineering, 2012, 36(10): 12~14
张忠文,李新梅,杜宝帅,邹勇,魏玉忠. Super304H钢700 ℃时效后组织和韧性的变化[J]. 机械工程材料, 2012, 36(10): 12~14


被引情况:


【1】唐波,朱丽慧, "高温和应力作用下国产S30432钢中Z相的析出行为",机械工程材料 39, 19-22(2015)

【2】刘婉颖,朱毅科,施太和,时宇,邵登全,李慧莹, "V-150钻杆钢的示波冲击韧性及动态断裂韧性",机械工程材料 39, 87-90(2015)

【3】李文胜,黄 翔,王 伟,胡 平,张春雷,高 岩, "Super304H奥氏体不锈钢高温下组织与性能演变的研究进展",机械工程材料 40, 1-5(2016)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】杨富, 章应霖, 任永宁, 等.新型耐热钢焊接[M].北京: 中国电力出版社, 2006.
 
【2】周荣灿, 范长信.超超临界火电机组材料研究及选材分析[J].中国电力, 2005, 38(8): 41-47.
 
【3】KAN T, SAWARAGI Y, YAMADERA Y, et al. Properties and experiences of a new austenitic stainless steel super 304H (0.1C-18Cr-9Ni-3Cu-Nb-N) tubes for boiler tube application[C]// Materials for advanced power engineering 1998. Belgium:[s.n],1998: 441-450.
 
【4】SAWARAGI Y, OTSUKA N, SENBA H, et al. Properties of a new 18-8 austenitic steel tube (SUPER 304H) for fossil fired boilers after service exposure with high elevated temperature strength[J].Sumitomo Search,1994,56:34-43.
 
【5】杨岩, 程世长, 杨钢.Super304H锅炉用钢的开发和研究现状[J].特殊钢, 2002, 23(1): 27-30.
 
【6】刘正东, 程世长, 包汉生, 等.超超临界火电机组用锅炉钢技术国产化问题[J].钢铁, 2009, 44(6): 1-7.
 
【7】李新梅, 邹勇, 张忠文, 等.时效温度对Super304H钢析出相的影响[J].材料热处理学报, 2009, 30(6): 51-56.
 
【8】于鸿垚, 迟成宇, 董建新, 等.650 ℃长期时效过程中Super304H耐热不锈钢组织的演变[J].北京科技大学学报, 2010, 32(7): 877-881.
 
【9】杨岩, 程世长, 杨钢.铜含量对Super304H钢持久性能的影响[J].机械工程材料, 2002, 26(10): 23-25.
 
【10】肖纪美.不锈钢的金属学问题[M].北京: 冶金工业出版社, 2006.
 
【11】张忠文, 李新梅, 杜宝帅, 等.时效温度对Super304H钢焊缝金属组织和韧性影响[J].焊接学报, 2011(7): 43-46.
 
【12】李新梅, 邹勇, 张忠文, 等.Super304H钢焊接接头时效脆化机理[J].焊接学报, 2011(2): 1-6.
 
相关信息
   标题 相关频次
 650 ℃时效不同时间后Super304H钢的显微组织
 10
 高温长期运行后F12钢焊接接头的显微组织和冲击韧性
 8
 时效处理Super304H不锈钢的晶间腐蚀敏感性
 8
 600 ℃时效后HR3C钢的显微组织和冲击韧性
 7
 新型耐热HR3C/T92异种钢接头的显微组织和性能
 7
 不同冷却时间下Q690高强贝氏体钢焊接粗晶区的组织与性能
 6
 长期服役后超超临界机组P92钢焊接接头焊缝金属中微裂纹的特征
 6
 Super304H超超临界锅炉过热器管长期服役后的显微组织及力学性能
 4
 超低碳微合金管线钢焊接接头的组织与冲击性能
 4
 电化学动电位再活化法评价HR3C钢晶间腐蚀敏感性
 4
 微量锆、镧对Al-Zn-Mg-Cu合金组织和性能的影响
 3
 06CuNiCrMoNb钢模拟焊接热影响区的组织和性能
 2
 20Cr钢与B级钢焊接接头的组织和性能
 2
 2205双相不锈钢/Q345低合金钢爆炸复合板的组织与力学性能
 2
 22Cr双相不锈钢锻件韧性下降原因分析
 2
 35钢螺钉断裂分析
 2
 6061-T6铝合金超声辅助搅拌摩擦焊接头的组织与力学性能
 2
 630 ℃长时时效对G112钢组织和力学性能的影响
 2
 660 MW超超临界机组高温再热器的射线检测
 2
 C300马氏体时效钢等离子弧焊接接头的组织与硬度
 2
 Cr3C3/镍基合金等离子堆焊层的组织及耐磨性能
 2
 DZ55钢级φ102 mm×9.19 mm地质钻杆管体断裂原因分析
 2
 L360M管线钢管水压爆破试验开裂分析
 2
 La2O3/MoSi2复合微粒对烧结钼组织与力学性能的影响
 2
 Mn、Ti对热浸镀Zn-5Al合金镀层组织与耐蚀性的影响
 2
 MoSi2发热元件表面保护膜的形貌与结构
 2
 N80钢表面碳、氮、氧、铬共渗层的组织和耐腐蚀性能
 2
 NAK80模具钢表面激光熔覆钴基合金涂层的组织和摩擦磨损性能
 2
 Super304H奥氏体不锈钢高温下组织与性能演变的研究进展
 2
 T91钢管在600℃长期时效后的组织及力学性能
 2